Phase transformation and superconducting properties of MgB2 using ball-milled low purity boron

被引：0

作者：

Xu, X. ^{[1
]}

Kim, J.H. ^{[1
]}

Hossain, M.S.A. ^{[1
]}

Park, J.S. ^{[1
]}

Zhao, Y. ^{[1
]}

Dou, S.X. ^{[1
]}

Yeoh, W.K. ^{[2
]}

Rindfleisch, M. ^{[3
]}

Tomsic, M. ^{[3
]}

机构：

[1] Institute for Superconducting and Electronic Materials, University of Wollongong, Wollongong, NSW 2522, Australia

[2] IRC in Superconductivity, Department of Engineering, University of Cambridge, Madingley Road, Cambridge, CB3 0HE, United Kingdom

[3] Hyper Tech Research, Inc., 1275 Kinnear Road, Columbus, OH 43212, United States

来源：

Journal of Applied Physics | 2008年 / 103卷 / 02期

关键词：

MgB2 samples were prepared by using 96% boron (B) powder with strong crystalline phase that had been ball milled for various times. We observed samples that contained ball-milled 96% B in comparison with one made from as-supplied commercial 96% B; with the results showing a significant enhancement in the high field critical current density (Jc) due to small grain size and better reactivity. Specifically; many grain boundaries for MgB2 could be acting as strong flux pinning centers. Based on Rowell connectivity analysis; when the ball-milling time increased; the connectivity factor; described as the active cross-sectional area fraction (AF); was decreased. This implies that the intergrain connectivity became worse. These properties could lead to poor Jc in low field. However; the pinning force strength; Jc; 1/2; ×; B1/4; of samples using ball-milled 96% B is larger than that of the reference sample using commercial 96% B powder. These results accompany enhanced irreversibility (Hirr) and upper critical fields (Hc2). © 2008 American Institute of Physics;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

共 50 条

[21] High trapped fields in bulk MgB2 prepared by hot-pressing of ball-milled precursor powder
Fuchs, G.
Haessler, W.
Nenkov, K.
Scheiter, J.
Perner, O.
Handstein, A.
Kanai, T.
Schultz, L.
Holzapfel, B.
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2013, 26 (12):
[22] Self-sintering-assisted high intergranular connectivity in ball-milled ex situ MgB2 bulks
Mizutani, Shunsuke
Yamamoto, Akiyasu
Shimoyama, Jun-ichi
Ogino, Hiraku
Kishio, Kohji
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2014, 27 (11):
[23] Microstructure and superconducting properties of MgB2 tapes fabricated with boron fibers
Kumakura, H
Matsumoto, A
Yamada, H
Hirakawa, M
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2003, 67 (09) : 487 - 493
[24] Influence of different boron precursors on superconducting and mechanical properties of MgB2
S. Safran
A. Kılıç
E. Asikuzun
E. Kılıçarslan
O. Ozturk
A. Gencer
Journal of Materials Science: Materials in Electronics, 2014, 25 : 2737 - 2747
[25] The role of various boron precursor on superconducting properties of MgB2/Fe
Safran, S.
Kilicarslan, E.
Kilic, A.
Gencer, A.
CRYOGENICS, 2014, 63 : 133 - 137
[26] Influence of different boron precursors on superconducting and mechanical properties of MgB2
Safran, S.
Kilic, A.
Asikuzun, E.
Kilicarslan, E.
Ozturk, O.
Gencer, A.
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2014, 25 (06) : 2737 - 2747
[27] WC contamination or addition effect on the superconducting properties in ex situ processed MgB2 tapes using unmilled and ball milled filling powders
Fujii, Hiroki
Iwanade, Akio
Kitaguchi, Hitoshi
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2019, 559 : 32 - 41
[28] Degradation of superconducting properties in MgB2 by formation of the MgB4 phase
Yakinci, ME
Balci, Y
Aksan, MA
Adigüzel, HI
Gencer, A
JOURNAL OF SUPERCONDUCTIVITY, 2002, 15 (06): : 607 - 611
[29] Degradation of Superconducting Properties in MgB2 by Formation of the MgB4 Phase
M. E. Yakıncı
Y. Balcı
M. A. Aksan
H. İ. Adigüzel
A. Gencer
Journal of Superconductivity, 2002, 15 : 607 - 611
[30] Investigation of the Effect of Low Purity Boron on the Critical Properties of L-IMD MgB2 Wires
Cicek, O.
JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, 2025, 38 (01)

← 1 2 3 4 5 →