In situ observation of microstructure evolution in tungsten under 400 keV Kr+irradiation

被引：0
|
作者：
机构：
[1] Ran, Guang
[2] Huang, Shilin
[3] Huang, Zijing
[4] Yan, Qingzhi
[5] 1,Xu, Jiangkun
[6] Li, Ning
[7] 1,Wang, Lumin
来源：
Ran, Guang | 1600年 / Elsevier B.V., Netherlands卷 / 455期
基金：
中国国家自然科学基金;
关键词：
Argonne National Laboratory - Density of networks - Dislocation cells - Dislocation walls - Empirical formulas - Final microstructures - In-situ observations - In-situ transmission electron microscopies;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Tungsten was irradiated with 400 keV Kr+ions using the IVEM-Tandem Facility at Argonne National Laboratory. The evolution of microstructure and gas bubbles during the irradiation was observed by in situ transmission electron microscopy. Under irradiation, dislocation loops were created and grew into an increased density of network dislocations with increasing Kr+ion fluence. The irradiation induced final microstructure consists of dislocation cells ∼50 nm in diameter separated by dislocation walls. The irradiation also induced formation of Kr gas bubbles with an average diameter of 1.4 nm after 3.0 × 1016ions/cm2at 525 K. The gas bubbles were observed to grow to 2.6 nm diameter after additional Kr-irradiation of 5.0 × 1016ions/cm2at 815 K. The relationship between bubble size and irradiation time was obtained from experimental data obtained at 815 K and an empirical formula for calculating Kr bubble size was developed by fitting bubble growth equations with experiment data. The growth mechanisms of Kr gas bubbles in tungsten are discussed. © 2014 Published by Elsevier B.V.
引用
收藏
相关论文
共 50 条
  • [31] In situ MeV ion beam analysis of ceramic surfaces modified by 100-400 keV ion irradiation
    Yu, N
    Levine, TE
    Sickafus, KE
    Nastasi, M
    Mitchell, JN
    Maggiore, CJ
    Evans, CR
    Hollander, MG
    Tesmer, JR
    Weber, WJ
    Mayer, JW
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 1996, 118 (1-4): : 766 - 771
  • [32] In situ MeV ion beam analysis of ceramic surfaces modified by 100-400 keV ion irradiation
    Los Alamos Natl Lab, Los Alamos, United States
    Nucl Instrum Methods Phys Res Sect B, 1-4 (766-771):
  • [33] Effect of mechanical milling on the microstructure of tungsten under He+ irradiation condition
    Tan, Xiao-Yue
    Li, Ping
    Luo, Lai-Ma
    Chen, Hong-Yu
    Zan, Xiang
    Zhu, Xiao-Yong
    Luo, Guang-Nan
    Wu, Yu-Cheng
    FUSION ENGINEERING AND DESIGN, 2015, 100 : 571 - 575
  • [34] In situ Observation of Nanoprotrusion Growth on a Carbon Coated Tungsten Nanotip under Field
    Meng, Guodong
    Yimeng, L.
    Koitermaa, Roni Aleksi
    Zadin, Veronika
    Cheng, Yonghong
    Kyritsakis, Andreas
    2024 37TH INTERNATIONAL VACUUM NANOELECTRONICS CONFERENCE, IVNC 2024, 2024,
  • [35] The structural behavior of SrTiO3 under 400 keV Ne2+ ion irradiation
    Su, X.
    Liu, C. G.
    Yang, D. Y.
    Wen, J.
    Fu, E. G.
    Zhang, J.
    Chen, L. J.
    Xu, D. P.
    Wang, Y. Q.
    Li, Y. H.
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2015, 121 (03): : 1211 - 1217
  • [36] Microstructural evolution in tungsten and copper probes under hydrogen irradiation at ISTTOK
    Nunes, D.
    Mateus, R.
    Nogueira, I. D.
    Carvalho, P. A.
    Correia, J. B.
    Shohoji, N.
    Gomes, R. B.
    Fernandes, H.
    Silva, C.
    Franco, N.
    Alves, E.
    JOURNAL OF NUCLEAR MATERIALS, 2009, 390-91 : 1039 - 1042
  • [37] Electron microscopy study of the structural defect formation in ZnS under irradiation by electrons with energy of 400 keV
    Yu. Yu. Loginov
    A. V. Bril’kov
    A. V. Mozzherin
    Physics of the Solid State, 2016, 58 : 2468 - 2471
  • [38] In situ observation of the ultrafast lattice dynamics of graphite under ion irradiation
    Ishioka, K
    Hase, M
    Kitajima, M
    SOLID STATE COMMUNICATIONS, 2004, 130 (05) : 327 - 330
  • [39] The structural behavior of SrTiO3 under 400 keV Ne2+ ion irradiation
    X. Su
    C. G. Liu
    D. Y. Yang
    J. Wen
    E. G. Fu
    J. Zhang
    L. J. Chen
    D. P. Xu
    Y. Q. Wang
    Y. H. Li
    Applied Physics A, 2015, 121 : 1211 - 1217
  • [40] Electron microscopy study of the structural defect formation in ZnS under irradiation by electrons with energy of 400 keV
    Loginov, Yu. Yu.
    Bril'kov, A. V.
    Mozzherin, A. V.
    PHYSICS OF THE SOLID STATE, 2016, 58 (12) : 2468 - 2471
12345