Synthesis and in vitro degradation of novel copolymers of cyclic carbonate and D,L-lactide

被引：0
|
作者：
Xu, Jian [1 ]
Liu, Zhi-Lan [1 ]
Zhuo, Ren-Xi [1 ]
机构：
[1] Department of Chemistry, Wuhan University, Ministry of Education, Wuhan 430072, China
来源：
Journal of Applied Polymer Science | 2006年 / 101卷 / 03期
关键词：
Cyclic carbonate 9-phenyl-2,4,8,10-tetraoxaspiro-[5,5]undcane-3-one is a six-membered carbonate monomer with a rigid side group. Novel biodegradable poly(carbonate-ester), poly(9-phenyl-2,4,8,10-tetraoxaspiro[5,5]undecan-3-one- co-D,L-lactide) P(CC-co-DLLA), was synthesized by ring-opening polymerization in bulk, using stannous octanoate catalyst. Effects of polymerization conditions such as catalyst concentration, reaction time, and reaction temperature on the polymerization were investigated. The structure of the copolymers was characterized by FTIR, 1H NMR, and 13C NMR. Their molecular weights and polydispersity index were determined by gel permeation chromatography. The protecting benzyl ketal group was removed subsequently by catalytic hydrogenation to give a poly(carbonate-ester) containing pendant hydroxyl groups. The in vitro degradation of the copolymers was performed at (37 ±0.5)°C in two media: phosphate buffer solution (pH 7.4) or Tris-HCl buffer solution (pH 8.6) in the presence of proteinase K. The degradation rate can be regulated by adjusting the composition of two monomers. The pendant hydroxyl groups in the copolymers resulted in a prominent enhancement of the degradation rate in PBS. © 2006 Wiley Periodicals, Inc;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：1988 / 1994
相关论文
共 50 条
  • [31] Polyethylene-poly(L-lactide) diblock copolymers: Synthesis and compatibilization of poly(L-lactide)/polyethylene blends
    Wang, YB
    Hillmyer, MA
    JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 2001, 39 (16) : 2755 - 2766
  • [32] Preparation and degradation properties of hydroxyethyl chitosan-g-poly(D,L-lactide) copolymers
    Luo, Bing-hong
    Li, Jian-hua
    Xu, Wan
    Zhou, Chang-ren
    ADVANCED MATERIALS AND ENGINEERING MATERIALS, PTS 1 AND 2, 2012, 457-458 : 308 - +
  • [33] Influence of Chain Microstructure on the Hydrolytic Degradation of Copolymers from 1,3-Trimethylene Carbonate and L-Lactide
    Hua, Jiajie
    Gebarowska, Katarzyna
    Dobrzynski, Piotr
    Kasperczyk, Janusz
    Wei, Jia
    Li, Suming
    JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 2009, 47 (15) : 3869 - 3879
  • [34] Synthesis and characterization of novel ABA triblock copolymers from L-lactide, glycolide, and PEG
    Mohammadi-Rovshandeh, J
    Farnia, SMF
    Sarbolouki, MN
    JOURNAL OF APPLIED POLYMER SCIENCE, 1999, 74 (08) : 2004 - 2009
  • [35] SYNTHESIS AND HYDROLYTIC DEGRADATION BEHAVIOR OF HIGH-MOLECULAR-WEIGHT L-LACTIDE AND GLYCOLIDE COPOLYMERS
    GRIJPMA, DW
    NIJENHUIS, AJ
    PENNINGS, AJ
    POLYMER, 1990, 31 (11) : 2201 - 2206
  • [36] Microwave irradiation: A novel method for rapid synthesis of D,L-lactide
    Zhang, Ying Min
    Wang, Peng
    Han, Ning
    Lei, Hai Fen
    MACROMOLECULAR RAPID COMMUNICATIONS, 2007, 28 (04) : 417 - 421
  • [37] Plasticization of Poly-L-lactide with L-Lactide, D-Lactide, and D,L-Lactide Monomers
    Lopez-Rodriguez, N.
    Sarasua, J. R.
    POLYMER ENGINEERING AND SCIENCE, 2013, 53 (10): : 2073 - 2080
  • [38] Synthesis and characterization of novel biodegradable triblock copolymers from L-lactide, glycolide, and PPG
    Farnia, SMF
    Mohammadi-Rovshandeh, J
    Sarbolouki, MN
    JOURNAL OF APPLIED POLYMER SCIENCE, 1999, 73 (05) : 633 - 637
  • [39] Hydrolytic degradation of cellulose-graft-poly(L-lactide) copolymers
    Yan, Chenghu
    Wu, Jin
    Zhang, Jinming
    He, Jiasong
    Zhang, Jun
    POLYMER DEGRADATION AND STABILITY, 2015, 118 : 130 - 136
  • [40] Synthesis of Poly(ethylene glycol)/Polypeptide/Poly(D,L-lactide) Copolymers and Their Nanoparticles
    Lee, Hyunpyo
    Park, Jun Beum
    Chang, Ji Young
    JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 2011, 49 (13) : 2859 - 2865
12345