Characterization of composite materials damage under quasi-static three-point bending test using wavelet and fuzzy C-means clustering

被引：0

|

作者：

Fotouhi, Mohamad ^{[1
]}

Heidary, Hossein ^{[1
]}

Ahmadi, Mehdi ^{[1
]}

Pashmforoush, Farzad ^{[1
]}

机构：

[1] Non-destructive Testing Lab, Department of Mechanical Engineering, Amirkabir University of Technology, 424 Hafez Ave, 15914 Tehran, Iran

来源：

Journal of Composite Materials | 2012年 / 46卷 / 15期

关键词：

Compendex;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Delamination

引用

收藏

页码：1795 / 1808

相关论文

共 24 条

[21] Experimental analysis of behavior and damage of sandwich composite materials in three-point bending. Part 1. Static tests and stiffness degradation at failure studies
Bezazi A.
Mahi A.
Berthelot J.-M.
Bezzazi B.
Strength of Materials, 2007, 39 (2) : 170 - 177
[22] Assessing the failure mechanisms and mechanical performance of Co-moulded hybrid AA5182-O/GFRP hat-channel beams under quasi-static three-point bending
Asaee, Zohreh
Montesano, John
Worswick, Michael
Composite Structures, 2021, 256
[23] Assessing the failure mechanisms and mechanical performance of Co-moulded hybrid AA5182-O/GFRP hat-channel beams under quasi-static three-point bending
Asaee, Zohreh
Montesano, John
Worswick, Michael
COMPOSITE STRUCTURES, 2021, 256
[24] An experimental investigation of transverse tension fatigue characterization of IM6/3501-6 composite materials using a three-point bend test
Peck, AW
COMPOSITE MATERIALS: FATIGUE AND FRACTURE, SEVENTH VOLUME, 1998, 1330 : 145 - 161