Dynamic mechanical and thermal behavior of liquid-crystalline polybutadiene-diols with mesogenic groups in side chains

被引：0

作者：

Jigounov, Alexander ^{[1
]}

Sedláková, Zdeňka ^{[2
]}

Spěváček, Jiří ^{[2
]}

Ilavský, Michal ^{[1
,2
]}

机构：

[1] Faculty of Mathematics and Physics, Charles University, V Holesovickach 2, 18000 Prague 8, Czech Republic

[2] Institute of Macromolecular Chemistry, Academy of Sciences of the Czech Republic, 16206 Prague 6, Czech Republic

来源：

European Polymer Journal | 2006年 / 42卷 / 10期

关键词：

Liquid-crystalline polybutadiene-diols (LCPBDs) with the comb-like architecture were synthesized by reaction of a LC thiol with the double bonds of telechelic HO-terminated polybutadiene (PBD). LCPBDs with various initial molar ratios of thiol to double bonds of PBD; R0; in the range from 0.15 to 1; were prepared by the radical reaction at temperature 60 °C for 48 h. The experimentally obtained degree of modification; Re; after the reaction and purification; was determined from elemental analysis - from the amount of sulphur bounded in LCPBDs; GPC and from 1H NMR spectra. The physical properties were investigated by differential scanning calorimetry and dynamic mechanical spectroscopy. With increasing Re ratio the glass transition temperature of LCPBDs; Tg; increases from ∼ - 45 °C (neat PBD) to ∼20 °C (Re ∼ 0.5). LC transition starts at Re ∼ 0.27 (the transition temperature Tm ∼ 27 °C). With increasing Re temperature Tm increases and for Re ∼ 0.5 reaches the value Tm ∼ 74 °C; at the same time also the change in enthalpy at LC transition increases. The LC transition could be detected also by the dynamic mechanical spectroscopy; especially shape and position of mechanical functions on frequency and free volume parameters strongly depend on degree of modification. © 2006 Elsevier Ltd. All rights reserved;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Journal article (JA)

引用

页码：2450 / 2457

共 50 条

[31] Mesogenic polybutadiene diols with thiol side-chain units: synthesis and thermal behaviour
Bubnov, Alexej
Kaspar, Miroslav
Sedlakova, Zdenka
PHASE TRANSITIONS, 2010, 83 (01) : 16 - 27
[32] Thermal and liquid crystalline properties of a polymer with amphiphilic-mesogenic side-chains
Ujiie, S
Yano, Y
Mori, A
ADVANCES IN LIQUID CRYSTALLINE MATERIALS AND TECHNOLOGIES, 2002, 709 : 135 - 140
[33] PREPARATION OF LIQUID-CRYSTALLINE POLYSILOXANES WITH TERMINAL CYANO GROUPS IN THE SIDE-CHAINS
GRAY, GW
LACEY, D
NESTOR, G
WHITE, MS
MAKROMOLEKULARE CHEMIE-RAPID COMMUNICATIONS, 1986, 7 (02): : 71 - 76
[34] Optical properties of liquid-crystalline side-chain polysiloxanes with laterally attached mesogenic groups
Ogawa, H
Stibal-Fischer, E
Finkelmann, H
KOBUNSHI RONBUNSHU, 2004, 61 (06) : 368 - 370
[35] BROWNIAN DYNAMICS OF THE POLYMER-CHAIN HAVING MESOGENIC SIDE GROUPS IN THE LIQUID-CRYSTALLINE STATE
DARINSKII, AA
LYULIN, AV
NEELOV, IM
VYSOKOMOLEKULYARNYE SOEDINENIYA SERIYA A, 1992, 34 (08): : 73 - 83
[36] CHOLESTERIC AND OTHER PHASES IN THERMOTROPIC LIQUID-CRYSTALLINE POLYMERS WITH SIDE-CHAIN MESOGENIC GROUPS
PLATE, NA
FREIDZON, YS
SHIBAEV, VP
PURE AND APPLIED CHEMISTRY, 1985, 57 (11) : 1715 - 1726
[37] Synthesis and properties of side chain cholesteric liquid-crystalline polyacrylates containing two mesogenic groups
Zhang, BY
Hu, JS
Zang, BL
Zhou, AJ
JOURNAL OF APPLIED POLYMER SCIENCE, 2003, 88 (08) : 1936 - 1941
[38] LIQUID-CRYSTALLINE BEHAVIOR OF POLYMERIC GLYCOLS TERMINATED WITH AROMATIC DIESTER AND DIACID MESOGENIC GROUPS
HOSHINO, H
JIN, JI
LENZ, RW
JOURNAL OF APPLIED POLYMER SCIENCE, 1984, 29 (02) : 547 - 554
[39] Preparation and thermal properties of liquid crystalline ionomers having mesogenic ester side chains containing three phenyl groups
Changcheng Wu
Ju-Myung Song
Joon-Seop Kim
Polymer Bulletin, 2013, 70 : 249 - 262
[40] Preparation and thermal properties of liquid crystalline ionomers having mesogenic ester side chains containing three phenyl groups
Wu, Changcheng
Song, Ju-Myung
Kim, Joon-Seop
POLYMER BULLETIN, 2013, 70 (01) : 249 - 262

← 1 2 3 4 5 →