Effect of sand-blasting pretreatment on surface morphology, electrocatalytic activities and service life of Ti/IrO2·Ta2O5 anodes

被引：0
|
作者：
Jiang, Jun-Feng [1 ]
Meng, Hui-Min [1 ]
Sun, Dong-Bai [1 ]
机构：
[1] Corrosion and Protection Center, School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China
来源：
Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals | 2010年 / 20卷 / 06期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：1161 / 1169
相关论文
共 50 条
  • [21] Effect of Acid Etching on Lifetime of IrO2-Ta2O5/Ti Anodes
    Feng Qing
    Wang Kuaishe
    Yan Ailing
    Hao Xiaojun
    Jia Bo
    Chai Zuoqiang
    Song Kexing
    RARE METAL MATERIALS AND ENGINEERING, 2022, 51 (07) : 2387 - 2392
  • [22] Electrochemical and physical characterisation of lead-based anodes in comparison to Ti–(70%) IrO2/(30%) Ta2O5 dimensionally stable anodes for use in copper electrowinning
    Z. S. Msindo
    V. Sibanda
    J. H. Potgieter
    Journal of Applied Electrochemistry, 2010, 40 : 691 - 699
  • [23] Electrochemical oxidation of sulfide ion at a Ti/IrO2–Ta2O5 anode in the presence and absence of naphthenic acids
    Jamie Haner
    Dorin Bejan
    Nigel J. Bunce
    Journal of Applied Electrochemistry, 2009, 39 : 1733 - 1738
  • [24] Degradation mechanism of long service life Ti/IrO2-Ta2O5 oxide anodes in sulphuric acid
    Hu, JM
    Meng, HM
    Zhang, JQ
    Cao, CN
    CORROSION SCIENCE, 2002, 44 (08) : 1655 - 1668
  • [25] IrO2·Ta2O5涂层钛阳极的研究和应用
    张招贤
    唐仁衡
    张建华
    广东有色金属学报, 2002, (02) : 102 - 106
  • [26] Electrochemical and physical characterisation of lead-based anodes in comparison to Ti-(70%) IrO2/(30%) Ta2O5 dimensionally stable anodes for use in copper electrowinning
    Msindo, Z. S.
    Sibanda, V.
    Potgieter, J. H.
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 2010, 40 (03) : 691 - 699
  • [27] Titanium Anodes with Active Coatings Based on Iridium Oxides: The Chemical Composition of the Coatings and the Distribution of Their Components over Depth on Anodes Made of IrO2, IrO2 + TiO2, IrO2 + RuO2 + TiO2, and IrO2 + RuO2 + TiO2 + Ta2O5
    V. V. Gorodetskii
    V. A. Neburchilov
    Russian Journal of Electrochemistry, 2003, 39 : 1116 - 1123
  • [28] Effect of precursor baking on the electrochemical properties of IrO2-Ta2O5/Ti anodes
    Huang, Ching An
    Yang, Shu Wei
    Lai, Po Liang
    SURFACE & COATINGS TECHNOLOGY, 2018, 350 : 896 - 903
  • [29] Effect of preparation conditions on the properties of Ti based IrO2+Ta2O5 anodes
    Jinshu Xuebao/Acta Metallurgica Sinica, 2002, 38 (01):
  • [30] Effect of preparation conditions on the properties of Ti based IrO2+Ta2O5 anodes
    Hu, JM
    Meng, HM
    Zhang, JQ
    Cao, CN
    ACTA METALLURGICA SINICA, 2002, 38 (01) : 69 - 73
12345