PROPERTIES OF ELECTROLESS NICKEL COATINGS ON HIGH STRENGTH STEELS.

被引：0
|
作者：
Turns, E.W.
Browning, J.W.
机构：
来源：
Plating | 1973年 / 60卷 / 05期
关键词：
ADHESION - ELECTROLESS PLATING - METALS AND ALLOYS - Mechanical Properties - PROTECTIVE COATINGS;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Coatings applied to D6AC and Maraging 200 CVM steels from the alkaline solution and some acid solutions exhibited good adhesion with no post-plating heat conditioning treatment. For other acid solutions the marginal adhesion can be adequately improved by post plating heat conditioning treatment. In general, the higher the temperature, the more adherent the treated electroless nickel coating. Salt spray corrosion resistance and Falex endurance limits are both adversely affected by higher temperature heat conditioning whereas Taber abrasion resistance is improved by heating.
引用
收藏
页码：463 / 467
相关论文
共 50 条
  • [21] Autobody Weight Reduction by Using High Strength Steels.
    Arrigoni, G.
    Carli, E.
    Metallurgia Italiana, 1982, 74 (10): : 677 - 685
  • [22] Nickel thin film coatings on steels with electroless plating and sputter deposition
    Mu, HC
    Seok, J
    Lin, RY
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2003, 150 (02) : C67 - C72
  • [23] HIGH-STRENGTH RAPID-NITRIDING STEELS.
    Yakhnina, V.D.
    Izmailov, F.Z.
    Metal Science and Heat Treatment, 1976, 18 (5-6): : 480 - 483
  • [24] HIGH-IMPACT STRENGTH BRAZED JOINTS IN STEELS.
    Yoshida, T.
    Ohmura, H.
    Welding Journal (Miami, Fla), 1986, 65 (10):
  • [25] 18% NICKEL MARAGING STEELS.
    Stauffer, Robert N.
    Manufacturing Engineering, 1980, 85 (03): : 50 - 51
  • [26] Modelling the effects of microalloying on the hardenability of high strength steels.
    Siwecki, T
    Rodell, B
    AUSTENITE FORMATION AND DECOMPOSITION, 2003, : 227 - 245
  • [27] SPOT WELDABILITY OF HIGH-STRENGTH SHEET STEELS.
    Sawhill Jr., J.M.
    Baker, J.C.
    Welding Journal (Miami, Fla), 1980, 59 (01):
  • [28] Development and Welding of High-Strength Pipeline Steels.
    Aigmmueller, G.
    Schutz, H.
    Schweisstechnik Wien, 1985, 39 (01): : 2 - 7
  • [29] ULTIMATE STRENGTH AND FAILURE MODE OF SPOT WELDS IN HIGH STRENGTH STEELS.
    VandenBossche, D.J.
    SAE Preprints, 1977, (770214):
  • [30] CRITERIA FOR DETERMINING THE STRUCTURAL STRENGTH AND RELIABILTY OF HIGH-STRENGTH STEELS.
    Potak, Ya.M.
    Voznesenskaya, N.M.
    Pokrovskaya, N.G.
    1600, (18): : 7 - 8
12345