Hot isostatically pressed silicon carbide fibre/mullite composites

被引：0

作者：

Holmquist, Magnus ^{[1
]}

Kristoffersson, Annika ^{[1
]}

Lundberg, Robert ^{[1
]}

Adlerborn, Jan ^{[1
]}

机构：

[1] Volvo Aero Corp, Trollhattan, Sweden

来源：

Doktorsavhandlingar vid Chalmers Tekniska Hogskola | 1999年 / 1525期

关键词：

Bending strength - Consolidation - Fiber reinforced materials - Fracture toughness - Hot isostatic pressing - Laminated composites - Silicon carbide;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Silicon carbide fibre/mullite matrix composites were fabricated. Fibres were uniaxially aligned by winding and the matrix material was cast in slip form on top of the fibres. Pre-pregs were cut, stacked and laminated to uniaxially reinforced green composites. Consolidation was done by hot isostatic pressing. Flexure strengths between 856 and 956 MPa were obtained for composites HIPed at 1450 °C, 160 MPa and the fracture behaviour was non-brittle with extensive fibre pull-out.

引用

页码：239 / 246

共 50 条

[31] MICROSTRUCTURAL STUDIES OF HOT PRESSED SILICON CARBIDE CERAMIC
Ghosh, Abhijit
Gulnar, Abdul K.
Fotedar, Ram K.
Dey, Goutam K.
Suri, Ashok K.
CERAMICS IN NUCLEAR APPLICATIONS, 2010, 30 (10): : 113 - 122
[32] Thermal conductivity in hot-pressed silicon carbide
Liu, DM
Lin, BW
CERAMICS INTERNATIONAL, 1996, 22 (05) : 407 - 414
[33] Residual stress measurements of hot isostatically pressed silicon nitride rolling elements
Hadfield, M
Tobe, S
CERAMICS INTERNATIONAL, 1998, 24 (05) : 387 - 392
[34] Raman spectroscopic analysis of structural defects in hot isostatically pressed silicon nitride
Akimune, Y
Munakata, F
Matsuo, K
Hirosaki, N
Okamoto, Y
Misono, K
JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1999, 107 (04) : 339 - 342
[35] Spall strengths of sintered and hot pressed silicon carbide
Bartkowski, P
Dandekar, DP
SHOCK COMPRESSION OF CONDENSED MATTER - 1995, 1996, 370 : 535 - 538
[36] Hot pressed hydroxyapatite-carbon fibre composites
Slosarczyk, A
Klisch, M
Blazewicz, M
Piekarczyk, J
Stobierski, L
Rapacz-Kmita, A
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2000, 20 (09) : 1397 - 1402
[37] CREEP BEHAVIOR OF HOT ISOSTATICALLY PRESSED GRAPHITE
ZUKAS, EG
GREEN, WV
CARBON, 1969, 7 (06) : 729 - &
[38] ISOSTATICALLY HOT-PRESSED HARD METAL
不详
METALLURGIA AND METAL FORMING, 1975, 42 (04): : 119 - 120
[39] Phase analysis and thermal stability of hot isostatically pressed zirconia-hydroxyapatite composites
Adolfsson, E
Alberius-Henning, P
Hermansson, L
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2000, 83 (11) : 2798 - 2802
[40] Reverse cyclic fatigue of a hot isostatically pressed silicon nitride at 1370 degrees C
Wereszczak, AA
Kirkland, TP
Ferber, MK
JOURNAL OF MATERIALS SCIENCE, 1996, 31 (24) : 6541 - 6553

← 1 2 3 4 5 →