Effect of thermal spraying parameters on cracking and thermal cycling life of thermal barrier coatings

被引：0

作者：

Yu, Zexin ^{[1
]}

Yu, Jingye ^{[1
]}

Wu, Liangmin ^{[1
]}

Wang, Weize ^{[1
]}

机构：

[1] Key Laboratory of Pressure Systems and Safety, Ministry of Education, East China University of Science and Technology, Shanghai,200237, China

来源：

Hanjie Xuebao/Transactions of the China Welding Institution | 2016年 / 37卷 / 10期

关键词：

Plasma spraying - Thermal cycling - Ceramic coatings - Sprayed coatings - Cracks - Ceramic materials - Preheating;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Segmentation cracks can be formed in the top ceramic coatings of thermal barrier coating system by the thermal spraying process without any cooling. The crack system can strengthen the strain tolerance of ceramic coatings. Up to now, there are almost no systemic studies on the cracking, especially on the branch cracks. The quantitative effects of feeding rate and substrate preheating temperature were studied on the cracking in this paper. And the thermal cycling lifetimes of coatings with different cracking systems were compared. It was found that with the increase of feeding rate, the density of vertical cracks and length of branch cracks increase firstly and then decrease. The density of vertical cracks shows an increment tendency with the increase of substrate preheating temperature. However, the length of branch cracks increases firstly, and then shows a decreasing trend. It shows that the lifetime of the top ceramic coatings can be improved effectively through restraining the total length and number of branch cracks in coating and maintaining the density of segmentation cracks at a certain level. © 2016, Editorial Board of Transactions of the China Welding Institution, Magazine Agency Welding. All right reserved.

引用

页码：55 / 58

共 50 条

[41] Thermal Fatigue Life Prediction Model for Thermal Barrier Coatings
Yao Y.-D.
Ai Y.-T.
Guan P.
Tian J.
Bao T.-N.
Surface Technology, 2022, 51 (06): : 267 - 274
[42] Thermal Cycling Behavior of Thermal Barrier Coatings with HVOF NiCrAlY Bond Coat
L. Y. Ni
C. Liu
H. Huang
C. G. Zhou
Journal of Thermal Spray Technology, 2011, 20
[43] FAILURE DURING THERMAL CYCLING OF PLASMA-SPRAYED THERMAL BARRIER COATINGS
BERNDT, CC
HERMAN, H
THIN SOLID FILMS, 1983, 108 (04) : 427 - 437
[44] The role of transient oxides during deposition and thermal cycling of thermal barrier coatings
Nijdam, T.J.
Sloof, W.G.
Mater High Temp, 3-4 (551-559):
[45] Degradation of thermal barrier coatings due to thermal cycling up to 1150°C
M. S. Ali
Shenhua Song
Ping Xiao
Journal of Materials Science, 2002, 37 : 2097 - 2102
[46] Porosity and thermal cycling behavior of plasma sprayed and EBPVD thermal barrier coatings
Agu, Ogad
Diwan, Ravinder
Mensah, Patrick F.
Silva, Monica B.
Guo, S. M.
PROCEEDINGS OF THE ASME TURBO EXPO 2010, VOL 1, 2010, : 435 - 444
[47] The role of transient oxides during deposition and thermal cycling of thermal barrier coatings
Nijdam, T. J.
Sloof, W. G.
MATERIALS AT HIGH TEMPERATURES, 2005, 22 (3-4) : 551 - 559
[48] Delamination mechanism of thermal barrier coatings induced by thermal cycling and growth stresses
Xiao, Y. Q.
Yang, L.
Zhu, W.
Zhou, Y. C.
Pi, Z. P.
Wei, Y. G.
ENGINEERING FAILURE ANALYSIS, 2021, 121
[49] Thermal Cycling Behavior of Thermal Barrier Coatings with HVOF NiCrAlY Bond Coat
Ni, L. Y.
Liu, C.
Huang, H.
Zhou, C. G.
JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2011, 20 (05) : 1133 - 1138
[50] Degradation of thermal barrier coatings due to thermal cycling up to 1150°C
Ali, MS
Song, SH
Xiao, P
JOURNAL OF MATERIALS SCIENCE, 2002, 37 (10) : 2097 - 2102

← 1 2 3 4 5 →