Fluxless joining of aluminium alloy to steel by laser irradiation method

被引：13
|
作者：
Takemoto, Tadashi [1 ]
Kimura, Sachio [2 ,3 ]
Kawahito, Yousuke [1 ]
Nishikawa, Hiroshi [1 ]
Katayama, Seiji [1 ]
机构：
[1] Joining and Welding Research Institute, Osaka University, Osaka, Japan
[2] Graduate School of Engineering, Osaka University, Osaka, Japan
[3] Nissan Motor Co. Ltd., Yokosuka, Japan
来源：
Welding International | 2009年 / 23卷 / 05期
关键词：
Joining - Zinc coatings - Irradiation - Filler metals;
D O I：
10.1080/09507110802542643
中图分类号：
学科分类号：
摘要：
A6061 aluminium alloy was joined with steel using Zn filler metal under laser irradiation process. The quality of joint was evaluated by the strength of a lap joint. The effects of laser power irradiation conditions such as travelling speed and defocused distance on the joint strength were investigated. The maximum joint strength was obtained at relatively medium laser travelling speed. The excess reaction between filler metal and aluminium formed thick brittle intermetallic compounds between steel and aluminium alloy. The compounds are considered to lead to the reduction in joint strength. It was found that low wetting at high travelling speed and excess reaction layer formation at low travelling speed were responsible for low joint strength. The study revealed that the relatively high joint strength between aluminium alloy and steel was obtained by laser joining method using Zn filler without the use of flux in air atmosphere.
引用
收藏
页码：316 / 322
相关论文
共 50 条
  • [1] Fluxless laser beam joining of aluminium with zinc coated steel
    Laukant, H
    Wallmann, C
    Müller, M
    Korte, M
    Stirn, B
    Haldenwanger, HG
    Glatzel, U
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2005, 10 (02) : 219 - 226
  • [2] Fluxless laser brazing of aluminium alloy to galvanized steel using a tandem beam - dissimilar laser brazing of aluminium alloy and steels
    Saida K.
    Ohnishi H.
    Nishimoto K.
    Welding International, 2010, 24 (03) : 161 - 168
  • [3] Joining of Aluminium Alloy and Steel by Laser Assisted Reactive Wetting
    Liedl G.
    Vázquez R.G.
    Murzin S.P.
    Lasers in Manufacturing and Materials Processing, 2018, 5 (1) : 1 - 15
  • [4] Fluxless arc weld-brazing of aluminium alloy to steel
    Yagati, Krishna P.
    Bathe, Ravi N.
    Rajulapati, Koteswararao V.
    Rao, K. Bhanu Sankara
    Padmanabham, G.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2014, 214 (12) : 2949 - 2959
  • [5] Perpendicular ultrasonic joining of steel to aluminium alloy plates
    Munoz-Guijosa, Juan M.
    Nanaumi, Genki
    Ohtani, Kazuki
    Ohtake, Naoto
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2017, 243 : 112 - 122
  • [6] Galvanised steel to aluminium joining by laser and GTAW processes
    Sierra, G.
    Peyre, P.
    Beaume, F. Deschaux
    Stuart, D.
    Fras, G.
    MATERIALS CHARACTERIZATION, 2008, 59 (12) : 1705 - 1715
  • [7] Joining of aluminium alloy to pre-holed carbon steel by aluminium extrusion using friction spot method
    Abdullah, Isam Tareq
    Hussein, Sabah Khammass
    Hussein, Abbas Khammas
    INTERNATIONAL JOURNAL OF STRUCTURAL INTEGRITY, 2020, 11 (06) : 849 - 860
  • [8] Arc joining of aluminium alloy to stainless steel with the aid of milling
    Xu, Huibin
    Gao, Pengyu
    Cong, Wei
    Li, Moyang
    Cai, Yuhua
    MATERIALS SCIENCE AND TECHNOLOGY, 2019, 35 (01) : 107 - 115
  • [9] Advances in Laser Welding Technology for Dissimilar Metal Joining of Dual-phase Steel and Aluminium Alloy
    Li, Ang
    Zeng, Yida
    Li, Zhiyong
    He, Rong
    Guo, Zhenghua
    Chen, Yuhua
    Jiang, Yi
    Yang, Zirui
    Cailiao Daobao/Materials Reports, 2024, 38 (22):
  • [10] Laser direct joining of CFRTP and aluminium alloy with a hybrid surface pre-treating method
    Jiao, Junke
    Jia, Shaohui
    Xu, Zifa
    Ye, Yiyun
    Sheng, Liyuan
    Zhang, Wenwu
    COMPOSITES PART B-ENGINEERING, 2019, 173
12345