Mechanically induced crystallization of an amorphous CoFeZrB alloy

被引：0

作者：

Bednarčík, J. ^{[1
,3
]}

Burkel, E. ^{[1
]}

Saksl, K. ^{[2
]}

Kollár, P. ^{[3
]}

Roth, S. ^{[4
]}

机构：

[1] Institute of Physics, University of Rostock, August-Bebel-Straße 55, D-18055 Rostock, Germany

[2] Deutsches Elektronen Synchrotron (HASYLAB), Notkestraße 85, D-22607 Hamburg, Germany

[3] Department of Condensed Matter Physics, Faculty of Science, P.J. Šafárik University, Park Angelinum 9, 041 54 Košice, Slovakia

[4] IFW Dresden, Institut für Metalische Werkstoffe, Helmholtzstraße 20, D-01069 Dresden, Germany

来源：

Journal of Applied Physics | 2006年 / 100卷 / 01期

关键词：

The short-time (12 h) ball milling of the amorphous Co56Fe 16Zr8B20 (at. %) alloy resulted in the formation of bcc-Fe nanocrystals embedded in an amorphous matrix. X-ray diffraction (XRD) using synchrotron radiation; differential scanning calorimetry (DSC); vibrating sample magnetometery (VSM); and the Faraday magnetic balance experiments were used to characterize the materials. XRD and DSC show that the fraction of crystallized bcc-Fe gradually increases with the milling time. The VSM measurements confirm the structure observations showing that the saturation magnetization increases with the milling time as the fraction of crystallized bcc-Fe increases. After 12 h of milling; the powder sample exhibited a Curie temperature of the amorphous phase TCam; which is approximately 55 K higher compared to the as-quenched ribbon (TC am=601 K). Thermomagnetic measurements of heat-treated ribbons suggest that such an increase in TCam is not only due to temperature rises during the milling but may also be attributed to the combination of mechanical and thermal effects connected with the nature of milling. © 2006 American Institute of Physics;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

共 50 条

[31] CRYSTALLIZATION OF AN AMORPHOUS ALUMINUM-PALLADIUM ALLOY
SASTRY, GVS
SURYANARAYANA, C
SRIVASTAVA, CN
DAVIES, HA
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1978, 31 (5-6): : 292 - &
[32] Isothermal Crystallization Kinetics of an Amorphous CuTi Alloy
苗卫方
李淑苓
王景唐
Journal of Materials Science & Technology, 1992, (03) : 197 - 203
[33] SURFACE CRYSTALLIZATION OF AMORPHOUS ALLOY METGLAS 2826
PREGGER, BA
KRAMER, JJ
IEEE TRANSACTIONS ON MAGNETICS, 1989, 25 (05) : 3333 - 3335
[34] CHARACTERIZATION OF CRYSTALLIZATION IN AMORPHOUS 2605 SC ALLOY
INAL, OT
SCHERER, A
REINEKE, EG
BORDEN, MJ
THIN SOLID FILMS, 1984, 119 (04) : 395 - 412
[35] EVIDENCE OF A SEQUENTIAL CRYSTALLIZATION IN A TERNARY AMORPHOUS ALLOY
RZEPSKI, J
HARMELIN, M
CHEVALIER, JP
JOURNAL DE MICROSCOPIE ET DE SPECTROSCOPIE ELECTRONIQUES, 1985, 10 (02): : A14 - A14
[36] Research on Crystallization Start Diagram for Amorphous Alloy
Li Bo
Xia Chun
He Kelong
Long Wenyuan
Li Zhiyuan
RARE METAL MATERIALS AND ENGINEERING, 2009, 38 (03) : 447 - 450
[37] CRYSTALLIZATION AND GRAIN GROWTH IN AMORPHOUS ALLOY FILMS
MADER, S
JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1969, 116 (08) : C295 - &
[38] EARLY CRYSTALLIZATION BEHAVIOR OF AN AMORPHOUS METAL ALLOY
MORRIS, DG
SCRIPTA METALLURGICA, 1982, 16 (05): : 585 - 588
[39] CRYSTALLIZATION OF AN AMORPHOUS CU-ZR ALLOY
VITEK, JM
VANDERSANDE, JB
GRANT, NJ
ACTA METALLURGICA, 1975, 23 (02): : 165 - 176
[40] CRYSTALLIZATION STUDY OF AN AMORPHOUS ALUMINUM - BASED ALLOY
CHENAL, B
DUBOIS, JM
BILDE, A
VENTURINI, G
COMPTES RENDUS DE L ACADEMIE DES SCIENCES SERIE II, 1987, 304 (10): : 501 - &

← 1 2 3 4 5 →