Effect of pulsed laser irradiation on the coincidence site lattice grain boundary of 316L stainless steel

被引：0
|
作者：
Qu, Xiao-Jian [1 ]
Yang, Zhan-Bing [1 ]
Yang, Su-Bing [2 ]
机构：
[1] School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing,100083, China
[2] Hokkaido University, Sapporo,060-8628, Japan
来源：
Surface Technology | 2019年 / 48卷 / 05期
基金：
中国国家自然科学基金;
关键词：
Coincidence site lattice grain boundaries - Electron back scatter diffraction - Grain boundary character distributions - Grain boundary migrations - Pulse laser irradiations - Random grain boundaries - Stacking fault tetrahedron - Twin;
D O I：
10.16490/j.cnki.issn.1001-3660.2019.05.030
中图分类号：
学科分类号：
摘要：
The work aims to improve the intergranular corrosion resistance by increasing the proportion of coincidence site lattice (CSL) grain boundaries and reducing the proportion of random grain boundaries in 316L stainless steel. The surface of SUΣ316L austenitic stainless steel was irradiated by femtosecond and nanosecond laser with Nd:YAG laser at suitable temperature. The grain boundary character distributions of irradiated samples were analyzed by electron backscatter diffraction (EBSD) to study the effect of different laser irradiation conditions on the grain boundary. In addition, the crystal defects and Σ3 grain boundaries in the pulsed laser irradiation sample were observed under a transmission electron microscope (TEM). Compared with non-irradiated specimens, the proportion of the Σ3 grain boundary of specimens under femtosecond laser irradiation at 723 K increased by 2.88% and random grain boundary decreased by 4.24%; Compared with non-irradiated specimens, the proportion of the Σ3 grain boundary of specimens under nanosecond laser irradiation at 723 K increased by 10.78% and random grain boundary decreased by 9.97%; The proportion of the Σ3 grain boundary of specimens under nanosecond laser irradiation at 773 K increased by 12.52% and random grain boundary decreased by 10.68%. TEM images showed that there were a large number of stacking fault tetrahedrons in the pulsed laser irradiated sample at 773 K, but few such defects were found in the step of twin nucleation. The change of CSL grain boundary ratio is mainly related to grain boundary migration and twin formation, in which the energy generated by the pulse laser irradiation provides favorable conditions for the grain boundary migration in the skin layer of specimens, and the crystal defects caused by pulsed laser irradiation might promote the nucleation and growth of twins during grain boundary migration. © 2019, Chongqing Wujiu Periodicals Press. All rights reserved.
引用
收藏
页码：201 / 208
相关论文
共 50 条
  • [21] The effect of grain boundary character distribution on the mechanical properties at different strain rates of a 316L stainless steel
    Zhuo, Zhen
    Xia, Shuang
    Bai, Qin
    Zhou, Bangxin
    JOURNAL OF MATERIALS SCIENCE, 2018, 53 (04) : 2844 - 2858
  • [22] Recrystallization-based grain boundary engineering of 316L stainless steel produced via selective laser melting
    Gao, Shubo
    Hu, Zhiheng
    Duchamp, Martial
    Krishnan, P. S. Sankara Rama
    Tekumalla, Sravya
    Song, Xu
    Seita, Matteo
    ACTA MATERIALIA, 2020, 200 : 366 - 377
  • [23] Effect of Laser Surface Treatment on the Corrosion Resistance of 316L Stainless Steel
    Yuan S.-S.
    Wang D.-Z.
    Wang J.-T.
    Wang C.-G.
    He Q.-B.
    Cai X.-N.
    Hu W.
    Surface Technology, 2021, 50 (07): : 83 - 89
  • [24] Effect of High Laser Energy Density on Selective Laser Melted 316L Stainless Steel: Analysis on Metallurgical and Mechanical Properties and Comparison with Wrought 316L Stainless Steel
    Shanmuganathan, Pradeep Kumar
    Purushothaman, Dinesh Babu
    Ponnusamy, Marimuthu
    3D PRINTING AND ADDITIVE MANUFACTURING, 2023, 10 (03) : 383 - 392
  • [25] Effect of laser texturing bulges on tribological properties of 316L stainless steel
    Li, Wen-Xuan
    Liu, Yan
    Duan, Hai-Tao
    Wang, Yi-Han
    Zhan, Sheng-Peng
    Zhang, Wu-Lin
    Yang, Tian
    Li, Guo-Zheng
    Dan, Jia
    SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES, 2023, 11 (01)
  • [26] Effect of Laser Peening without Coating on 316L austenitic stainless steel
    Sathyajith, S.
    Kalainathan, S.
    INTERNATIONAL CONFERENCE ON MATERIALS SCIENCE AND TECHNOLOGY (ICMST 2012), 2015, 73
  • [27] Effect of High Laser Energy Density on Selective Laser Melted 316L Stainless Steel: Analysis on Metallurgical and Mechanical Properties and Comparison with Wrought 316L Stainless Steel
    Shanmuganathan, Pradeep Kumar
    Purushothaman, Dinesh Babu
    Ponnusamy, Marimuthu
    3D PRINTING AND ADDITIVE MANUFACTURING, 2021,
  • [28] Effect of temperature and grain size on the corrosion behavior of 316L stainless steel in seawater
    Xin, SenSen
    Xu, Jian
    Lang, FengJun
    Li, MouCheng
    MATERIALS AND MANUFACTURING, PTS 1 AND 2, 2011, 299-300 : 175 - 178
  • [29] THE EFFECT OF PASSIVATION ON THE HAEMOCOMPATIBILITY OF 316L STAINLESS STEEL
    Shi Yongjuan
    Ren Yibin
    Zhang Bingchun
    Yang Ke
    ACTA METALLURGICA SINICA, 2011, 47 (12) : 1575 - 1580
  • [30] The effect of cerium solutions on 316L stainless steel
    Askarian, M.
    Peikari, M.
    Javadpour, S.
    Masoum, S.
    Abolhasanzade, A.
    MATERIALS CHARACTERISATION IV: COMPUTATIONAL METHODS AND EXPERIMENTS, 2009, 64 : 249 - 257
12345