Hydrogen storage properties of La1.8Ca0.2Mg14Ni3 alloy prepared by ball milling in different milling environments

被引：0

作者：

Gao, Linhui ^{[1
]}

Chen, Changpin ^{[1
]}

Chen, Lixin ^{[1
]}

Wang, Qidong ^{[1
]}

Wang, Changyao ^{[1
]}

An, Yue ^{[1
]}

机构：

[1] College of Materials Science and Chemical Engineering, Zhejiang University, Hangzhou, 310027, China

来源：

Journal of Alloys and Compounds | 2006年 / 424卷 / 1-2期

关键词：

The hydriding/dehydriding properties of the La1.8Ca0.2Mg14Ni3 alloy modified by mechanical ball milling for 20 h in different environment media; namely under argon; in toluene and in THF; respectively; have been investigated. XRD and SEM results show that the environment media affect the microstructure and surface morphology of the alloy noticeably. For the three environment media used; THF achieved the highest enhancement in hydriding/dehydriding properties. The effect of argon ranked the second and that of toluene the third. But the difference between the second and the third was very small. For the samples milled in THF; the amount of hydrogen absorbed reached 5.1 wt.% within 300 s at 600 K and 4.2 wt.% within 600 s at room temperature. The amount of hydrogen desorbed reached 5.05 wt.% at 613 K. The remarkable improvement of the hydrogen storage properties of the ball-milled alloy in different environment media experimented is ascribed to the physical and chemical change of the alloy surface. Most probably are due to the appearance of the active sites and the electron donor-acceptor (EDA) complexes produced by the ball-milling process. © 2006 Elsevier B.V. All rights reserved;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

下载

页码：338 / 341

共 50 条

[41] Effects of Ni Content and Ball Milling Time on the Hydrogen Storage Thermodynamics and Kinetics Performances of La–Mg–Ni Ternary Alloys
Zhen-Yang Li
Sheng-Li Li
Ze-Ming Yuan
Yang-Huan Zhang
Acta Metallurgica Sinica(English Letters), 2019, 32 (08) : 961 - 971
[42] La1.8Ca0.2Mg14Ni3合金在甲苯溶液中球磨改性后的储氢性能
汪伦
郭绍义
高林辉
裴有斌
浙江理工大学学报(自然科学版), 2011, 28 (05) : 744 - 748
[43] Microstructure and improved hydrogen storage properties of Mg based alloy powders prepared by modified milling method
Wu, Z.
Yang, F. S.
Bao, Z. W.
Nyamsi, S. N.
Wang, Y. Q.
Zhang, Z. X.
POWDER METALLURGY, 2014, 57 (01) : 45 - 53
[44] Structural and Kinetic Hydrogen Sorption Properties of Zr0.8Ti0.2Co Alloy Prepared by Ball Milling
He, Hui
Kou, Huaqin
Luo, Wenhua
Tang, Tao
Huang, Zhiyong
Sang, Ge
Zhang, Guanghui
Ba, Jingwen
Liu, Meng
SCANNING, 2018,
[45] Kinetic properties of La2Mg17-x wt.% Ni (x=0-200) hydrogen storage alloys prepared by ball milling
Li, Xia
Yang, Tai
Zhang, Yanghuan
Zhao, Dongliang
Ren, Huiping
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2014, 39 (25) : 13557 - 13563
[46] High energy ball milling composite modification of Mg2Ni hydrogen storage alloy by graphene and MWCNTs
Wang, Yankun
Liu, Xusheng
Chen, Yuping
Cai, Xiaolan
Zhou, Lei
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2024, 50 : 1562 - 1573
[47] Hydrogen storage properties of Mg2Ni1-xCux (x=0, 0.2, 0.4) synthesized by induction melting followed by ball milling
Chen, Yu'an
Huang, Hua
Fu, Jie
Guo, Qing
Pan, Fusheng
Deng, Shiping
Li, Jiaming
Zhao, Guangming
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2010, 39 (01): : 149 - 152
[48] Anelastic properties of Mg+3vol.%Gr prepared by ball milling
Trojanova, Zuzanka
Bosse, Michael
Ziegmann, Gerhard
Mielczarek, Agnieszka
Ferkel, Hans
HIGH DAMPING MATERIALS II, 2006, 319 : 189 - 195
[49] Hydrogen Storage Properties of Mg2Ni1-xCux (x=0, 0.2, 0.4) Synthesized by Induction Melting Followed by Ball Milling
Chen Yu'an
Huang Hua
Fu Jie
Guo Qing
Pan Fusheng
Deng Shiping
Li Jiaming
Zhao Guangming
RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (01) : 149 - 152
[50] Hydrogen storage properties of MgH2/SWNT composite prepared by ball milling
Wu, C. Z.
Wang, P.
Yao, X.
Liu, C.
Chen, D. M.
Lu, G. Q.
Cheng, H. M.
JOURNAL OF ALLOYS AND COMPOUNDS, 2006, 420 (1-2) : 278 - 282

← 1 2 3 4 5 →