Development of quasi-cleavage crack leading to fracture of hydrogen charged high strength steel

被引：5
|
作者：
Oyanagi, Mitsushi [1 ]
Suzuki, Tetsuya [1 ]
Yamada, Kunihiro [1 ]
机构：
[1] Keio Univ., Kouhoku-ku, Yokohama 223-8522, Japan
来源：
Zairyo/Journal of the Society of Materials Science, Japan | 2002年 / 51卷 / 05期
关键词：
D O I：
10.2472/jsms.51.561
中图分类号：
学科分类号：
摘要：
23
引用
收藏
页码：561 / 566
相关论文
共 50 条
  • [41] DEPENDENCE OF THE FRACTURE TOUGHNESS OF HIGH-STRENGTH STEEL ON CRACK VELOCITY
    BILEK, Z
    SCRIPTA METALLURGICA, 1978, 12 (12): : 1101 - 1106
  • [42] Crack size dependence of the ductile fracture behaviour of a high strength steel
    Betegon, C
    Rodriguez, C
    Belzunce, FJ
    ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 831 - 836
  • [43] Influence of hydrogen on deformation and torsional fracture of high strength steel
    Romaniv, O.M.
    Nykyforchyn, H.M.
    Skrypnyk, I.D.
    Schaper, M.
    Fiziko-Khimicheskaya Mekhanika Materialov, 1993, 29 (04): : 93 - 101
  • [44] Quasi-cleavage hydrogen-assisted cracking path investigation by fractographic and side surface observations
    Merson, E. D.
    Myagkikh, P. N.
    Poluyanov, V. A.
    Merson, D. L.
    Vinogradov, A.
    ENGINEERING FRACTURE MECHANICS, 2019, 214 : 177 - 193
  • [45] Hydrogen analysis ahead of the fatigue crack tip in the high strength steel
    Matvienko, Yu. G.
    ENGINEERING STRUCTURAL INTEGRITY: RESEARCH, DEVELOPMENT AND APPLICATION, VOLS 1 AND 2, 2007, : 1569 - 1571
  • [46] HYDROGEN OXYGEN AND SUBCRITICAL CRACK GROWTH IN A HIGH-STRENGTH STEEL
    HANCOCK, GG
    JOHNSON, HH
    TRANSACTIONS OF THE METALLURGICAL SOCIETY OF AIME, 1966, 236 (04): : 513 - &
  • [47] BASIC STUDIES LEADING TO THE DEVELOPMENT OF AN ULTRAHIGH STRENGTH, HIGH FRACTURE-TOUGHNESS LOW-ALLOY STEEL
    MALAKONDAIAH, G
    SRINIVAS, M
    RAO, PR
    BULLETIN OF MATERIALS SCIENCE, 1995, 18 (04) : 325 - 341
  • [48] Crack resistance and micromechanisms of fracture of thermomechanically treated high-strength steel
    V. A. Zolot'ko
    Materials Science, 1997, 33 : 341 - 345
  • [49] Crack resistance and micromechanisms of fracture of thermomechanically treated high-strength steel
    Zolot'ko, VA
    MATERIALS SCIENCE, 1997, 33 (03) : 341 - 345
  • [50] Pre-strain effects on critical stress and hydrogen content for hydrogen-induced quasi-cleavage fracture in a TRIP-aided bainitic ferrite steel: Martensitic transformation, matrix damage, and strain aging
    Kumai, Bakuya
    Hojo, Tomohiko
    Koyama, Motomichi
    Akiyama, Eiji
    Waki, Hiroyuki
    Nagasaka, Akihiko
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2020, 45 (51) : 27920 - 27928
12345