Flexible and lightweight metalized polyamide nonwoven for electromagnetic interference shielding, electrothermal, photothermal, and antibacterial applications

被引：0
|
作者：
Khajeh, Ehsan [1 ]
Nasouri, Komeil [1 ]
Askari, Gholamreza [2 ]
Mandegari, Mansoor [1 ]
机构：
[1] Department of Textile Engineering, Isfahan University of Technology, Isfahan, Iran
[2] Information & Communication Technology Institute, Isfahan University of Technology, Isfahan, Iran
来源：
Chemical Engineering Journal | 1600年 / 502卷
关键词：
The adoption of multifunctional nonwovens (NWs); which have more than one primary use; is increasing worldwide. In this paper; metalized nylon 6 NWs are prepared using nickel–phosphor (Ni-P) plating for electromagnetic shielding; electrothermal; photothermal; and antibacterial applications. The sensitized and activated NWs are deposited in an electroless nickel plating for different durations. The deposition amount increased in the electroless plating process from 1 to 8 min. Afterward; the precipitation rate of Ni-P particles decreases; and the coated surface of the NWs also becomes non-uniform. Surface morphology and elemental analysis mapping showed that Ni-P particles are uniformly deposited on surfaces of Ni-P/NWs with 8 min electroless plating. As a result; it is shown that the sample with 8 min electroless plating is the optimal and best sample to use in the shielding effectiveness of 55.4 dB; and specific shielding of 490.27 dB.cm3.g−1. Also; the optimal specimen has the best electrothermal application with an average maximum temperature of 133.5 °C at 5 V with relative preservation of the necessary properties of the fabric; compared to other prepared samples. Also; this optimal fabric in the photothermal performance; reaches an average maximum temperature of 77.9 °C in 800 mW/cm2. The optimal sample shows significant antibacterial efficiency against E. coli and S. aureus bacteria and reaches 62.70 ± 0.20 and 88.30 ± 1.30 % under light irradiation; respectively. The results show that the optimal sample with great washing durability can perform very well in cold environments and exhibit excellent shielding; and photothermal performances which can be used as lightweight electro-heating and shielding fabrics. © 2024 Elsevier B.V;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [41] SPECIFICATION FOR FLEXIBLE CONDUIT FOR ELECTROMAGNETIC INTERFERENCE SHIELDING
    PRYSNER, WJ
    IEEE ELECTROMAGNETIC COMPATIBILITY SYMPOSIUM RECORD, 1970, (12): : 97 - &
  • [42] Facile Preparation of a Lightweight and Ultra-Thin Nonwoven Carbon Fiber Film with Excellent Electromagnetic Interference Shielding Performance
    Bai, Ruicheng
    Li, Xiaolin
    Zhang, Leilei
    Liu, Shaohua
    Zhang, Pei
    Shao, Qinsi
    JOURNAL OF NANOELECTRONICS AND OPTOELECTRONICS, 2023, 18 (05) : 441 - 451
  • [43] Lightweight and highly conductive silver nanoparticles functionalized meta-aramid nonwoven fabric for enhanced electromagnetic interference shielding
    Zhou, Yanfen
    Li, Wenyue
    Li, Lele
    Sun, Zhenhua
    Jiang, Liang
    Ma, Jianwei
    Chen, Shaojuan
    Ning, Xin
    Zhou, Feng-Lei
    JOURNAL OF MATERIALS SCIENCE, 2021, 56 (10) : 6499 - 6513
  • [44] Lightweight and highly conductive silver nanoparticles functionalized meta-aramid nonwoven fabric for enhanced electromagnetic interference shielding
    Yanfen Zhou
    Wenyue Li
    Lele Li
    Zhenhua Sun
    Liang Jiang
    Jianwei Ma
    Shaojuan Chen
    Xin Ning
    Feng-Lei Zhou
    Journal of Materials Science, 2021, 56 : 6499 - 6513
  • [45] Highly Stable, Flexible, Anticorrosive Coating of Metalized Nonwoven Textiles for Durable EMI Shielding and Thermal Properties
    Khan, Muhammad Zaman
    Taghavian, Hadi
    Zhang, Xiuling
    Militky, Jiri
    Ali, Azam
    Wiener, Jakub
    Tunakova, Veronika
    Venkataraman, Mohanapriya
    Dvorak, Lukas
    ACS OMEGA, 2025, 10 (08): : 8127 - 8139
  • [46] Flexible MXene/Nanocellulose Composite Aerogel Film with Cellular Structure for Electromagnetic Interference Shielding and Photothermal Conversion
    Ma, Chang
    Mai, Tian
    Wang, Pei-Lin
    Guo, Wen-Yan
    Ma, Ming-Guo
    ACS APPLIED MATERIALS & INTERFACES, 2023, 15 (40) : 47425 - 47433
  • [47] Flexible multilayer MXene/Polyimide composite film with excellent electromagnetic interference shielding and photothermal conversion performance
    Chen, Jinqiu
    Hu, Xingman
    Nie, Zhuguang
    Feng, Yang
    Qi, Shuhua
    Wang, Rumin
    JOURNAL OF ALLOYS AND COMPOUNDS, 2024, 990
  • [48] Flexible, lightweight and multi-level superimposed titanium carbide films for enhanced electromagnetic interference shielding
    Zhao, Weiwei
    Xu, Haotian
    Zhao, Junde
    Zhu, Xianjun
    Lu, Yuyuan
    Ding, Chengbo
    He, Wenjun
    Bian, Jing
    Liu, Leilei
    Ma, Linfeng
    Wang, Weikang
    Zhou, Tongqing
    Zhou, Xingcheng
    Li, Jianmin
    Liu, Shujuan
    Zhao, Qiang
    CHEMICAL ENGINEERING JOURNAL, 2022, 437
  • [49] Lightweight and Flexible MXene/rGO Thermally Expanded Foams for High-Efficiency Electromagnetic Interference Shielding
    Liao, Si-Yuan
    Wang, Xiao-Yun
    Li, Xing-Miao
    Wan, Yan-Jun
    zhu, Pengli
    Sun, Rong
    2020 21ST INTERNATIONAL CONFERENCE ON ELECTRONIC PACKAGING TECHNOLOGY (ICEPT), 2020,
  • [50] Gradient structure design of lightweight and flexible silicone rubber nanocomposite foam for efficient electromagnetic interference shielding
    Yang, Jianming
    Liao, Xia
    Wang, Gui
    Chen, Jia
    Guo, Fumin
    Tang, Wanyu
    Wang, Wei
    Yan, Zhihui
    Li, Guangxian
    CHEMICAL ENGINEERING JOURNAL, 2020, 390
12345