Estimations of stress intensity factors for small cracks at notches

被引：0
|
作者：
Kujawski, D. [1 ]
机构：
[1] Univ of Alberta, Edmonton, Canada
来源：
Fatigue and Fracture of Engineering Materials and Structures | 1991年 / 14卷 / 10期
关键词：
22;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：953 / 965
相关论文
共 50 条
  • [31] Stress intensity factors for cracks in thin plates
    Dirgantara, T
    Aliabadi, MH
    ENGINEERING FRACTURE MECHANICS, 2002, 69 (13) : 1465 - 1486
  • [32] Stress intensity factors for cracks in bolted joints
    S.h. Ju
    International Journal of Fracture, 1997, 84 : 129 - 141
  • [33] STRESS INTENSITY FACTORS FOR CRACKS AT FASTENER HOLES
    NURSE, AD
    OBRIEN, EW
    PATTERSON, EA
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1994, 17 (07) : 791 - 799
  • [34] COMPUTATION OF STRESS INTENSITY FACTORS FOR INTERFACIAL CRACKS
    RAVEENDRA, ST
    BANERJEE, PK
    ENGINEERING FRACTURE MECHANICS, 1991, 40 (01) : 89 - 103
  • [35] Computing stress intensity factors for curvilinear cracks
    Chiaramonte, Maurizio M.
    Shen, Yongxing
    Keer, Leon M.
    Lew, Adrian J.
    INTERNATIONAL JOURNAL FOR NUMERICAL METHODS IN ENGINEERING, 2015, 104 (04) : 260 - 296
  • [36] Stress intensity factors for cracks at attachment lugs
    Rigby, R
    Aliabadi, MH
    ENGINEERING FAILURE ANALYSIS, 1997, 4 (02) : 133 - 146
  • [37] Stress intensity factors for cracks at fastener holes
    Nurse, A.D.
    O'Brien, E.W.
    Patterson, E.A.
    Fatigue and Fracture of Engineering Materials and Structures, 1994, 17 (07): : 791 - 799
  • [38] Stress intensity factors for cracks in bolted joints
    Ju, SH
    INTERNATIONAL JOURNAL OF FRACTURE, 1997, 84 (02) : 129 - 141
  • [39] Solutions of stress intensity factors of subsurface cracks
    Department of Engineering Mechanics, FML, Tsinghua University, Beijing 100084, China
    Key Eng Mat, 2006, (83-88):
  • [40] On Stress Intensity Factors of Multiple Cracks at Small Distances in 2-D Problems
    Larissa Gorbatikh
    Stepan Lomov
    Ignace Verpoest
    International Journal of Fracture, 2007, 143 : 377 - 384
12345