An examination of the fatigue characteristics of aluminum alloy composite high pressure tanks (The effect of prestrain on the fatigue characteristics of age-hardened aluminum alloy)

被引：0

作者：

Ikematsu, Koji ^{[1
]}

Kang, Min-Woo ^{[1
]}

Aono, Yuuta ^{[1
]}

Noguchi, Hiroshi ^{[1
]}

机构：

[1] Department of Mechanical Engineering, Kyushu University, 744 Moto oka, Nishi-ku, Fukuoka shi, Fukuoka, 819 0395, Japan

来源：

Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A | 2009年 / 75卷 / 752期

关键词：

Grain growth - Hardening - Fatigue crack propagation - Bending tests - Tanks (containers) - Fatigue testing - High pressure effects - Precipitation (chemical);

D O I：

10.1299/kikaia.75.446

中图分类号：

学科分类号：

摘要：

Spinning process and pretension treatment are used for Al-Alloy composite tanks. The spinning process develops coarsened grains and the pretension treatment shears precipitation particles. These changes of material properties is considered to affect the fatigue characteristics of age-hardened metals, such as Al alloy 6061-TO. In this study, the effect of the prestrain and grain size on fatigue crack growth characteristic of age-hardened Al-alloy 6061-T6 was investigated. Fatigue tests were performed with a rotating bending fatigue test machine. The specimen with an artificial hole were prepared to observe mode I fatigue crack. Coarse grained plain specimens were used for observation of mode II fatigue crack. Mode I fatigue crack growth rates were decelerated a little by the pretension in the stable crack growth region. But in the case of mode II fatigue crack, the crack growth rates of prestrained specimens became about ten times faster than those of the nonpres. trained specimens. The observation of the fatigue process showed that the slip bands due to prestrain accelerate the mode II crack growth. The specimens taken from a real high pressure tank showed similar crack growth characteristics.

引用

页码：446 / 454

共 50 条

[11] Fatigue Resistance of Dispersion-Hardened Aluminum Alloy
Mylnikov, V. V.
Zakharychev, E. A.
Pronin, A. I.
Mylnikova, M. V.
Shetulova, T. G.
METAL SCIENCE AND HEAT TREATMENT, 2024, 66 (1-2) : 25 - 31
[12] FATIGUE BEHAVIOR OF COMPOSITE PRESSURE VESSELS WITH ALUMINUM ALLOY LINERS
Kim, S-T
Lee, K-M
Park, J-S
COMPOSITE MATERIALS FOR STRUCTURAL PERFORMANCE: TOWARDS HIGHER LIMITS, 2011, : 351 - 358
[13] Effect of Humidity on Fatigue Strength of Age-hardened Al Alloy under Rotating Bending
Kawagoishi, N.
Kariya, K.
Nu, Y.
Furumoto, S.
Kondo, E.
ADVANCES IN FRACTURE AND DAMAGE MECHANICS IX, 2011, 452-453 : 745 - +
[14] INFLUENCE OF STRUCTURE HETEROGENEITY ON FATIGUE-STRENGTH OF AGE-HARDENED ALLOY
KRASAVIN, DL
SUKHOVAROV, VF
STROKATOV, RD
IZVESTIYA VYSSHIKH UCHEBNYKH ZAVEDENII FIZIKA, 1989, 32 (02): : 86 - 91
[15] High cycle fatigue characteristics of 2124-T851 aluminum alloy
Li X.
Yin Z.
Nie B.
Zhong L.
Pan Q.
Jiang F.
Frontiers of Materials Science in China, 2007, 1 (2): : 168 - 172
[16] Nonlinear acoustic characteristics of fatigue cracks in aluminum alloy sheet
Department of Material Science and Engineering, Harbin University Science and Technology, Harbin 150040, China
不详
不详
Jixie Gongcheng Xuebao, 18 (71-76):
[17] Influence of microstructure characteristics on the fatigue properties of 7075 aluminum alloy
Jin, J. W.
Zhang, Z. J.
Hou, J. P.
Gong, B. S.
Wang, H. W.
Zhou, X. H.
Purcek, G.
Sheinerman, A. G.
Zhang, Z. F.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2024, 912
[18] EFFECT OF A FATIGUE CRACK ON FATIGUE STRENGTH OF AN ALUMINUM ALLOY
BENNETT, JA
MATERIALS RESEARCH AND STANDARDS, 1965, 5 (05): : 235 - &
[19] Fatigue performance of high pressure waterjet peened aluminum alloy
2000, American Society of Mechanical Engineers (406):
[20] Effect of humidity on fatigue strength of extruded and age-hardened Al alloy under rotating bending
Daiichi Univ. Coll. Tech., Kokubu-chuo, Kirishima, 899-4395, Japan
不详
Zairyo, 4 (339-344):

← 1 2 3 4 5 →