ION-IMPLANTATION IS IN ITS ELEMENT.

被引:0
|
作者
Anon
机构
来源
Machinery and Production Engineering | 1978年 / 132卷 / 3398期
关键词
D O I
暂无
中图分类号
TF [冶金工业]; TG14 [金属材料];
学科分类号
0806 ;
摘要
The service life of steel components treated by ion implantation in the unhardened state has been found to be three times longer than with similar components which have been heat-treated. Hardened components which have subsequently been subject to ion implantation have also shown improvements. In addition, the implantation of yttrium and rare earth ions has proven to be an effective tool for increasing resistance to corrosion.
引用
收藏
页码:22 / 23
相关论文
共 50 条
  • [31] ION-IMPLANTATION DAMAGE AND ITS ANNEALING PHENOMENA IN SEMICONDUCTORS
    NARAYAN, J
    JOURNAL OF METALS, 1984, 36 (12): : 52 - 52
  • [32] ION-IMPLANTATION UPDATE
    DESTEFANI, JD
    ADVANCED MATERIALS & PROCESSES, 1988, 134 (04): : 39 - 43
  • [33] ION-IMPLANTATION INTO POLYPROPYLENE
    SVORCIK, V
    RYBKA, V
    VOLKA, K
    HNATOWICZ, V
    KVITEK, J
    SEIDL, P
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 2-LETTERS & EXPRESS LETTERS, 1992, 31 (3A): : L287 - L290
  • [34] ION-IMPLANTATION INTO GAAS
    AGASHE, VV
    GUPTA, SC
    JAIN, BP
    INDIAN JOURNAL OF PURE & APPLIED PHYSICS, 1979, 17 (05) : 287 - 289
  • [35] ION-IMPLANTATION INTO GAAS
    CROSET, M
    ICOLE, J
    PERROCHEAU, J
    REVUE TECHNIQUE THOMSON-CSF, 1980, 12 (04): : 827 - 852
  • [36] ION-IMPLANTATION INTO HOPG
    WEBER, DC
    BRANT, P
    MORAN, MJ
    FISCHER, JE
    PREIL, M
    CARBON, 1982, 20 (02) : 135 - 135
  • [37] ION-IMPLANTATION OF ZNS
    GEORGOBI.AN
    KOTLJARE.MB
    ZLOBIN, VN
    TODUAL, PA
    GENERALO.YP
    DEMENTEV, BP
    MATERIALS RESEARCH BULLETIN, 1973, 8 (08) : 893 - 897
  • [38] ION-IMPLANTATION OF POWDERS
    FREEMAN, JH
    TEMPLE, W
    RADIATION EFFECTS AND DEFECTS IN SOLIDS, 1976, 28 (1-2): : 85 - 86
  • [39] ION-IMPLANTATION METALLURGY
    HIRVONEN, JK
    JOURNAL OF METALS, 1980, 32 (12): : 50 - 50
  • [40] ION-IMPLANTATION AND SUPERCONDUCTIVITY
    STRITZKER, B
    JOURNAL OF NUCLEAR MATERIALS, 1978, 72 (1-2) : 256 - 262