Flexible and lightweight metalized polyamide nonwoven for electromagnetic interference shielding, electrothermal, photothermal, and antibacterial applications

被引：0
|
作者：
Khajeh, Ehsan [1 ]
Nasouri, Komeil [1 ]
Askari, Gholamreza [2 ]
Mandegari, Mansoor [1 ]
机构：
[1] Department of Textile Engineering, Isfahan University of Technology, Isfahan, Iran
[2] Information & Communication Technology Institute, Isfahan University of Technology, Isfahan, Iran
来源：
Chemical Engineering Journal | 1600年 / 502卷
关键词：
The adoption of multifunctional nonwovens (NWs); which have more than one primary use; is increasing worldwide. In this paper; metalized nylon 6 NWs are prepared using nickel–phosphor (Ni-P) plating for electromagnetic shielding; electrothermal; photothermal; and antibacterial applications. The sensitized and activated NWs are deposited in an electroless nickel plating for different durations. The deposition amount increased in the electroless plating process from 1 to 8 min. Afterward; the precipitation rate of Ni-P particles decreases; and the coated surface of the NWs also becomes non-uniform. Surface morphology and elemental analysis mapping showed that Ni-P particles are uniformly deposited on surfaces of Ni-P/NWs with 8 min electroless plating. As a result; it is shown that the sample with 8 min electroless plating is the optimal and best sample to use in the shielding effectiveness of 55.4 dB; and specific shielding of 490.27 dB.cm3.g−1. Also; the optimal specimen has the best electrothermal application with an average maximum temperature of 133.5 °C at 5 V with relative preservation of the necessary properties of the fabric; compared to other prepared samples. Also; this optimal fabric in the photothermal performance; reaches an average maximum temperature of 77.9 °C in 800 mW/cm2. The optimal sample shows significant antibacterial efficiency against E. coli and S. aureus bacteria and reaches 62.70 ± 0.20 and 88.30 ± 1.30 % under light irradiation; respectively. The results show that the optimal sample with great washing durability can perform very well in cold environments and exhibit excellent shielding; and photothermal performances which can be used as lightweight electro-heating and shielding fabrics. © 2024 Elsevier B.V;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [1] Flexible and lightweight metalized polyamide nonwoven for electromagnetic interference shielding, electrothermal, photothermal, and antibacterial applications
    Khajeh, Ehsan
    Nasouri, Komeil
    Askari, Gholamreza
    Mandegari, Mansoor
    CHEMICAL ENGINEERING JOURNAL, 2024, 502
  • [2] Flexible metalized polyimide nonwoven fabrics for efficient electromagnetic interference shielding
    Tang, Xinwei
    Zhao, Xu
    Lu, Yezi
    Li, Shuangshuang
    Zhang, Zihang
    Zhu, Mingyang
    Yao, Kaiqing
    Zheng, Jianxing
    Chen, Haijun
    Duan, Yiqian
    Qiao, Yunlong
    Wang, Zicheng
    Liu, Tianxi
    CHEMICAL ENGINEERING JOURNAL, 2024, 480
  • [3] Flexible electrospun carbon nanofibers/silicone composite films for electromagnetic interference shielding, electrothermal and photothermal applications
    Li, Zhenwei
    Lin, Zijia
    Han, Meisheng
    Mu, Yongbiao
    Yu, Pengpeng
    Zhang, Yunlong
    Yu, Jie
    CHEMICAL ENGINEERING JOURNAL, 2021, 420
  • [4] Lightweight and Flexible Structures for Electromagnetic Interference Shielding - Present State
    Safarova, Veronika
    Militky, Jiri
    2015 38TH INTERNATIONAL CONFERENCE ON TELECOMMUNICATIONS AND SIGNAL PROCESSING (TSP), 2015, : 257 - 261
  • [5] Mathematical modeling for electromagnetic shielding effectiveness characterization of metalized nonwoven fabrics
    Hu, Shi
    Wang, Dan
    Kremenakova, Dana
    Militky, Jiri
    JOURNAL OF INDUSTRIAL TEXTILES, 2023, 53
  • [6] Progress in polymer nonwoven textile materials in electromagnetic interference shielding applications
    Jonathan Tersur Orasugh
    Orebotse Joseph Botlhoko
    Lesego Tabea Temane
    Suprakas Sinha Ray
    Functional Composite Materials, 5 (1):
  • [7] Lightweight MXene-coated cotton textiles with electromagnetic interference shielding, electrothermal/photothermal conversion and self-cleaning properties
    Zeng, Qi
    Su, Juanjuan
    Han, Jian
    CELLULOSE, 2025, : 2717 - 2733
  • [8] Highly efficient electromagnetic interference shielding composite with excellent superhydrophobic and photothermal/electrothermal effects
    Mei, Jie
    Liao, Huimin
    Hou, Minghuan
    Wang, Jian
    COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2024, 682
  • [9] Lightweight and flexible conducting polymer sponges and hydrogels for electromagnetic interference shielding
    Sarkar, Biporjoy
    Li, Xinda
    Quenneville, Eric
    Carignan, Louis-Philippe
    Wu, Ke
    Cicoira, Fabio
    JOURNAL OF MATERIALS CHEMISTRY C, 2021, 9 (46) : 16558 - 16565
  • [10] Ultrahigh electromagnetic interference shielding performance of lightweight, flexible, and highly conductive copper-clad carbon fiber nonwoven fabrics
    Lee, Jinpyo
    Liu, Yanan
    Liu, Yang
    Park, Soo-Jin
    Park, Mira
    Kim, Hak Yong
    JOURNAL OF MATERIALS CHEMISTRY C, 2017, 5 (31) : 7853 - 7861
12345