The Presence of Excess Oxygen in Burning Metallic Materials

被引：0
|
作者：
Wilson, D. Bruce
Steinberg, Theodore A.
Dewit, John R.
机构：
[1] P.O. Box 88, Mesilla Park, NM 88048, United States
[2] Department of Mechanical Engineering, University of Queensland, Brisbane, QLD 4072, Australia
来源：
ASTM Special Technical Publication | 2001年 / 1395期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Early work on burning of iron rods under conditions of the ASTM/NASA flammability test showed that there was excess oxygen, that is, above stoichiometric requirements for Fe2O3, present in the molten product formed during burning. Since that initial work, this phenomenon has been confirmed for burning under microgravity conditions and has been observed for a wide range of metals under various burning conditions at ambient pressures and under pressurized oxygen-enriched conditions. This paper reviews these experimental observations and discusses the possible thermodynamic analysis for the metals iron, cobalt, and nickel. The excess oxygen in the burning molten iron oxide is represented as combined to form a series of ferrite ions. For cobalt the excess oxygen is represented as a bridging species; that is, the cobalt oxide liquid is oxygenated. There is no definitive evidence for excess oxygen in nickel oxide.
引用
收藏
页码：145 / 162
相关论文
共 50 条
  • [21] EFFECT OF METALLIC LITHIUM ON STRUCTURE OF TUNGSTEN WIRES DOPED IN PRESENCE OF OXYGEN
    GROH, R
    MILLNER, T
    BARTHA, L
    PLANSEEBERICHTE FUR PULVERMETALLURGIE, 1977, 25 (04): : 269 - 271
  • [22] CHEMICAL-VAPOR DEPOSITION OF METALLIC COPPER FILM IN THE PRESENCE OF OXYGEN
    HAMMADI, Z
    LECOHIER, B
    DALLAPORTA, H
    JOURNAL OF APPLIED PHYSICS, 1993, 73 (10) : 5213 - 5215
  • [23] Cleaning efficiency of carbon films by oxygen plasmas in the presence of metallic getters
    Tabares, F. L.
    Ferreira, J. A.
    Tafalla, D.
    Tanarro, I.
    Herrero, V. J.
    Mendez, I.
    Gomez-Aleixandre, C.
    Albella, J. M.
    PROCEEDINGS OF THE 17TH INTERNATIONAL VACUUM CONGRESS/13TH INTERNATIONAL CONFERENCE ON SURFACE SCIENCE/INTERNATIONAL CONFERENCE ON NANOSCIENCE AND TECHNOLOGY, 2008, 100
  • [24] Chemical-vapor deposition of metallic copper film in the presence of oxygen
    1600, (73):
  • [25] Catalysis of oxygen reaction on positive electrode of a lithium-oxygen cell in the presence of metallic nanosystems
    Korchagin, O. V.
    Tarasevich, M. R.
    Tripachev, O. V.
    Bogdanovskaya, V. A.
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2016, 52 (04) : 581 - 589
  • [26] Chemisorption of microimpurities of nitrogen(II) and (IV) oxides in the presence of an excess amount of oxygen
    1600, Izdatel'stvo Nauka (87):
  • [27] Chemisorption of microimpurities of nitrogen(II) and (IV) oxides in the presence of an excess amount of oxygen
    Spetsow, E. A.
    Nefedova, L. A.
    Lavrishcheva, S. A.
    RUSSIAN JOURNAL OF APPLIED CHEMISTRY, 2014, 87 (04) : 434 - 438
  • [28] Chemisorption of microimpurities of nitrogen(II) and (IV) oxides in the presence of an excess amount of oxygen
    E. A. Spetsow
    L. A. Nefedova
    S. A. Lavrishcheva
    Russian Journal of Applied Chemistry, 2014, 87 : 434 - 438
  • [29] Plasma-enhanced HC-SCR of NOx in the presence of excess oxygen
    Miessner, H
    Francke, KP
    Rudolph, R
    APPLIED CATALYSIS B-ENVIRONMENTAL, 2002, 36 (01) : 53 - 62
  • [30] Critical study of the determination of ethane by combustion over platinum in the presence excess oxygen
    Shepherd, M
    Branham, JR
    BUREAU OF STANDARDS JOURNAL OF RESEARCH, 1933, 11 (4/6): : 783 - 797
12345