Sol-gel-derived alumina/polyvinylpyrrolidone hybrid nanocomposite film on metal for corrosion resistance

被引：0
|
作者：
Jing, Chengbin [1 ]
Hou, Jinxia [1 ]
机构：
[1] College of Materials and Engineering, Qingdao University of Science and Technology, Qingdao 266042, China
来源：
Journal of Applied Polymer Science | 2007年 / 105卷 / 02期
关键词：
With the addition of polyvinylpyrrolidone (PVP); alumina sol with an aluminum sec-butoxide/water molar ratio of 1 : 45 was synthesized. The surface tension of this alumina sol was found to be lower by 35% than the sol without PVP. Alumina/PVP hybrid film with a critical thickness up to 2 μm was fabricated by dip-coating method. The heat treatment between 200 and 300°C could produce a film with perfect hybrid nanocomposite structures. Alumina particles with a size of about 20 nm were uniformly distributed in this material. The hardness of the film samples increased with the increment of heat treatment temperature; and hardness values higher than the original metal were detected after heat treated above 400°C. The film-coated metals that were heat treated below 150°C or above 400°C exhibited relatively weak adhesion; but strong adhesion was obtained when heat treated between 200 and 300°C for 30 min. The corrosion rate of the film-coated metal that was heat treated between 200°C and 300°C for 30 min was lower by 95% than the uncoated metal. © 2007 Wiley Periodicals; Inc;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：697 / 705
相关论文
共 50 条
  • [41] Corrosion resistance of sol-gel alumina coated Mg metal in 3.5 % NaCl solution
    Singh, I. B.
    Gupta, Prasant
    Maheshwari, Arpit
    Agrawal, Naveen
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2015, 73 (01) : 127 - 132
  • [42] Sol-gel-derived hybrid materials multi-doped with rare-earth metal ions
    Zelazowska, E.
    Rysiakiewicz-Pasek, E.
    Borczuch-Laczka, M.
    Cholewa-Kowalska, K.
    MATERIALS SCIENCE-POLAND, 2012, 30 (02): : 105 - 120
  • [43] Effects of annealing temperature, ambient humidity and temperature on dielectric properties of sol-gel-derived amorphous alumina thin film
    Su, Zhen
    Yao, Manwen
    Chen, Jianwen
    Yao, Xi
    JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2017, 28 (16) : 12356 - 12362
  • [44] Direct electrochemistry and electrocatalysis of horseradish peroxidase immobilized in sol-gel-derived ceramic-carbon nanotube nanocomposite film
    Chen, Hongjun
    Dong, Shaojun
    BIOSENSORS & BIOELECTRONICS, 2007, 22 (08): : 1811 - 1815
  • [45] A Comparative Study of Solvothermal and Sol-Gel-Derived Nanocrystalline Alumina Catalysts for Ethanol Dehydration
    Wannaborworn, Mingkwan
    Praserthdam, Piyasan
    Jongsomjit, Bunjerd
    JOURNAL OF NANOMATERIALS, 2015, 2015
  • [46] Inhibitory effect of alumina additive on the titania phase transformation of a sol-gel-derived powder
    Yang, J
    Huang, YX
    Ferreira, JMF
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1997, 16 (23) : 1933 - 1935
  • [47] Effect of Incorporation of Silver on the Electrical Properties of Sol-Gel-Derived Titania Film
    Li, Hong
    Zhao, Gaoling
    Song, Bin
    Han, Gaorong
    JOURNAL OF CLUSTER SCIENCE, 2008, 19 (04) : 667 - 673
  • [48] Lanthanide-doped sol-gel-derived films fabricated in mesoporous anodic alumina
    Molchan, IS
    Gaponenko, NV
    Thompson, GE
    JOURNAL OF THE SOCIETY FOR INFORMATION DISPLAY, 2005, 13 (04) : 295 - 299
  • [49] Sol-Gel-Derived Epitaxial Nanocomposite Thin Films with Large Sharp Magnetoelectric Effect
    Liu, Bin
    Sun, Tao
    He, Jiaqing
    Dravid, Vinayak P.
    ACS NANO, 2010, 4 (11) : 6836 - 6842
  • [50] Selective growth of ZnO nanorods by patterning of sol-gel-derived thin film
    Kwon, S. Joon
    Park, Jae-Hwan
    Park, Jae-Gwan
    JOURNAL OF ELECTROCERAMICS, 2006, 17 (2-4) : 455 - 459
12345