Corrosion Behaviour of Boronized Ductile irons in Formic and Nitric Acid Solutions

被引:0
|
作者
Toktas, Gulcan [1 ]
Korkmaz, Selman [2 ]
机构
[1] Balikesir Univ, Dept Mech Engn, Balikesir, Turkiye
[2] Beycelik Gestamp Co, Prod Engn, Bursa, Turkiye
关键词
FRACTURE-TOUGHNESS; MECHANICAL-PROPERTIES; BORIDE LAYERS; MILD-STEEL; KINETICS; PARAMETERS;
D O I
10.1134/S207020512470182X
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The corrosion behavior of boronized Cu, Ni, and Mo-alloyed and unalloyed ductile irons in two acid solutions was investigated using the gravimetric method. Ductile irons were pack boronized at 900 and 950 degrees C for 2, 4, 6, and 8 h. The boride-layer compounds were detected using X-ray analysis. Boronized and untreated irons were immersed in 10 wt % formic acid and 10 wt % nitric acid solutions for 14 days (336 h). Every two days, mass losses were measured, and corrosion rates were estimated using these results. The corroded surfaces were examined with scanning electron microscopy. Untreated alloyed ductile cast iron lost less mass in both acid solutions than unalloyed cast iron. Pitting is the most common type of corrosion in formic acid solution. Higher corrosion rates after 48 h of immersion decreased dramatically in 96 h for all irons due to the passivation effect of the nitric acid solution.
引用
收藏
页码:535 / 543
页数:9
相关论文
共 50 条
  • [31] THE VAPOUR PRESSURES OF NITRIC ACID SOLUTIONS .2. THE BEHAVIOUR OF SOLUTES IN NITRIC ACID
    LLOYD, L
    WYATT, PAH
    JOURNAL OF THE CHEMICAL SOCIETY, 1957, (OCT): : 4268 - 4274
  • [32] Liquid crystalline behaviour of chitosan in formic, acetic, and monochloroacetic acid solutions
    Prabaharan, M.
    Borges, J. P.
    Godinho, M. H.
    Mano, J. F.
    ADVANCED MATERIALS FORUM III, PTS 1 AND 2, 2006, 514-516 : 1010 - 1014
  • [33] Corrosion Behaviour of Mild Steel in a Glacial Acetic-Formic Acid System
    Singh, S. K.
    Mukherjee, A. K.
    Singh, M. M.
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2024, 77 (06) : 1481 - 1488
  • [34] Electrochemical Corrosion Evaluation of Copper-Alloyed Ductile Cast Irons
    Brito, P.
    Pereira, W.
    Santos, W.
    Comes, H.
    ARCHIVES OF FOUNDRY ENGINEERING, 2020, 20 (02) : 26 - 30
  • [35] ION EXCHANGE BEHAVIOUR OF NEPTUNIUM IN NITRIC ACID SOLUTIONS
    STEINWAN.H
    BOBLETER, O
    HECHT, F
    MONATSHEFTE FUR CHEMIE, 1971, 102 (05): : 1351 - &
  • [36] Behaviour of titanium in nitric-hydrofluoric acid solutions
    Sutter, E.M.M., 1600, (30): : 4 - 5
  • [37] Corrosion Resistance Behaviour of Duplex (α β) Brass in Nitric Acid Concentrations
    Loto, C. A.
    Loto, R. T.
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2012, 7 (12): : 12021 - 12033
  • [38] A comparison of the corrosion behaviour of copper materials in dilute nitric acid
    Dobkowska, Anna
    Castillo, Millicent Dayle H.
    Turnbull, Joseph P.
    Ramamurthy, Sridhar
    Zagidulin, Dmitrij
    Moser, Desmond E.
    Behazin, Mehran
    Keech, Peter G.
    Shoesmith, David W.
    Noel, James J.
    CORROSION SCIENCE, 2021, 192 (192)
  • [39] Corrosion Behaviour of Heat Treated Duplex (αβ) Brass in Nitric Acid
    C. A. Loto
    R. T. Loto
    Silicon, 2018, 10 : 2877 - 2888
  • [40] Corrosion Behaviour of Heat Treated Duplex (αβ) Brass in Nitric Acid
    Loto, C. A.
    Loto, R. T.
    SILICON, 2018, 10 (06) : 2877 - 2888