Effect of rotation speed on microstructure and properties of 2024-T4 aluminum alloy submerged friction stir weld

被引：0

作者：

Wang, Kuai-She ^{[1
]}

Wu, Nan ^{[1
]}

Wang, Wen ^{[1
]}

Ding, Kai ^{[1
]}

Guo, Qiang ^{[1
]}

机构：

[1] College of Metallurgical Engineering, Xi'an University of Architecture and Technology, Xi'an 710055, China

来源：

Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals | 2013年 / 23卷 / 02期

关键词：

Aluminum alloys - Friction - Speed - Friction stir welding - Research laboratories - Welds - Cooling water - Rotation - Tensile strength - Tribology - Precipitates;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

2024-T4 aluminum alloy plate was jointed by submerged friction stir welding (SFSW). The effects of rotation speed on the welding temperature fields of SFS weld, precipitate morphology of the nugget zone and mechanical properties of SFS weld were investigated. The results show that the cooling water circulation medium has significant instantaneous cooling effect; the peak value of welding temperature fields increases from 271.0°C to 310.8°C with the rotation speed increases from 600 r/min to 1180 r/min. The precipitate phases of the nugget zone precipitate and grow under welding thermal cycle. The quantity and size of the precipitates gradually increase with the increase of the rotation speed. The average value of microhardness in the nugget zone of SFS weld decreases from 117.5HV to 99.2HV with the increase of the rotation speed, meanwhile, tensile strength and elongation of SFS weld decrease from 403.3 MPa and 3.24% to 334.5 MPa and 1.44%, respectively.

引用

页码：343 / 348

共 50 条

[21] Mechanical properties of friction stir lap welded 2024-T4 aluminum alloy joints for pin not plunging into lower sheet
Ye J.
Liu X.
Wang S.
Liu, Xuesong (liuxuesong@hit.edu.cn), 2018, Harbin Research Institute of Welding (39): : 71 - 74
[22] Study on dislocation and microstructural properties of friction stir welded joint for 2024-T4 aluminum alloys
Zhang Geming
Liu Peng
Shi Qingyu
Xu Shubo
Li Jianing
Feng Keyun
Jing Cainian
KOVOVE MATERIALY-METALLIC MATERIALS, 2017, 55 (04): : 245 - 253
[23] Effect of post-weld heat treatment on joint properties of dissimilar friction stir welded 2024-T4 and 7075-T6 aluminum alloys
Safarbali, B.
Shamanian, M.
Eslami, A.
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2018, 28 (07) : 1287 - 1297
[24] Effect of rotation speed on microstructure and mechanical properties of refill friction stir spot welded 6061-T6 aluminum alloy
L. Zhou
L. Y. Luo
T. P. Zhang
W. X. He
Y. X. Huang
J. C. Feng
The International Journal of Advanced Manufacturing Technology, 2017, 92 : 3425 - 3433
[25] Effect of rotation speed on microstructure and mechanical properties of refill friction stir spot welded 6061-T6 aluminum alloy
Zhou, L.
Luo, L. Y.
Zhang, T. P.
He, W. X.
Huang, Y. X.
Feng, J. C.
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2017, 92 (9-12): : 3425 - 3433
[26] Microstructure and mechanical properties as a function of rotation speed in underwater friction stir welded aluminum alloy joints
Zhang, H. J.
Liu, H. J.
Yu, L.
MATERIALS & DESIGN, 2011, 32 (8-9): : 4402 - 4407
[27] The Microstructure of Aluminum-Magnesium Alloy Friction Stir Weld
Sizova, Olga
Kolubaev, Alexander
Kolubaev, Evgeny
Zaikina, Anastasiya
Rubtsov, Valery
Psakhie, Sergey
Chernyavsky, Alexander
Lopota, Vitaly
INTERNATIONAL CONFERENCE ON PHYSICAL MESOMECHANICS OF MULTILEVEL SYSTEMS 2014, 2014, 1623 : 587 - 590
[28] Effect of the Stir Rotation Speed on the Microstructure and Properties of Super304H/T92 Friction Weld Joints
J. L. Zhang
H. Xue
Y. Lu
Strength of Materials, 2020, 52 : 51 - 58
[29] Effect of the Stir Rotation Speed on the Microstructure and Properties of Super304H/T92 Friction Weld Joints
Zhang, J. L.
Xue, H.
Lu, Y.
STRENGTH OF MATERIALS, 2020, 52 (01) : 51 - 58
[30] Mechanical properties of 2024-T4 aluminium alloy joints in ultrasonic vibration enhanced friction stir welding
刘小超
武传松
Michael Rethmeier
Andreas Pittner
China Welding, 2013, 22 (04) : 8 - 13

← 1 2 3 4 5 →