High temperature oxidation behavior of CrHfSiN coatings deposited by magnetron sputtering

被引：0
|
作者：
Duo, Shu-Wang [1 ]
Xu, Xiang-Min [1 ]
Zhang, Hao [1 ]
Shang, Jin [1 ]
Luo, Chen-Gang [1 ]
机构：
[1] Jiangxi Key Laboratory of Surface Engineering, Jiangxi Science and Technology Normal University, Nanchang, China
来源：
Rengong Jingti Xuebao/Journal of Synthetic Crystals | 2015年 / 44卷
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
10
引用
收藏
页码：246 / 250
相关论文
共 50 条
  • [31] Advantages of nanocomposite coatings deposited by high power pulse magnetron sputtering technology
    Bobzin, K.
    Bagcivan, N.
    Immich, P.
    Bolz, S.
    Alami, J.
    Cremer, R.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2009, 209 (01) : 165 - 170
  • [32] Enhancing adhesion of AlFeCr coatings deposited by magnetron sputtering
    Ewa Ura-Bińczyk
    Krzysztof Kulikowski
    Jerzy Smolik
    Bogusława Adamczyk-Cieślak
    Małgorzata Lewandowska
    Archives of Civil and Mechanical Engineering, 25 (3)
  • [33] Characterization of NbC coatings deposited by magnetron sputtering method
    Zoita, C. N.
    Braic, L.
    Kiss, A.
    Braic, M.
    SURFACE & COATINGS TECHNOLOGY, 2010, 204 (12-13): : 2002 - 2005
  • [34] Characterization of DLC coatings deposited by rf magnetron sputtering
    Chowdhury, S
    Laugier, MT
    Rahman, IZ
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2004, 153 : 804 - 810
  • [35] TiAlON black decorative coatings deposited by magnetron sputtering
    Luthier, R.
    Levy, F.
    Vacuum, 1990, 41 (7 -9 Pt3) : 2205 - 2208
  • [36] Growth effects in carbon coatings deposited by magnetron sputtering
    Vetter, J
    Stüber, M
    Ulrich, S
    SURFACE & COATINGS TECHNOLOGY, 2003, 168 (2-3): : 169 - 178
  • [37] TIAION BLACK DECORATIVE COATINGS DEPOSITED BY MAGNETRON SPUTTERING
    LUTHIER, R
    LEVY, F
    VACUUM, 1990, 41 (7-9) : 2205 - 2208
  • [38] Wear resistant TiMoN coatings deposited by magnetron sputtering
    Yang, Q.
    Zhao, L. R.
    Patnaik, P. C.
    Zeng, X. T.
    WEAR, 2006, 261 (02) : 119 - 125
  • [39] MCrAlY coatings deposited by electrospark andtheir high-temperature oxidation behavior
    Beijing Key Laboratory for Corrosion Erosion and Surface Technology, Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2008, 29 (04): : 143 - 147
  • [40] Influence of Annealing Temperature on the Microstructure and Hardness of TiN Coatings Deposited by High-Power Impulse Magnetron Sputtering
    Anas Ghailane
    El Yazid Maadane
    Ayyoube Barchid
    Sabah Berchane
    Soukayna Badre-Eddine
    Hicham Larhlimi
    Christian B. Fischer
    Jones Alami
    Mohammed Makha
    Journal of Materials Engineering and Performance, 2022, 31 : 5593 - 5601
12345