Effect of environment polarity on sulfate attack resistance of cementitious materials at low temperature

被引:0
|
作者
Xiao, Jia [1 ]
Meng, Qing-Ye [1 ,2 ]
Guo, Ming-Lei [1 ]
Wu, Ting [1 ]
机构
[1] School of Civil Engineering, Central South University, Changsha, China
[2] Chinese Academy of Inspection and Quarantine Comprehensive Test Center, Beijing, China
来源
关键词
Cementitious materials - Effect of environments - Ground limestone - Polarity - Sulfate-attack resistances - Thaumasite - Thaumasite form of sulfate attack - Thaumasite formation;
D O I
10.3969/j.issn.1001-9731.2015.07.007
中图分类号
学科分类号
摘要
By means of analyzing the effect of glycerol sulfate attack resistance of cement-ground limestone cementitious materials at low temperature(5, 5% Na2SO4), the effect of solvent polarity on thaumasite formation was studied. The results showed that the degree of corrosion of cement-limestone powder specimens aggravated with prolonged, and the corrosion products were mainly thaumasite. The specimens without glycerol fell out at edges and corners obviously, while the glycerol reduced the generation of thaumasite in the corrosion products, and the generation of thaumasite decreased with the increase of glycerol content. Glycerol can reduce the generation of thaumasite in cement-ground limestone cementitious material, and lowering environment polarity of cementitious materials could improve the resistance of cementitious material to thaumasite form of sulfate attack at low temperature. ©, 2015, Journal of Functional Materials. All right reserved.
引用
收藏
页码:07035 / 07038
相关论文
共 50 条
  • [21] Effect of temperature on hydration of cementitious materials
    Schindler, AK
    ACI MATERIALS JOURNAL, 2004, 101 (01) : 72 - 81
  • [22] Investigations of cementitious materials with low temperature SEM
    Göske, J
    Pöllmann, H
    Pankau, HG
    APPLIED MINERALOGY, VOLS 1 AND 2: RESEARCH, ECONOMY, TECHNOLOGY, ECOLOGY AND CULTURE, 2000, : 779 - 782
  • [23] Sulfate resistance of limestone cement concrete exposed to combined chloride and sulfate environment at low temperature
    Sotiriadis, K.
    Nikolopoulou, E.
    Tsivilis, S.
    CEMENT & CONCRETE COMPOSITES, 2012, 34 (08): : 903 - 910
  • [24] Lab and Field Study of Physical Sulfate Attack on Concrete Mixtures with Supplementary Cementitious Materials
    Alyami, Mohammed H.
    Mosavi, Hossein
    Alrashidi, Raid S.
    Almarshoud, Mohammed A.
    Ferraro, Christopher C.
    Riding, Kyle A.
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2021, 33 (01)
  • [25] Monitoring the cementitious materials subjected to sulfate attack with optical fiber excitation Raman spectroscopy
    Yue, Yanfei
    Bai, Yun
    Basheer, P. A. Muhammed
    Boland, John J.
    Wang, Jing Jing
    OPTICAL ENGINEERING, 2013, 52 (10)
  • [26] Thaumasite sulfate attack characteristic of seawater and sea sand concrete with limestone powder in different sulfate environment at low temperature
    Wang, Dehui
    Zhang, Zhiwen
    Chen, Rong
    Wang, Ming
    Chen, Ran
    Weng, Lincheng
    Chen, Longhui
    Fang, Lei
    CONSTRUCTION AND BUILDING MATERIALS, 2024, 437
  • [27] Chemical Mechanisms Involved in the Coupled Attack of Sulfate and Chloride Ions on Low-Carbon Cementitious Materials: An In-Depth Study
    El Inaty, Francois
    Marchetti, Mario
    Quiertant, Marc
    Omikrine Metalssi, Othman
    APPLIED SCIENCES-BASEL, 2023, 13 (21):
  • [28] Degradation resistance of different cementitious materials to phosphoric acid attack at early stage
    Ren, Jie
    Zhang, Lihai
    Walkley, Brant
    Black, Jay R.
    San Nicolas, Rackel
    CEMENT AND CONCRETE RESEARCH, 2022, 151
  • [29] Degradation resistance of different cementitious materials to phosphoric acid attack at early stage
    Ren, Jie
    Zhang, Lihai
    Walkley, Brant
    Black, Jay R.
    San Nicolas, Rackel
    Cement and Concrete Research, 2022, 151
  • [30] Influence of limestone powder particle size on the sulfate resistance of cement-based materials under the coupling effect of time-varying temperature and sulfate attack
    Yang, Yonggan
    Gao, Peng
    Zhan, Binggen
    Yu, Qijun
    Wang, Jingfeng
    Zhang, Yunsheng
    JOURNAL OF BUILDING ENGINEERING, 2024, 98