Effects of different corrosion environments on fatigue property and crack growth rate in 7475-T7351 aluminum alloy

被引：0
|
作者：
Gong, Yu-Hui [1 ]
Liu, Ming [1 ]
Zhang, Kun [1 ]
Huang, Min [1 ]
Yi, Lin-Na [1 ]
Dai, Sheng-Long [1 ]
机构：
[1] Beijing Institute of Aeronautical Materials, Beijing 100095, China
来源：
Cailiao Gongcheng/Journal of Materials Engineering | 2010年 / 09期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
13
引用
收藏
页码：71 / 73
相关论文
共 50 条
  • [31] Effects of anodic oxidation on fatigue property and fracture of 7475 aluminum alloy
    College of Mechanical Engineering, Changzhou University, Changzhou, China
    不详
    Cailiao Rechuli Xuebao, 11 (119-125):
  • [32] Shot peening and fatigue crack growth in 7075-T7351 aluminum
    Honda, T
    Ramulu, M
    Kobayshi, AS
    ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4, 2005, 297-300 : 72 - 77
  • [33] Thickness effects on the fatigue crack growth rate of 2024-T4 aluminum alloy
    Xu Feng
    Wang Xiaogui
    Yang Guang
    Gao Zengliang
    MECHANICAL, MATERIALS AND MANUFACTURING ENGINEERING, PTS 1-3, 2011, 66-68 : 1592 - 1597
  • [34] Laser and shot peening effects on fatigue crack growth in friction stir welded 7075-T7351 aluminum alloy joints
    Hatamleh, Omar
    Lyons, Jed
    Forman, Royce
    INTERNATIONAL JOURNAL OF FATIGUE, 2007, 29 (03) : 421 - 434
  • [35] Effects of precipitates on fatigue crack growth rate of AA 7055 aluminum alloy
    陈军洲
    甄良
    杨守杰
    戴圣龙
    Transactions of Nonferrous Metals Society of China, 2010, 20 (12) : 2209 - 2214
  • [36] Effects of precipitates on fatigue crack growth rate of AA 7055 aluminum alloy
    Chen Jun-zhou
    Zhen Liang
    Yang Shou-jie
    Dai Sheng-long
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2010, 20 (12) : 2209 - 2214
  • [37] Evaluation of Overloading and Crack Closure Effects on Fatigue Crack Growth in an Aircraft 7075-T7351 Al-Alloy
    Cerny, Ivo
    Mikulova, Dagmar
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS XII, 2014, 577-578 : 325 - 328
  • [38] Influence of corrosion environments on corrosion fatigue property of pre-corroded aluminum alloy
    Ma, Shao-Hua
    Hui, Li
    Zhou, Song
    Xu, Liang
    Zhu, Yong-Hui
    Cailiao Gongcheng/Journal of Materials Engineering, 2015, 43 (02): : 91 - 95
  • [39] Fatigue crack growth behaviour in aluminium alloy 7475 under different aging conditions
    Gürbüz, R
    Sarioglu, F
    MATERIALS SCIENCE AND TECHNOLOGY, 2001, 17 (12) : 1539 - 1543
  • [40] Effects of nonhalide anions on the stress corrosion cracking behaviour of alloy 7475 in the tempers T651 and T7351
    Braun, R
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2000, 51 (09): : 607 - 615
12345