Fracture mechanism of full lamellar TiAl under high-temperature creep and fatigue conditions based on the in situ observational tests

被引：2
|
作者：
Yokobori Jr., A. Toshimitsu [1 ,4 ]
Yoshida, M. [2 ]
Shibata, M. [1 ]
Sugiura, R. [1 ]
Fuji, A. [3 ]
机构：
[1] Department of Nanomechanics, Graduate School of Engineering, Tohoku University, Miyagi, Japan
[2] Department of Material Science and Engineering, Miyagi National College of Technology, Miyagi, Japan
[3] Structural Materials Department, Research Institute, Ishikawajima Harima Heavy Industries Co. Ltd., Tokyo, Japan
[4] Department of Nano Mechanics, Graduate School of Engineering, Tohuku University, Aobayama 6-6-01, Aobaku, Sendai 980-8579, Japan
来源：
Strength, Fracture and Complexity | 2009年 / 5卷 / 2-3期
关键词：
D O I：
10.3233/SFC-2009-0096
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：117 / 132
相关论文
共 50 条
  • [21] Fretting wear behaviors and mechanism of a high Nb–TiAl alloy with full lamellar microstructure at ambient temperature
    Qiang Song
    Lihua Liu
    Daosheng Wen
    Yanjun Wang
    Gaoqi Wang
    Ziqiang Yin
    Shouren Wang
    [J]. Journal of Materials Science, 2022, 57 : 15636 - 15650
  • [22] High-Temperature Combined Fatigue Tests on Full-Scale Turbine Blades
    Yan, Xiaojun
    Qin, Xiaoyu
    Huang, Dawei
    [J]. JOURNAL OF MULTISCALE MODELLING, 2019, 10 (03)
  • [23] HIGH-TEMPERATURE TRIAXIAL TORSIONAL CREEP TESTS OF CONCRETE AT VARIOUS HYGRAL CONDITIONS
    BAZANT, ZP
    PRASANNAN, S
    [J]. NUCLEAR ENGINEERING AND DESIGN, 1986, 94 (02) : 137 - 151
  • [24] Installation for High-temperature Cyclic Creep and Low-cycle Fatigue Tests.
    Osasyuk, V.V.
    Kuzema, Yu.A.
    Man'ko, V.D.
    [J]. Problemy Prochnosti, 1982, (01):
  • [25] Prediction of the corrosion cracking of structures under the conditions of high-temperature creep
    O. K. Morachkovskii
    Yu. V. Romashov
    [J]. Materials Science, 2011, 46
  • [26] PREDICTION OF THE CORROSION CRACKING OF STRUCTURES UNDER THE CONDITIONS OF HIGH-TEMPERATURE CREEP
    Morachkovskii, O. K.
    Romashov, Yu. V.
    [J]. MATERIALS SCIENCE, 2011, 46 (05) : 613 - 618
  • [27] A FRACTURE-MECHANICS BASED FATIGUE-CREEP-ENVIRONMENT CRACK-GROWTH MODEL FOR HIGH-TEMPERATURE
    KRUCH, S
    PRIGENT, P
    CHABOCHE, JL
    [J]. INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 1994, 59 (1-3) : 141 - 148
  • [28] CHARACTERIZATION FOR CRACK INITIATION LIFE, PROPAGATION LIFE AND TOTAL FRACTURE LIFE, RESPECTIVELY UNDER HIGH TEMPERATURE CREEP, FATIGUE AND CREEP-FATIGUE CONDITIONS.
    Yokobori, Toshimitsu
    Yokobori, Takeo
    Kuriyama, Takashi
    [J]. Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1986, 52 (477): : 1215 - 1220
  • [29] High cycle fatigue tests at high temperature under superheated steam conditions
    Dzugan, Jan
    Misek, Tomas
    [J]. MATERIALS PROCESSING TECHNOLOGY II, PTS 1-4, 2012, 538-541 : 1630 - +
  • [30] Fretting wear behaviors and mechanism of a high Nb-TiAl alloy with full lamellar microstructure at ambient temperature
    Song, Qiang
    Liu, Lihua
    Wen, Daosheng
    Wang, Yanjun
    Wang, Gaoqi
    Yin, Ziqiang
    Wang, Shouren
    [J]. JOURNAL OF MATERIALS SCIENCE, 2022, 57 (32) : 15636 - 15650
12345