Effect of Aging on the Annealing Texture in Silicon Iron.

被引：0

作者：

Livshits, B.G.

Malinina, R.I.

Mikhailova, I.B.

机构：

来源：

Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya | 1977年 / 10期

关键词：

METALLOGRAPHY; -; Textures;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

It is established that aging carried out before final annealing of transformer steel has a significant effect on the texture which forms during final annealing. By varying the aging regime, it is possible to cause the formation of a particular texture desired. The optimum regime for obtaining a cubic texture is annealing at 500 degree C for 1. 5 hr.

引用

页码：93 / 96

共 50 条

[31] Note on the reversal of the Corbino effect in iron.
Smith, AW
PHYSICAL REVIEW, 1918, 12 (05): : 337 - 339
[32] Effect of temperature on the hysteresis loss in iron.
Willis, R. L.
PHILOSOPHICAL MAGAZINE, 1903, 5 (25-30) : 117 - 133
[33] STUDY OF THE STRUCTURE AND TEXTURE CHANGES DURING THE ANNEALING OF SILICON-IRON DEFORMATED BY WEAK PRESSING
GOLDSTEYN, VY
SAVINSKAYA, AA
FIZIKA METALLOV I METALLOVEDENIE, 1983, 56 (05): : 956 - 961
[34] FORMATION OF CUBIC COMPONENT IN TEXTURE OF SILICON-IRON AFTER HIGH-TEMPERATURE ANNEALING
LIVSHITS, BG
FIONOVA, LK
MALININA, RI
STEEL IN THE USSR, 1972, 2 (03): : 222 - &
[35] Effect of high magnetic field during primary annealing on texture of silicon steel
Bacaltchuk, CMB
Castello-Branco, GA
Gault, B
Garmestani, H
THERMEC'2003, PTS 1-5, 2003, 426-4 : 3733 - 3738
[36] Effect of Initial Annealing Parameters on the Structure and Texture of 3% Silicon Steel.
Zidek, Artur
Sobecka, Eva
Moucka, Milan
Benda, Petr
Kovove Materialy, 1980, 18 (01): : 44 - 61
[37] Development of Texture Gradients and Surface Textures During Rolling of alpha -Iron.
Oesterle, Werner
Wever, Hans
Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques, 1981, 72 (04): : 230 - 237
[38] SECOND ROLLING TEMPERATURE EFFECT ON DEFORMATION TEXTURE AND RECRYSTALLIZATION OF SILICON IRON
LIVSHITS, BG
NOVIKOV, VY
KOSHKINA, LA
IZVESTIYA AKADEMII NAUK SSSR SERIYA FIZICHESKAYA, 1970, 34 (02): : 289 - &
[39] Investigations on the Melting Loss of Silicon during Dephosphorization of Pig Iron.
Klodt, J.
Lange, K.W.
Berg- und Huettenmaennische Monatshefte, 1987, 132 (03): : 71 - 78
[40] Dependence of the Sulfur Content on the Silicon Content in Foundry Pig Iron.
Stec, Roman
Girszewski, Jerzy
Hutnik, 1976, 43 (12): : 519 - 523

← 1 2 3 4 5 →