EFFECT OF CYCLIC STRAIN AGING ON THE FATIGUE STRENGTH OF SPHEROIDAL GRAPHITE CAST IRON AT ELEVATED TEMPERATURES.

被引：0
|
作者：
Kato, Yozo
Nakano, Norihiko
Hasegawa, Norihiko
机构：
来源：
Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A | 1986年 / 52卷 / 480期
关键词：
FATIGUE OF MATERIALS - High Temperature Effects - IRON AND ALLOYS - Crack Propagation;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Rotating bending fatigue tests of a spheroidal graphite cast iron with a ferrite matrix were performed at temperatures between room temperature and 450 degree C. The behaviors of both the nucleation and the propagation of small surface cracks were observed. Because of the strengthening effect due to cyclic strain aging, the maximum fatigue limit could be seen at about 350 degree C. The peaking phenomenon of fatigue limit, however, was not so striking as that seen in carbon steels. The contribution of cyclic strain aging to the increase in fatigue life was not made so much that the peaking phenomenon could not be readily identified, differing from the remarkable peaking phenomenon in carbon steels.
引用
收藏
页码：1786 / 1792
相关论文
共 50 条
  • [11] FATIGUE STRENGTH OF SPHEROIDAL GRAPHITE CAST IRON UNDER AXIAL LOAD.
    Kogo, Sahachiro
    Ogino, Harunosuke
    Nakagawa, Takashi
    Kobayashi, Masataka
    Asami, Katsutoshi
    1984, (33)
  • [12] FATIGUE STRENGTH OF SPHEROIDAL GRAPHITE CAST IRONS.
    Anon
    British Foundryman, 1977, 70 (pt 1): : 25 - 30
  • [13] Fatigue damage in Spheroidal Graphite cast Iron (SGI)
    Nadot, Y
    Mendez, J
    Ranganathan, N
    Beranger, AS
    ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 1155 - 1160
  • [14] EFFECTS OF ELASTICITY AND COMPACTNESS OF GRAPHITES ON THE FATIGUE STRENGTH OF SPHEROIDAL GRAPHITE CAST IRON.
    Yano, Mitsuru
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1986, 52 (481): : 2150 - 2154
  • [15] Effect of microstructure on fatigue crack growth resistance of spheroidal graphite cast iron
    Funaki, K.
    Takahashi, T.
    Hirose, Y.
    Zairyo/Journal of the Society of Materials Science, Japan, 2001, 50 (09) : 943 - 948
  • [16] Effect of sampling position from cast blocks on fatigue properties for spheroidal graphite cast iron
    Fukuyama, Kunio
    Hasegawa, Norihiko
    Nishikawa, Yuji
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1994, 60 (576): : 1734 - 1739
  • [17] EVALUATION OF FATIGUE LIMIT OF SPHEROIDAL GRAPHITE CAST-IRON
    TANAKA, Y
    YANG, ZL
    MIYAMOTO, K
    MATERIALS TRANSACTIONS JIM, 1995, 36 (06): : 749 - 756
  • [18] STUDY OF IMPACT STRENGTH OF SPHEROIDAL GRAPHITE CAST-IRON
    DECROP, M
    SCHISSLER, JM
    VIGNERON, B
    GUYOT, J
    FONDERIE, 1978, 33 (381): : 241 - 246
  • [19] Effect of microstructure on resonant vibration fatigue fracture of ferritic spheroidal graphite cast iron
    Lin, SC
    Lui, TS
    Chen, LH
    INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2000, 13 (02) : 77 - 83
  • [20] Dissipative Processes during Cyclic Hardening of Spheroidal Graphite Cast Iron
    Shakhnazarov, T. A.
    Takhtarova, J. A.
    RUSSIAN METALLURGY, 2006, (04): : 323 - 328
12345