Size-dependent pitting corrosion behavior for L12-strengthened high-entropy alloys

被引：0
|
作者：
Li, Tianrun [1 ,2 ]
Wang, Debin [1 ]
Cui, Jingping [1 ]
Li, Ning [3 ]
Zhang, Suode [1 ]
Wang, Jianqiang [1 ]
机构：
[1] Shenyang National Laboratory for Materials Science, Institute of Metal Research, CAS, Shenyang,110016, China
[2] School of Materials Science and Engineering, University of Science and Technology of China, Shenyang,110016, China
[3] Shi-changxu Innovation Center for Advanced Materials, Institute of Metal Research, CAS, Shenyang,110016, China
来源：
Corrosion Science | 2025年 / 245卷
关键词：
Corrosion resistant alloys;
D O I：
10.1016/j.corsci.2025.112679
中图分类号：
学科分类号：
摘要：
This work thoroughly investigated the effects of the L12 size upon the corrosion behavior for L12-strengthened HEAs. Compared with the single-phase homogenized HEA, HEAs strengthened by small-sized L12 exhibited higher pitting potential (Epit). Nevertheless, with the L12 coarsening, Epit decreases markedly. The exceptional corrosion behavior for small-sized L12-strengthened HEAs was attributed to the rapid repassivation of the remaining FCC matrix after the complete dissolution of L12, forming the uniform and Cr-enriched films. The deteriorated corrosion resistance induced by the larger L12 was ascribed to heterogeneous films due to the incomplete dissolution of L12 and the reduced pitting growth resistance. © 2025 Elsevier Ltd
引用
收藏
相关论文
共 50 条
  • [1] L12-strengthened high-entropy alloys for advanced structural applications
    Tao Yang
    Yilu Zhao
    Weihong Liu
    Jijung Kai
    Chaintsuan Liu
    Journal of Materials Research, 2018, 33 : 2983 - 2997
  • [2] L12-strengthened high-entropy alloys for advanced structural applications
    Yang, Tao
    Zhao, Yilu
    Liu, Weihong
    Kai, Jijung
    Liu, Chaintsuan
    JOURNAL OF MATERIALS RESEARCH, 2018, 33 (19) : 2983 - 2997
  • [3] Design of L12-type high-entropy intermetallic compounds from L12-strengthened high-entropy alloys
    Qin, Yuan (qinyuan@njust.edu.cn), 2025, 1010
  • [4] Competition between continuous and discontinuous precipitation in L12-strengthened high-entropy alloys
    Fang, J. Y. C.
    Liu, W. H.
    Luan, J. H.
    Yang, T.
    Wu, Y.
    Fu, M. W.
    Jiao, Z. B.
    INTERMETALLICS, 2022, 149
  • [5] Oxidation behaviors and mechanical properties of L12-strengthened high-entropy alloys at 700?
    Liu, Shaofei
    Kai, Wu
    Hou, Jinxiong
    Zhao, Yilu
    Li, Qian
    Yang, Chin-hua
    Yang, Tao
    Kai, Ji-jung
    CORROSION SCIENCE, 2022, 206
  • [6] Corrosion-resistant L12-strengthened high-entropy alloy with high strength and large ductility
    Zhang, J. Y.
    Chou, T. H.
    Zhou, Y. H.
    Luan, J. H.
    Zhao, Y. L.
    Yang, T.
    CORROSION SCIENCE, 2023, 225
  • [7] High-temperature oxidation behaviors and mechanisms in newly designed L12-strengthened high-entropy alloys
    Hou, Jinxiong
    Tan, Yi
    Liu, Shaofei
    Zhang, Jianyang
    Xiao, Weicheng
    Kong, Haojie
    Li, Qian
    Cao, Boxuan
    Luan, Junhua
    Zhao, Yilu
    Kai, Jijung
    Yang, Tao
    CORROSION SCIENCE, 2022, 208
  • [8] A novel L12-strengthened AlCoCuFeNi high-entropy alloy with both high hardness and good corrosion resistance
    Ren, Yaojia
    Wu, Hong
    Liu, Bin
    Shan, Quan
    Guo, Sheng
    Jiao, Zengbao
    Baker, Ian
    MATERIALS LETTERS, 2023, 331
  • [9] Microstructure and mechanical properties of L12-strengthened CoFeMnNiMo0.2Alx high-entropy alloys
    Xu, Hanqing
    Zhang, Mengdi
    Zhang, Gaimei
    Li, Gong
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2024, 118
  • [10] L12-strengthened heterostructure high-entropy alloys with ultra-high strength over a wide temperature range
    Yuan, J. L.
    Wang, Z.
    Jin, X.
    Han, P. D.
    Qiao, J. W.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2022, 853
12345