Effect of carrier gas of Bi4Ti3O12 thin film prepared by metalorganic vapor deposition method

被引：0

作者：

Nakamura, Makoto ^{[1
]}

Higuchi, Tohru ^{[1
]}

Tsukamoto, Takeyo ^{[1
]}

机构：

[1] Department of Applied Physics, Tokyo University of Science, 1-3 Kagurazaka, Shinjuku, Tokyo 162-8601, Japan

来源：

Japanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers | 2003年 / 42卷 / 9 B期

关键词：

Annealing - Argon - Ferroelectricity - Metallorganic chemical vapor deposition - Oxygen - Platinum - Polarization - Semiconducting bismuth compounds - Semiconducting silicon - Silica - Substrates - Titanium;

D O I：

10.1143/jjap.42.5969

中图分类号：

学科分类号：

摘要：

Undoped Bi4Ti3O12 (BIT) thin films on (111) Pt/Ti/SiO2/Si substrates were prepared by a metalorganic vapor deposition method using Bi(CH3)3 and Ti(i-OC3H7)4 sources. The ferroelectricity of BIT thin films was observed at a low deposition temperature of 500°C. The electrical and structural properties were found to depend on the total gas flow rate of Ar and O2 gases during deposition. The remanent polarization (Pr) and the coercive field (Ec) of highly (117)-oriented BIT thin films prepared at a total gas flow rate of 90 sccm were 2Pr = 28.8 μC/cm2 and 2Ec = 130.7 kV/cm, respectively. The Pr and Ec of highly c-axis-oriented BIT thin films prepared at a total gas flow rate of 180 sccm were 2Pr = 6.2 μC/cm2 and 2Ec = 107.6 kV/cm, respectively.

引用

页码：5969 / 5972

共 50 条

[41] Study on hydrothermally prepared Bi4Ti3O12 nanoparticles
Yang, QB
Li, YX
Yin, QR
Wang, PL
Cheng, YB
JOURNAL OF INORGANIC MATERIALS, 2002, 17 (06) : 1135 - 1140
[42] Study on hydrothermally prepared Bi4Ti3O12 nanoparticles
Yang, Qun-Bao
Li, Yong-Xiang
Yin, Qing-Rui
Wang, Pei-Ling
Cheng, Yi-Bing
Wuji Cailiao Xuebao/Journal of Inorganic Materials, 2002, 17 (06): : 1135 - 1140
[43] Switching properties of Bi3.15Nd0.85Ti3O12 thin films prepared by metalorganic deposition method
Li, W
Song, CH
Ma, J
Kan, YM
Lu, X
Zhu, JS
INTEGRATED FERROELECTRICS, 2004, 68 : 269 - 278
[44] PREPARATION AND PROPERTIES OF BI4TI3O12 SINGLE-CRYSTAL THIN-FILMS BY ATMOSPHERIC-PRESSURE METALORGANIC CHEMICAL-VAPOR-DEPOSITION
WANG, H
FU, LW
SHANG, SX
JOURNAL OF APPLIED PHYSICS, 1993, 73 (11) : 7963 - 7965
[45] Ferroelectric and Physical Characteristic of the La and V doped on Bi4Ti3O12 Thin Film Prepared by RF Magnetron Sputtering Method
Chen, Shih-Fang
Chen, Kai-Huang
Cheng, Chien-Min
HIGH-PERFORMANCE CERAMICS VII, PTS 1 AND 2, 2012, 512-515 : 1321 - +
[46] Bi4Ti3O12 and Bi3.25La0.75Ti3O12 Thin Films Prepared by RF Magnetron Sputtering
Yang, Jian-Ping
Li, Xing-Ao
Zuo, An-You
Yuan, Zuo-Bin
Weng Zhu-Lin
HIGH-PERFORMANCE CERAMICS VI, 2010, 434-435 : 296 - +
[47] Ferroelectric Bi4Ti3O12 thin films on Pt-coated silicon by halide chemical vapor deposition
Schuisky, M
Hårsta, A
Khartsev, S
Grishin, A
JOURNAL OF APPLIED PHYSICS, 2000, 88 (05) : 2819 - 2824
[48] Ferroelectric Bi4Ti3O12 thin films on Pt-coated silicon by halide chemical vapor deposition
1600, American Institute of Physics Inc. (88):
[49] Effect of pyrolysis temperature on Bi4Ti3O12/MgO(100) structures prepared by chemical solution deposition
Jeong, Ju-Hyun
Lee, Young-Hwan
Hwang, K. S.
JOURNAL OF CERAMIC PROCESSING RESEARCH, 2007, 8 (02): : 110 - 113
[50] Improved characteristics of Bi4Ti3O12 thin film on ITO glass by using excess Bi2O3-added Bi4Ti3O12 ceramic as source target
Chia, W. K.
Chen, Y. C.
Yang, C. F.
Tzou, W. C.
JOURNAL OF PHYSICS AND CHEMISTRY OF SOLIDS, 2008, 69 (2-3) : 465 - 469

← 1 2 3 4 5 →