Effects of alternating magnetic field aged on microstructure and mechanical properties of AA2219 aluminum alloy

被引：0
|
作者：
Liu, Y.Z. [1 ,2 ]
Zhan, L.H. [1 ,2 ]
Ma, Q.Q. [3 ]
Ma, Z.Y. [1 ,2 ]
Huang, M.H. [1 ,2 ]
机构：
[1] State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha,410083, China
[2] School of Mechanical and Electrical Engineering, Central South University, Changsha,410083, China
[3] Light Alloy Research Institute, Central South University, Changsha,410083, China
来源：
Journal of Alloys and Compounds | 2015年 / 647卷
关键词：
Abstract In order to improve the mechanical properties; magnetic field heat treatment was developed; which is a process combined temperature field and magnetic field together. By alternating magnetic field aging test; the effect of the magnetic field aging on mechanical properties of AA2219 aluminum alloy was studied by TEM analysis; Vickers hardness measurement; and mechanical tensile test. It is shown that alternating magnetic field can accelerate the aging precipitation process; and significantly improve the hardness and strength; The TEM images show that there is more precipitated phase and is bigger dispersion degree in the samples than those with the conventional. The microstructure and mechanical properties of the aluminum alloy were improved significantly by alternating magnetic field aging treatment. © 2015 Elsevier B.V;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：644 / 647
相关论文
共 50 条
  • [41] Mechanical properties of cryo-rolled aluminium alloy AA2219 at 300, 77 and 20 K
    Nayan, Niraj
    Singh, Gaurav
    Baunthiyal, Davinder
    Murty, S. V. S. Narayana
    Prabhu, T. Antony
    Singh, Satish K.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2023, 881
  • [42] Analysis on exceptional cryogenic mechanical properties of AA2219 alloy FSW joints in multi-scale
    Hao, Yong-gang
    Liu, Wei
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2022, 850
  • [43] EXPERIMENTAL INVESTIGATION ON FRICTION STIR WELDING OF CRYOROLLED AA2219 ALUMINUM ALLOY JOINTS
    Babu, K. Kamal
    Panneerselvam, K.
    Sathiya, P.
    Haq, A. Noorul
    Sundarrajan, S.
    Mastanaiah, P.
    Murthy, C. V. Srinivasa
    SURFACE REVIEW AND LETTERS, 2017, 24 (01)
  • [44] Integral Hot Gas Pressure Forming of an AA2219 Aluminum Alloy Ellipsoidal Shell
    Yuan, S. J.
    Zhang, R.
    Zhang, W. W.
    JOM, 2017, 69 (04) : 742 - 747
  • [45] Development of Processing Maps and Constitutive Relationship for Thermomechanical Processing of Aluminum Alloy AA2219
    S. V. S. Narayana Murty
    Aditya Sarkar
    P. Ramesh Narayanan
    P. V. Venkitakrishnan
    J. Mukhopadhyay
    Journal of Materials Engineering and Performance, 2017, 26 : 2190 - 2203
  • [46] Integral Hot Gas Pressure Forming of an AA2219 Aluminum Alloy Ellipsoidal Shell
    S. J. Yuan
    R. Zhang
    W. W. Zhang
    JOM, 2017, 69 : 742 - 747
  • [47] Improvement of mechanical properties of aluminium-copper alloy (AA2219) GTA welds by Sc addition
    Seshagiri, P. C.
    Nair, B. S.
    Reddy, G. M.
    Rao, K. S.
    Bhattacharya, S. S.
    Rao, K. P.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2008, 13 (02) : 146 - 158
  • [48] Development of Processing Maps and Constitutive Relationship for Thermomechanical Processing of Aluminum Alloy AA2219
    Murty, S. V. S. Narayana
    Sarkar, Aditya
    Narayanan, P. Ramesh
    Venkitakrishnan, P. V.
    Mukhopadhyay, J.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2017, 26 (05) : 2190 - 2203
  • [49] Microstructural and Mechanical Characterization of as Weld and Aged Conditions of AA2219 Aluminium Alloy by Gas Tungsten Arc Welding Process
    S. Arunkumar
    P. Sathiya
    K. Devakumaran
    S. Ramesh Kumar
    Russian Journal of Non-Ferrous Metals, 2018, 59 : 93 - 101
  • [50] Effect of post weld aging treatment on tensile properties of electron beam welded AA2219 aluminum alloy
    S. Malarvizhi
    K. Raghukandan
    N. Viswanathan
    The International Journal of Advanced Manufacturing Technology, 2008, 37 : 294 - 301
12345