Room temperature ferromagnetism of iron-doped rutile TiO2 nanorods synthesized by a low temperature method

被引：0
|
作者：
Melghit, Khaled [1 ]
Bouziane, Khalid [2 ]
机构：
[1] Chemistry Department, College of Science, Sultan Qaboos University, P.O. Box 36, Al-Khodh 123, Oman
[2] Physics Department, College of Science, Sultan Qaboos University, P.O. Box 36, Al-Khodh 123, Oman
来源：
Journal of Alloys and Compounds | 2008年 / 453卷 / 1-2期
关键词：
Nanorods of Fe-TiO2 were synthesized at 100 °C and room pressure by mixing titanium oxide wet gel TiO2&middotxH2O with a boiling solution of iron nitrate. The results of EDAX; performed on different selected area of the sample; revealed a homogeneous composition of about 3 at% Fe. Electron diffraction and XRD measurements show that the as-prepared Fe-TiO2 and annealed one at 550 °C have both a single rutile structure with no indication about the presence of a secondary phase. The transmission electron microscopy (TEM) micrographs show that both as-prepared Fe-TiO2 and annealed one at 550 °C have nanorod-shape with dimensions length by diameter of about 60 × 5 nm and 52 × 12 nm; respectively. Magnetization measurements show that both samples present a nonzero remanence and a coercivity of 108 and 120 Oe; respectively. At higher temperature; 850; °C; Fe-TiO2 decomposes to rutile TiO2 and new iron-titanate phase. © 2006 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：102 / 107
相关论文
共 50 条
  • [31] Defect types and room-temperature ferromagnetism in undoped rutile TiO2 single crystals
    Li Dong-Xiang
    Qin Xiu-Bo
    Zheng Li-Rong
    Li Yu-Xiao
    Cao Xing-Zhong
    Li Zhuo-Xin
    Yang Jing
    Wang Bao-Yi
    CHINESE PHYSICS B, 2013, 22 (03)
  • [32] Defect types and room-temperature ferromagnetism in undoped rutile TiO2 single crystals
    李东翔
    秦秀波
    郑黎荣
    李玉晓
    曹兴忠
    李卓昕
    杨静
    王宝义
    Chinese Physics B, 2013, 22 (03) : 495 - 498
  • [33] Room-Temperature Ferromagnetism in TiO2 Nanocrystals Synthesized by the Controlled Hydrolysis Procedure
    Gu, Deen
    Sun, Zhanhong
    Zhou, Lv
    Hu, Yongda
    Jiang, Yadong
    JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2016, 16 (03) : 2996 - 3002
  • [34] Room-Temperature Synthesis of Iron-Doped Anatase TiO2 for Lithium-Ion Batteries and Photocatalysis
    Andriamiadamanana, Christian
    Laberty-Robert, Christel
    Sougrati, Moulay T.
    Casale, Sandra
    Davoisne, Carine
    Patra, Snehangshu
    Sauvage, Frederic
    INORGANIC CHEMISTRY, 2014, 53 (19) : 10129 - 10139
  • [35] And room temperature ferromagnetism in Fe doped NiO nanorods
    Manna, S.
    Deb, A. K.
    Jagannath, J.
    De, S. K.
    JOURNAL OF PHYSICAL CHEMISTRY C, 2008, 112 (29): : 10659 - 10662
  • [36] Room temperature ferromagnetism in Fe doped CuO nanorods
    Manna, S.
    De, S. K.
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2010, 322 (18) : 2749 - 2753
  • [37] Effect of Ar ion irradiation on the room temperature ferromagnetism of undoped and Cu-doped rutile TiO2 single crystals
    Xu, Nan-Nan
    Li, Gong-Ping
    Lin, Qiao-Lu
    Liu, Huan
    Bao, Liang-Man
    CHINESE PHYSICS B, 2016, 25 (11)
  • [38] Room temperature ferromagnetism in combustion reaction prepared iron-doped zinc oxide nanoparticles
    Franco, A., Jr.
    Alves, T. E. P.
    MATERIALS SCIENCE IN SEMICONDUCTOR PROCESSING, 2013, 16 (06) : 1804 - 1807
  • [39] Effect of Ar ion irradiation on the room temperature ferromagnetism of undoped and Cu-doped rutile TiO2 single crystals
    许楠楠
    李公平
    林俏露
    刘欢
    包良满
    Chinese Physics B, 2016, (11) : 403 - 407
  • [40] Magnetic properties of the highly iron-doped rutile TiO2 nano crystals
    Yamaura, K.
    Wang, X. H.
    Li, J. -G.
    Ishigaki, T.
    Takayama-Muromachi, E.
    MATERIALS RESEARCH BULLETIN, 2006, 41 (11) : 2080 - 2087
12345