ELECTROCHEMICAL STUDY ON EROSION-CORROSION OF CARBON STEEL AND STAINLESS STEEL.

被引：0

作者：

Umemura, Fumio ^{[1
]}

Matukura, Shinji ^{[1
]}

Kawamoto, Teruaki ^{[1
]}

机构：

[1] Ishikawajima-Harima Heavy Industries, Co, Ishikawajima-Harima Heavy Industries Co

来源：

Boshoku gijutsu | 1987年 / 36卷 / 10期

关键词：

CORROSION PROTECTION; CATHODIC - ELECTROCHEMISTRY - HYDROGEN ION CONCENTRATION - STAINLESS STEEL - Corrosion - STEEL CORROSION;

D O I：

10.3323/jcorr1974.36.10_627

中图分类号：

学科分类号：

摘要：

Erosion corrosion behavior of a carbon steel and a stainless steel was studied by electrochemical measurements in jet-in-slit sand erosion testing. The test was conducted under the conditions of slurry flow rates lower than 5 m/s, pH range 1. 5-7. 0 and alumina particles of 4 multiplied by 10** minus **5 m diameter. The erosion corrosion rate is evaluated in terms of the corrosion rate obtained by electrochemical measurement and the erosion rate. The rate of the carbon steels is 15-300 times higher than that of the stainless steel. Under cathodic protection, the rate decreases, resulting in about the same rate as the stainless steel.

引用

页码：627 / 635

共 50 条

[21] Comparative Study on Flow-Accelerated Corrosion and Erosion-Corrosion at a 90° Carbon Steel Bend
Zeng, Li
Chen, Geng
Chen, Hanxin
MATERIALS, 2020, 13 (07)
[22] Comparing Erosion-Corrosion Behaviors of Carbon Steel and Hadfield Steel According to Pipe Forming
Yun, Duck Bin
Park, Jin Sung
Lee, Sang Cheol
Choi, Jong Gyo
Hwang, Joong Ki
Kim, Sung Jin
CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2022, 21 (03): : 209 - 220
[23] Study on high-temperature naphthenic acid corrosion and erosion-corrosion of aluminized carbon steel
X. Q. Wu
H. M. Jing
Y. G. Zheng
Z. M. Yao
W. Ke
Journal of Materials Science, 2004, 39 : 975 - 985
[24] Study on high-temperature naphthenic acid corrosion and erosion-corrosion of aluminized carbon steel
Wu, XQ
Jing, HM
Zheng, YG
Yao, ZM
Ke, W
JOURNAL OF MATERIALS SCIENCE, 2004, 39 (03) : 975 - 985
[25] MECHANISM OF THE INDUCTION PERIOD OF HYDROGEN CORROSION (EROSION) OF CARBON STEEL.
Archakov, Yu.I.
Ershova, O.B.
Grebeshkova, I.D.
Skop, S.L.
Journal of applied chemistry of the USSR, 1986, 59 (5 pt 2): : 1044 - 1046
[26] Technical note: Application of surface and surface imaging techniques in the study of erosion-corrosion in stainless steel
Salaita, GN
Tate, PH
CORROSION, 1996, 52 (07) : 493 - 495
[27] Erosion-corrosion behavior of 2205 duplex stainless steel in wet gas environments
Wang, Luntao
Xing, Yunying
Liu, Zhiyong
Zhang, Dawei
Du, Cuiwei
Li, Xiaogang
JOURNAL OF NATURAL GAS SCIENCE AND ENGINEERING, 2016, 35 : 928 - 934
[28] An Approach to Mapping the Erosion-Corrosion of Stainless Steel: Applications to Tidal Energy Systems
Crawley, J.
Miller, M.
Stack, M. M.
TRIBO-CORROSION: RESEARCH, TESTING, AND APPLICATIONS, 2013, 1563 : 19 - 46
[29] Ultrasonic cavitation erosion-corrosion behavior of friction stir processed stainless steel
Selvam, Karthikeyan
Mandal, Priya
Grewal, Harpreet Singh
Arora, Harpreet Singh
ULTRASONICS SONOCHEMISTRY, 2018, 44 : 331 - 339
[30] EVALUATION OF INTERGRANULAR CORROSION IN STAINLESS STEEL.
Loginow, A.W.
1600, (04):

← 1 2 3 4 5 →