Structural characterization of sulfur vulcanized deproteinized natural rubber by solid-state13C NMR spectroscopy

被引：0

作者：

Sakdapipanich, Jitladda T. ^{[1
,2
]}

Kowitteerawut, Tippawan ^{[1
]}

Tuampoemsab, Surakit ^{[1
]}

Kawahara, Seiichi ^{[3
]}

机构：

[1] Department of Chemistry, Faculty of Science, Mahidol University, Bangkok 10400, Thailand

[2] Institute of Science and Technology for Research and Development, Mahidol University, Nakornpathom 73170, Thailand

[3] Department of Chemistry, Faculty of Engineering, Nagaoka University of Technology, Niigata 940-2188, Japan

来源：

Journal of Applied Polymer Science | 2006年 / 100卷 / 03期

关键词：

The structural changes in unfilled and filled vulcanized deproteinized natural rubber (DPNR); which is a highly purified natural rubber (NR); were investigated by solid-state 13C NMR spectroscopy. The chemical shifts of new signal were assigned by calculation and compared with those observed by Koenig et al. for conventional vulcanized NR. The crosslink structure of sulfur vulcanized DPNR were similar to that of sulfur-vulcanized NR for CV system assigned by Koenig et al. The increase in the relative intensities of signals between 45 and 58 ppm; which was assigned to monosulfidic and polysulfidic bonds; was concerned with the increase in crosslink density. In this case; the crosslink density was increased after aging; which might be due to incomplete curing. Furthermore; the solid-state 13C NMR spectrum of the aged sulfur vulcanizate DPNR showed new signals at around 73 ppm; which is assignable to carbon attached to hydroxyl group because of thermal oxidation. It can provide more complete understanding of the final vulcanizate crosslink structure of DPNR vulcanizates. © 2006 Wiley Periodicals; Inc;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

页码：1875 / 1880

共 50 条

[41] SOLID-STATE C-13 NMR-STUDIES OF VULCANIZED ELASTOMERS .12. ACCELERATED SULFUR-VULCANIZED HIGH-VINYL POLYBUTADIENE
RANA, MA
KOENIG, JL
[J]. RUBBER CHEMISTRY AND TECHNOLOGY, 1993, 66 (02): : 242 - 256
[42] Strain-induced crystallization of natural rubber as studied by high-resolution solid-state 13C NMR spectroscopy
Lin, WX
Bian, MH
Yang, G
Chen, Q
[J]. POLYMER, 2004, 45 (14) : 4939 - 4943
[43] High-resolution latex-state 13C-NMR spectroscopy for natural rubber vulcanizates
Kawahara, Seiichi
Ukawa, Jinta
Sakai, Junichiro
Yamamoto, Yoshimasa
Isono, Yoshinobu
[J]. RUBBER CHEMISTRY AND TECHNOLOGY, 2007, 80 (05): : 751 - 761
[44] Characterization of vulcanized natural rubber through field gradient-fast magic angle spinning NMR spectroscopy
Kawahara, Seiichi
Chaikumpollert, Oraphin
[J]. ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2013, 245
[45] STRUCTURAL CHARACTERIZATION OF POLYACENIC POLYMERS IN THE SOLID-STATE BY HIGH-RESOLUTION C-13 NMR-SPECTROSCOPY
KUROSU, H
NAKAJIMA, Y
ANDO, I
[J]. JOURNAL OF MOLECULAR STRUCTURE, 1995, 355 (01) : 27 - 32
[46] Solid-state 13C-NMR and equilibrium-swelling studies of filled, TBBS-accelerated sulfur vulcanization of natural rubber
Mori, M
Koenig, JL
[J]. JOURNAL OF APPLIED POLYMER SCIENCE, 1998, 70 (07) : 1391 - 1399
[47] Identification of elastomers in vulcanized compounds by 13C-NMR spectroscopy
Fontao, I.
Gonzalez, L.
Jimeno, M.L.
Marcos, A.
[J]. Kautschuk und Gummi Kunststoffe, 1993, 46 (06):
[48] IDENTIFICATION OF ELASTOMERS IN VULCANIZED COMPOUNDS BY C-13-NMR SPECTROSCOPY
FONTAO, I
GONZALEZ, L
JIMENO, ML
MARCOS, A
[J]. KAUTSCHUK GUMMI KUNSTSTOFFE, 1993, 46 (06): : 431 - 435
[49] Structural characterization of stearic acid in the crystalline state by the cross polarization in solid state 13C NMR
Arata, S
Kurosu, H
Kuroki, S
Ando, I
[J]. JOURNAL OF MOLECULAR STRUCTURE, 1999, 513 (1-3) : 133 - 138
[50] Crosslinking junctions of vulcanized natural rubber analyzed by solid-state NMR spectroscopy equipped with field-gradient-magic angle spinning probe
Kawahara, Seiichi
Chaikumpollert, Oraphin
Sakurai, Satoshi
Yamamoto, Yoshimasa
Akabori, Keiichi
[J]. POLYMER, 2009, 50 (07) : 1626 - 1631

← 1 2 3 4 5 →