Residual life assessment of water distribution system through analysis of cast iron pipes

被引：0

作者：

Lee, Hyun-Dong ^{[1
,2
]}

Shin, Hong-Cheol ^{[1
]}

机构：

[1] University of Science and Technology, Construction and Environment Engineering, 217, Gajeong-ro, Yuseong-gu, Daejeon, Korea, Republic of

[2] Korea Institute of Civil Engineering and Building Technology, Environment and Plant Engineering Research Institute, Daehwa-dong 283, Goyangdae-Ro, Ilsanseo-gu, Goyang-si, Gyeonggi-do, Korea, Republic of

来源：

International Journal of Control and Automation | 2015年 / 8卷 / 09期

关键词：

Cast iron - Pipeline corrosion - Water distribution systems;

D O I：

10.14257/ijca.2015.8.9.23

中图分类号：

学科分类号：

摘要：

Water distribution system is the facility to provide water stably. But sometimes, water leakages in water distribution systems cause enormous economic damage and destabilize such systems. To estimate residual life in this study, a total of 34 cast-iron pipes including ductile cast-iron pipes from differing laying environments in P city were used. After assessment, we determined that an improvement plan based on a residual life assessment was more efficient than a traditional plan based on laying year. © 2015 SERSC.

引用

页码：229 / 242

共 50 条

[31] Review on corrosion and corrosion scale formation upon unlined cast iron pipes in drinking water distribution systems
Zhang, Haiya
Liu, Dibo
Zhao, Lvtong
Wang, Jun
Xie, Shuguang
Liu, Shuming
Lin, Pengfei
Zhang, Xiaojian
Chen, Chao
[J]. JOURNAL OF ENVIRONMENTAL SCIENCES, 2022, 117 : 173 - 189
[32] Behavior Assessment of Exhumed Cast Iron Pipes Using Distributed Strain Sensing
Simmons, Joshua A.
Hoult, Neil A.
Moore, Ian D.
[J]. JOURNAL OF PIPELINE SYSTEMS ENGINEERING AND PRACTICE, 2024, 15 (01)
[33] Enhancing Sustainability in Italian Water Supply Pipes through Life Cycle Analysis
Simion, Isabela Maria
Pennellini, Sara
Awere, Eric
Rosatti, Alessandro
Bonoli, Alessandra
[J]. SUSTAINABILITY, 2024, 16 (07)
[34] Weibull analysis, extrapolations and implications for condition assessment of cast iron water mains
Belmonte, H. M. S.
Mulheron, M.
Smith, P. A.
[J]. FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2007, 30 (10) : 964 - 990
[35] Pressure-induced fatigue failures in cast iron water supply pipes
Jara-Arriagada, Carlos
Stoianov, Ivan
[J]. ENGINEERING FAILURE ANALYSIS, 2024, 155
[36] Simplified Numerical Method to Evaluate the Mechanical Strength of Cast Iron Water Pipes
Seica, Michael V.
Packer, Jeffrey A.
[J]. JOURNAL OF INFRASTRUCTURE SYSTEMS, 2006, 12 (01) : 60 - 67
[37] THE EFFECT OF PH ADJUSTMENT ON THE INTERNAL CORROSION RATE OF RESIDENTIAL CAST-IRON AND COPPER WATER DISTRIBUTION PIPES - DISCUSSION
BELL, J
[J]. CANADIAN JOURNAL OF CIVIL ENGINEERING, 1988, 15 (06) : 1085 - 1085
[38] Failure of corrosion affected buried cast iron pipes subject to water hammer
Firouzi, Afshin
Yang, Wei
Shi, Wenhai
Li, Chun-Qing
[J]. ENGINEERING FAILURE ANALYSIS, 2021, 120
[39] Characterization of corrosion morphologies from deteriorated underground cast iron water pipes
Deo, Ravin N.
Rathnayaka, Suranji
Zhang, Chunshun
Fu, Guoyang Y.
Shannon, Benjamin
Wong, Leslie
Kodikara, Jayantha K.
[J]. MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2019, 70 (10): : 1837 - 1851
[40] CHARACTERIZATION OF GRAPHITIC CORROSION RESIDUE OF CAST-IRON IN A WATER DISTRIBUTION-SYSTEM
BLOOM, PR
TUOVINEN, OH
[J]. MATERIALS PERFORMANCE, 1984, 23 (02) : 21 - 23

← 1 2 3 4 5 →