Preparation of flexible phenolic resin-based porous carbon fabrics by electrospinning

被引：0
|
作者：
机构：
[1] Wang, Lei
[2] Huang, Zheng-Hong
[3] Yue, Mengbin
[4] Li, Mingzhe
[5] Wang, Mingxi
[6] Kang, Feiyu
来源：
Huang, Z.-H. (zhhuang@mail.tsinghua.edu.cn) | 1600年 / Elsevier B.V., Netherlands卷 / 218期
关键词：
In the present study; we prepared flexible phenolic resin fabrics and corresponding porous carbon fabrics through electrospinning and successive curing and carbonization of resol/ethanol solutions. The addition of high-molecular-weight polyvinyl butyral (PVB) is essential for the stable fabrication of bead-free resol fabrics. Due to a high evaporation rate of ethanol and non-linear molecule structure of resol; the electrospun fabrics consist of entangled high aspect ratio ribbons instead of round fibers. The resol fabrics can be simply cured by heating at low temperature in air. Further carbonization at different temperatures resulted in flexible porous carbon fabrics with different specific surface area; which reached a maximum value of 855m2/g after heat treatment at 1000°C. These phenolic resin-based free-standing porous carbon fabrics would be promising in adsorption and electrochemical applications. © 2012 Elsevier B.V;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [41] Rich nitrogen-doped ordered mesoporous phenolic resin-based carbon for supercapacitors
    Chen, Hao
    Zhou, Min
    Wang, Zhao
    Zhao, Shiyong
    Guan, Shiyou
    ELECTROCHIMICA ACTA, 2014, 148 : 187 - 194
  • [42] Synthesis and Supercapacitor Performance of Boron-Doped Phenolic Resin-Based Mesoporous Carbon
    Bai, Zhi-Yan
    Yang, Fu
    Sun, Li-Juan
    Jia, Yan-Ming
    Xie, Yu-Long
    CHEMISTRYSELECT, 2025, 10 (05):
  • [43] Effect of calcium on the activation characteristics and pore structure of phenolic resin-based carbon spheres
    Yang, Junbing
    Kang, Feiyu
    Huang, Zhenghong
    Liang, Kaiming
    Qinghua Daxue Xuebao/Journal of Tsinghua University, 2002, 42 (10): : 1297 - 1299
  • [44] Research on Heat-resistant Phenolic Resin-based Activated Carbon for Supercapacitor Electrodes
    Sheng R.
    Tang T.
    Tian M.
    Yuan S.
    Zhang S.
    Fan Z.
    Cailiao Daobao/Materials Reports, 2023, 37 (04):
  • [45] STUDIES OF PHENOLIC RESIN-BASED MICROPOROUS SEPARATOR MATERIALS
    YANKOV, L
    PHILIPOVA, S
    ZLATANOV, I
    IVANOVA, L
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 1983, 13 (05) : 619 - 622
  • [46] Phenolic resin-based carbon aerogel composite reinforced by aluminum silicate ceramic fibers
    Cao, Sirui
    Dou, Yunhui
    Jiao, Yufeng
    Liu, Shujuan
    Liu, Dongmei
    Qi, Meili
    Hu, Ming
    JOURNAL OF ELECTROCERAMICS, 2024, 52 (01) : 3 - 9
  • [47] Preparation and performance of phenolic resin-based friction material modified with cardanol-graft-LNBR
    Feng J.
    Yu C.
    Qin W.
    Li C.
    Yu, Chuanbai (ycb2008@glut.edu.cn), 1600, Sichuan University (32): : 164 - 169
  • [48] Preparation and Performance of Porous Carbon Nanocomposite from Renewable Phenolic Resin and Halloysite Nanotube
    Yang, Xiaomeng
    Zeng, Xiaorui
    Han, Guihong
    Sui, Dong
    Song, Xiangyu
    Zhang, Yongsheng
    NANOMATERIALS, 2020, 10 (09) : 1 - 16
  • [49] UZnCl2-DES assisted synthesis of phenolic resin-based carbon aerogels for capacitors
    Deng, Junqian
    Chen, Ling
    Hong, Shu
    Lian, Hailan
    JOURNAL OF POROUS MATERIALS, 2020, 27 (03) : 789 - 800
  • [50] Insights into the pre-oxidation process of phenolic resin-based hard carbon for sodium storage†
    Wei, Zheng
    Zhao, Hai-Xia
    Niu, Yu-Bin
    Zhang, Si-Yuan
    Wu, Yuan-Bo
    Yan, Hui-Juan
    Xin, Sen
    Yin, Ya-Xia
    Guo, Yu-Guo
    MATERIALS CHEMISTRY FRONTIERS, 2021, 5 (10) : 3911 - 3917
12345