Dissimilar resistance spot welding of aluminum to magnesium with Zn-coated steel interlayers

被引：0
|
作者：
机构：
[1] Penner, P.
[2] Liu, L.
[3] Gerlich, A.
[4] Zhou, Y.
来源：
| 1600年 / American Welding Society卷 / 93期
关键词：
Coating interfaces - Dissimilar - Interlayer - Joint strength - Metallurgical bonding - Properties and microstructures - Resistance spot weld - Resistance spot welding;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Resistance spot welding of AZ31B Mg alloy to AI Alloy S754 was studied using Zn foil and Zn-coated steel interlayers. Mechanical properties and microstructure of the welds were analyzed. The strength requirements of AWS Standard D17.2 could not be met when a Zn foil interlayer was used. However, acceptable joint strengths were achieved using a Zn-coated steel interlayer, since the steel remains solid and can successfully keep AI and Mg from mixing. An ultrathin Fe-Al layer present at the Zn-coating interface of the steel interlayer promoted metallurgical bonding at both AI and Mg alloy interfaces. Welds made with Zn-coated steel interlayers met the strength requirements of the AWS standard and reached 74% of the strength of comparable AZ31B similar resistance spot welds.
引用
收藏
相关论文
共 50 条
  • [41] Enabling Dissimilar Joining of Coated Steels to Aluminum through Impact Spot Welding
    Kapil, Angshuman
    Mao, Yu
    Vivek, Anupam
    Daehn, Glenn
    SAE INTERNATIONAL JOURNAL OF MATERIALS AND MANUFACTURING, 2021, 14 (01) : 33 - 44
  • [42] Hybrid resistance-laser spot welding of aluminum to steel dissimilar materials: Microstructure and mechanical properties
    Li, Mingfeng
    Tao, Wu
    Zhang, Jiazhi
    Wang, Yanjun
    Yang, Shanglu
    MATERIALS & DESIGN, 2022, 221
  • [43] Resistance Spot Welding of Zn-Coated Third Generation Automotive Steels Using Mid-Frequency Direct Current Technology
    Baser, Tanya A.
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2023, 76 (01) : 49 - 57
  • [44] The thermal cycle during the dissimilar friction spot welding of aluminum and magnesium alloy
    Suhuddin, U. F. H.
    Fischer, V.
    dos Santos, J. F.
    SCRIPTA MATERIALIA, 2013, 68 (01) : 87 - 90
  • [45] Dissimilar metal joining of aluminum to steel by ultrasonic plus resistance spot welding - Microstructure and mechanical properties
    Lu, Ying
    Mayton, Ellis
    Song, Hyeyun
    Kimchi, Menachem
    Zhang, Wei
    MATERIALS & DESIGN, 2019, 165
  • [46] Joining of Aluminum alloy to dissimilar material using Resistance spot welding
    Iwase T.
    Okuda M.
    Keikinzoku/Journal of Japan Institute of Light Metals, 2022, 72 (06): : 395 - 402
  • [47] Resistance Spot Welding of Zn-Coated Third Generation Automotive Steels Using Mid-Frequency Direct Current Technology
    Tanya A. Başer
    Transactions of the Indian Institute of Metals, 2023, 76 : 49 - 57
  • [48] Laser welding of zinc coated steel: an alternative to resistance spot welding
    Dasgupta, A. K.
    Mazumder, J.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2008, 13 (03) : 289 - 293
  • [49] Resistance Spot Welding between Steel and Aluminum Alloy
    Cui, Lihu
    Qiu, Ranfeng
    Hou, LongLong
    Shen, Zhongbao
    Li, Qingzhe
    PROCEEDINGS OF THE 5TH INTERNATIONAL CONFERENCE ON ADVANCED DESIGN AND MANUFACTURING ENGINEERING, 2015, 39 : 777 - 781
  • [50] Investigations on the Oxidation of Zn-coated Steel Cables
    Pinto, G.
    Silva, F. J. G.
    Baptista, A.
    Campilho, R. D. S. G.
    Viana, F.
    FME TRANSACTIONS, 2021, 49 (03): : 587 - 597
12345