Preparation and adhesion performance of UV-crosslinkable acrylic pressure sensitive adhesives

被引：0
|
作者：
Do, Hyun-Sung [1 ]
Park, Young-Jun [1 ]
Kim, Hyun-Joong [1 ]
机构：
[1] Lab. of Adhesion and Bio-Composites, Program in Environmental Materials Science, Seoul National University, Seoul 151-921, Korea, Republic of
来源：
Journal of Adhesion Science and Technology | 2006年 / 20卷 / 13期
关键词：
UV-crosslinkable acrylic pressure sensitive adhesives (PSAs) were synthesized by copolymerization of 2-ethylhexyl acrylate (2-EHA); vinyl acetate (VAc); acrylic acid (AA); 2-hydroxyethyl methacrylate (2-HEMA) and 4-acryloyloxydiethoxy-4′-chlorobenzophenone (unsaturated photoinitiator); with varying contents of 2-HEMA and photoinitiator; by solution polymerization. The UV-crosslinking behavior of the PSAs was studied by ATR-FT-IR spectroscopy; and PSA performance was characterized by probe tack; peel resistance and shear adhesion failure temperature (SAFT). As 2-HEMA acts as a good hydrogen donor to benzophenone; the efficiency of the photo-reaction was enhanced; thus with increasing contents of 2-HEMA and photoinitiator in the PSAs the incorporation of benzophenone groups in the PSAs; even at low UV doses; was quite fast. In addition; as the crosslinking reaction proceeds via photo-reaction mainly between 2-HEMA and photoinitiator; the probe tack and peel resistance of the PSAs having high concentrations of 2-HEMA and photoinitiator rapidly decreased in the early stage of UV irradiation due to increased crosslink density. These phenomena were also observed in the SAFT test; with the PSAs containing high levels of 2-HEMA and photoinitiator showing high SAFT values at low UV doses. © VSP 2006;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：1529 / 1545
相关论文
共 50 条
  • [41] UV crosslinkable microsphere pressure sensitive adhesives-influence on adhesive properties
    Kajtna, J.
    Krajnc, M.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2011, 31 (01) : 29 - 35
  • [42] Preparation and characterization of acrylic pressure-sensitive adhesives based on UV and heat curing systems
    Lee, Seo Ho
    You, Ryong
    Yoon, Young Il
    Park, Won Ho
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2017, 75 : 190 - 195
  • [43] Preparation of environmentally friendly acrylic pressure-sensitive adhesives by bulk photopolymerization and their performance
    Zhu, Menglu
    Cao, Zhanshuo
    Zhou, Haijun
    Xie, Yijun
    Li, Guohua
    Wang, Nongyue
    Liu, Yingchun
    He, Lianqi
    Qu, Xiongwei
    RSC ADVANCES, 2020, 10 (17) : 10277 - 10284
  • [44] Adhesive Performance of Acrylic Pressure-Sensitive Adhesives from Different Preparation Processes
    Marquez, Irene
    Paredes, Nuria
    Alarcia, Felipe
    Velasco, Jose Ignacio
    POLYMERS, 2021, 13 (16)
  • [45] UV INITIATED POLYMERIZATION FOR THE PREPARATION OF PRESSURE SENSITIVE ADHESIVES
    SHANKS, RA
    CLARKE, SR
    POLYMER PHOTOCHEMISTRY, 1983, 3 (02): : 157 - 163
  • [46] Application of novel unsaturated organosilane ethers in cationic UV-crosslinkable acrylic PSA systems
    Czech, Z
    Urbala, M
    POLIMERY, 2004, 49 (11-12) : 837 - 840
  • [47] The Preparation and Adhesion Performances of Transparent Acrylic Pressure Sensitive Adhesives Containing Acrylamide Monomer for Optical Applications
    Baek, Seung-Suk
    Jang, Se-Jung
    Hwang, Seok-Ho
    ELASTOMERS AND COMPOSITES, 2016, 51 (03): : 181 - 187
  • [48] Preparation and characterization of expanded graphite intercalation compound/UV-crosslinked acrylic resin pressure sensitive adhesives
    Park, Gyu-Dae
    Jung, Hyun-Ok
    Kim, Kyung-Min
    Lim, Jung-Hyurk
    Lee, Ju-Won
    Lee, Sung-Goo
    Lee, Jae Heung
    Kim, Sung-Ryong
    MACROMOLECULAR RESEARCH, 2015, 23 (04) : 396 - 401
  • [49] Preparation and characterization of expanded graphite intercalation compound/UV-crosslinked acrylic resin pressure sensitive adhesives
    Gyu-Dae Park
    Hyun-Ok Jung
    Kyung-Min Kim
    Jung-Hyurk Lim
    Ju-Won Lee
    Sung-Goo Lee
    Jae Heung Lee
    Sung-Ryong Kim
    Macromolecular Research, 2015, 23 : 396 - 401
  • [50] Adhesion and Contact Aging of Acrylic Pressure-Sensitive Adhesives to Swollen Elastomers
    Jha, Anushka
    Gryska, Stefan
    Barrios, Carlos
    Frechette, Joelle
    LANGMUIR, 2024, 40 (08) : 4267 - 4276
12345