Development of high-coercivity nanocomposite permanent magnets based on Nd2Fe14B and FexB

被引：0

作者：

Hirosawa, Satoshi ^{[1
]}

Kanekiyo, Hirokazu ^{[1
]}

Miyoshi, Toshio ^{[1
]}

Shigemoto, Yasutaka ^{[1
]}

Murakami, Kaichi ^{[1
]}

Senzaki, Yuuka ^{[1
]}

Nishiuchi, Takashi ^{[1
]}

机构：

[1] Research and Development Center, NEOMAX Co., Ltd., 2-15-17 Egawa, Shimamoto-cho, Mishima-gun, Osaka-fu 618-0013, Japan

来源：

Journal of Alloys and Compounds | 1600年 / 408-412卷

关键词：

In a composition range along the tie line between Fe3B and Nd2Fe14B with Nd concentration between approximately 6 and 9 at%; it has been found that addition of a few atomic percent of Ti suppresses formation and growth of γ-iron and promotes the formation of Nd2Fe14B. This lead to development of a new series of nanocomposite permanent magnet materials on the Nd-Fe-B-Ti-C system; for which the strip-casting technique can be applied in the rapid solidification process. The newly developed Nd-Fe-B-Ti-C nanocomposite permanent magnets cover a wide range of magnetic properties and include a high-coercivity grade with coercivity (HcJ) of about 1 MA/m and remanence (Br) of 0. 8 T and a high-remanence grade with HcJ = 500 kA/m and Br = 0.86 T. The high coercivity owes its origin to a larger volume fraction of the hard magnetic Nd2Fe14B phase compared to the previous Fe3B/Nd2Fe14B nanocomposite permanent magnets in which the volume fraction of the Nd2Fe14B phase is limited by disappearance of this phase in Nd concentration range beyond about 5 at%. Resin-bonded magnets fabricated using these powders show excellent stability against oxidation under a humid; high-temperature atmosphere. © 2005 Elsevier B.V. All rights reserved;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

页码：260 / 265

共 50 条

[21] HIGH-COERCIVITY ND-FE-B-TYPE PERMANENT-MAGNETS WITH LESS DYSPROSIUM
HIROSAWA, S
TOMIZAWA, H
MINO, S
HAMAMURA, A
IEEE TRANSACTIONS ON MAGNETICS, 1990, 26 (05) : 1960 - 1962
[22] Effect of Nd2Fe14B/α-Fe Nanocomposite Permanent Magnets with a Combined Co and Nb Additions
马瑞
Journal of Wuhan University of Technology(Materials Science), 2009, (05) : 725 - 727
[23] Effect of Nd2Fe14B/α-Fe Nanocomposite Permanent Magnets with a Combined Co and Nb Additions
Ma Rui
Lu Bin
JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2009, 24 (05): : 725 - 727
[24] The coercivity mechanism in nanocomposite Nd2Fe14B+α-Fe magnets
Wnuk, I
Wyslocki, JJ
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2006, 175 (1-3) : 433 - 438
[25] Effects of V and Si additions on the coercivity and microstructure of nanocomposite Fe3B/Nd2Fe14B magnets
Xiong, XY
Hono, K
Hirosawa, S
Kanekiyo, H
JOURNAL OF APPLIED PHYSICS, 2002, 91 (11) : 9308 - 9314
[26] Effect of high magnetic field on the crystallization of Nd2Fe14B/α-Fe nanocomposite magnets
Wang Zhanyong
Xu Hui
Ni Jiansen
Li Qiang
Zhou Bangxin
RARE METALS, 2006, 25 (04) : 337 - 341
[27] Effect of high magnetic field on the crystallization of Nd2Fe14B/α-Fe nanocomposite magnets
WANG Zhanyong1
Rare Metals, 2006, (04) : 337 - 341
[28] Nanocomposite Nd2Fe14B/α-Fe magnets with Ti and C additions
Li, Shun
Bai, Shu-Xin
Zhang, Hong
Chen, Ke
Xiao, Jia-Yu
Cailiao Gongcheng/Journal of Materials Engineering, 2008, (12): : 15 - 18
[29] Direct formation of Fe3B/Nd2Fe14B nanocomposite permanent magnets in rapid solidification
Hirosawa, S
Shigemoto, Y
Miyoshi, T
Kanekiyo, H
SCRIPTA MATERIALIA, 2003, 48 (07) : 839 - 844
[30] High coercivity Pr2Fe14B/α-Fe nanocomposite permanent magnets with Zr addition
Mehran Khan Alam
Guang-Bing Han
Shi-Shou Kang
Rare Metals, 2020, 39 : 41 - 47

← 1 2 3 4 5 →