Microstructure of a rapidly-solidified Al-12wt%Si alloy

被引：0

作者：

Birol, Yucel ^{[1
]}

机构：

[1] TUBITAK, Gebze-Kocaeli, Turkey

来源：

Materials Science Forum | 1996年 / 217-222卷 / pt 1期

关键词：

Composition - Cooling - Metal casting - Metallographic microstructure - Optical microscopy - Particles (particulate matter) - Quenching - Rapid solidification - Silicon - Solubility - Transmission electron microscopy - X ray diffraction;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Ribbons of an Al-12wt%Si alloy, produced with the Planar Flow Casting process at a cooling rate of 106 Ksec-1, revealed a single-zone microcellular structure of (Al) and nanosize Si particles which were distributed inside and at the boundaries of these cells. The solubility of Si in α(Al) was estimated to have extended to approximately 6.35 at% upon rapid quenching. Thinner sections (t<30μ) which have experienced even higher cooling rates show, in addition to a cellular structure, a distinct zone which is featureless at optical microscope magnifications.

引用

页码：189 / 194

共 50 条

[1] Microstructure of a rapidly-solidified Al-12wt%Si alloy
Birol, Y
ALUMINIUM ALLOYS: THEIR PHYSICAL AND MECHANICAL PROPERTIES, PTS 1-3, 1996, 217 : 189 - 193
[2] Microstructural characterization of a rapidly-solidified Al-12 wt% Si alloy
Birol, Y
JOURNAL OF MATERIALS SCIENCE, 1996, 31 (08) : 2139 - 2143
[3] Effect of a high magnetic field on the microstructure in directionally solidified Al-12wt%Ni alloy
Li, Xi
Fautrelle, Yves
Ren, Zhongming
JOURNAL OF CRYSTAL GROWTH, 2007, 306 (01) : 187 - 194
[4] Investigation of structure, metallographic and micro-hardness properties of rapidly solidified Al-12wt% Si alloy by melt spinning
Karaaslan, T
Yigiter, AI
Keskin, M
Dagdemir, Y
PHYSICA SCRIPTA, 1998, 58 (02): : 182 - 184
[5] Effect of Sr addition on the microstructure of a rapidly solidified Al-12 wt.% Si alloy
Wang, Y
Zhang, ZH
Zheng, SH
Wang, WM
Bian, XF
PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY, 2005, 42 (08): : 411 - 422
[6] Cooling rate and microstructure of rapidly solidified Al-20 wt.% Si alloy
Xu, CL
Wang, HY
Qiu, F
Yang, YF
Jiang, QC
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 417 (1-2): : 275 - 280
[7] SHEAR FRACTURE OF A RAPIDLY-SOLIDIFIED AL SCRAP ALLOY IN TENSION
LI, DM
BAKKER, A
SCRIPTA METALLURGICA ET MATERIALIA, 1994, 30 (03): : 343 - 348
[8] A cubic quasicrystal in a rapidly-solidified Mg-Al alloy
Kato, T.
Seki, T.
Abe, E.
ACTA CRYSTALLOGRAPHICA A-FOUNDATION AND ADVANCES, 2014, 70 : C91 - C91
[9] TRANSFORMATION BEHAVIOR OF A RAPIDLY-SOLIDIFIED AL-LR ALLOY
PANDEY, SK
SURYANARAYANA, C
ZEITSCHRIFT FUR METALLKUNDE, 1989, 80 (01): : 9 - 14
[10] Microstructure and phase structure of rapidly solidified Al-Si alloy
Key Laboratory of Material Physics, Zhengzhou University, Zhengzhou 450052, China
不详
Cailiao Rechuli Xuebao, 2008, 2 (99-102):

← 1 2 3 4 5 →