Screening Strategy Identifies an Overlooked Deep-Ultraviolet Transparent Nonlinear Optical Crystal

In the deep-ultraviolet (DUV) region, nonlinear optical (NLO) crystals must meet stringent requirements, including a large optical band gap and sufficient second harmonic generation (SHG) response. Typically, these criteria are fulfilled by borates, carbonates and nitrates containing pi-conjugated groups. In contrast, sulfates and phosphates, with polarizabilities significantly smaller than those of pi-conjugated groups, struggle to achieve similar performance. Here, we present the discovery of Mg2PO4Cl, a magnesium-based phosphate, identified from over 10,000 phosphates based on a polar-axial-symmetry screening strategy, which exhibits the highest SHG response (5.2xKH2PO4 (KDP)) with phase-matching ability among non-pi-conjugated DUV transparent NLO crystals. This compound belongs to the Pna21 space group, with [PO4] units consistently aligned along the 21 screw axis and glide planes throughout its crystal structure. Theoretical calculations attribute its remarkable SHG effect to the orderly arrangement of heteroanionic [MgO5Cl] and [MgO4Cl2] polyhedra alongside isolated [PO4] tetrahedra, supported by Berry phase analysis. Furthermore, a crystallographic structure analysis of phosphates and sulfates with significant SHG effects validates the effectiveness of our screening strategy. These findings offer valuable insights into the origins of NLO effects in non-pi-conjugated compounds from both a material design and structural chemistry perspective, inspiring future efforts to revitalize DUV phosphates. Based on a strategy focusing on polar axial symmetry, a DUV transparent NLO crystal Mg2PO4Cl was discovered after screening over 10,000 phosphates. This crystal exhibits the highest SHG response (5.2xKDP) with phase-matching ability among non-pi-conjugated DUV compounds. Such a remarkable SHG effect can be attributed to the orderly arrangement of heteroanionic [MgO5Cl] and [MgO4Cl2] polyhedra alongside isolated [PO4] tetrahedra, supported by Berry phase analysis. image