In situ observation of microstructure evolution in tungsten under 400 keV Kr+irradiation

被引：0
|
作者：
机构：
[1] Ran, Guang
[2] Huang, Shilin
[3] Huang, Zijing
[4] Yan, Qingzhi
[5] 1,Xu, Jiangkun
[6] Li, Ning
[7] 1,Wang, Lumin
来源：
Ran, Guang | 1600年 / Elsevier B.V., Netherlands卷 / 455期
基金：
中国国家自然科学基金;
关键词：
Argonne National Laboratory - Density of networks - Dislocation cells - Dislocation walls - Empirical formulas - Final microstructures - In-situ observations - In-situ transmission electron microscopies;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Tungsten was irradiated with 400 keV Kr+ions using the IVEM-Tandem Facility at Argonne National Laboratory. The evolution of microstructure and gas bubbles during the irradiation was observed by in situ transmission electron microscopy. Under irradiation, dislocation loops were created and grew into an increased density of network dislocations with increasing Kr+ion fluence. The irradiation induced final microstructure consists of dislocation cells ∼50 nm in diameter separated by dislocation walls. The irradiation also induced formation of Kr gas bubbles with an average diameter of 1.4 nm after 3.0 × 1016ions/cm2at 525 K. The gas bubbles were observed to grow to 2.6 nm diameter after additional Kr-irradiation of 5.0 × 1016ions/cm2at 815 K. The relationship between bubble size and irradiation time was obtained from experimental data obtained at 815 K and an empirical formula for calculating Kr bubble size was developed by fitting bubble growth equations with experiment data. The growth mechanisms of Kr gas bubbles in tungsten are discussed. © 2014 Published by Elsevier B.V.
引用
收藏
相关论文
共 50 条
  • [1] In situ observation of microstructure evolution in tungsten under 400 keV Kr+ irradiation
    Ran, Guang
    Huang, Shilin
    Huang, Zijing
    Yan, Qingzhi
    Xu, Jiangkun
    Li, Ning
    Wang, Lumin
    JOURNAL OF NUCLEAR MATERIALS, 2014, 455 (1-3) : 320 - 324
  • [2] In situ Observation of Microstructure Evolution in 4H-SiC under 3.5 keV He+ Irradiation
    Shen, Qiang
    Ran, Guang
    Hinks, Jonathan
    Donnelly, Stephen E.
    Wang, Lumin
    Li, Ning
    JOURNAL OF NUCLEAR MATERIALS, 2016, 471 : 149 - 153
  • [3] In situ observation of surface morphology evolution in tungsten under focused Ga+ ion irradiation
    Ran, Guang
    Liu, Xiang
    Wu, Jihong
    Li, Ning
    Zu, Xiaotao
    Wang, Lumin
    JOURNAL OF NUCLEAR MATERIALS, 2012, 424 (1-3) : 146 - 152
  • [4] Effect of vanadium alloying on irradiation performance of tungsten under 60 keV helium irradiation
    Zhang, Ruijin
    Zhou, Hang
    Yu, Jiangang
    Han, Wenjia
    Liu, Mi
    Chen, Changan
    Zhu, Kaigui
    JOURNAL OF NUCLEAR MATERIALS, 2018, 512 : 65 - 71
  • [5] Evolution of a microstructure of materials under irradiation
    Slezov, VV
    Subbotin, AV
    Osmaev, OA
    PHYSICS OF THE SOLID STATE, 2005, 47 (03) : 477 - 483
  • [6] Evolution of a microstructure of materials under irradiation
    V. V. Slezov
    A. V. Subbotin
    O. A. Osmaev
    Physics of the Solid State, 2005, 47 : 477 - 483
  • [7] A Phase-Field Study of Microstructure Evolution in Tungsten Polycrystalline under He/D Irradiation
    Han, You-Sung
    MATERIALS, 2021, 14 (23)
  • [8] Tungsten evolution under helium irradiation: Shape of bubbles by TEM and in-situ GISAXS analysis
    Corso, L.
    Curiotto, S.
    Bernard, E.
    Cabie, M.
    Martin, C.
    Martinelli, L.
    Cheynis, F.
    Muller, P.
    Leroy, F.
    NUCLEAR MATERIALS AND ENERGY, 2023, 37
  • [9] In situ studies on the evolution of damage microstructures in tungsten under heavy ion irradiation and post annealing
    Liu, Xinyi
    Wu, Yukun
    Li, Yipeng
    Ding, Yifan
    Liu, Xiang
    Huang, Jinchi
    Zhang, Yaoli
    Ran, Guang
    PROGRESS IN NUCLEAR ENERGY, 2023, 160
  • [10] In Situ TEM Study of Microstructure Evolution of Zr-Nb-Fe Alloy Irradiated by 800 keV Kr2+ Ions
    Lei, Penghui
    Ran, Guang
    Liu, Chenwei
    Ye, Chao
    Lv, Dong
    Lin, Jianxin
    Wu, Yizhen
    Xu, Jiangkun
    MATERIALS, 2017, 10 (04)
12345