Effect of lead on the corrosion behavior of Alloy 690

被引：0
|
作者：
Li, Chengtao [1 ]
Fei, Kexun [1 ]
Song, Lijun [1 ]
机构：
[1] Plant Life Management Research Center, Suzhou Nuclear Power Research Institute, Suzhou,215004, China
来源：
Harbin Gongcheng Daxue Xuebao/Journal of Harbin Engineering University | 2015年 / 36卷 / 07期
关键词：
Intergranular corrosion - Scanning electron microscopy - Electrochemical corrosion - Lead - Localized corrosion - Sodium hydroxide - Residual stresses - Corrosive effects - Cracks - Stress corrosion cracking;
D O I：
10.3969/j.issn.1006-7043.201403020
中图分类号：
学科分类号：
摘要：
The corrosion test of Alloy 690 was conducted in solutions with Pb and without Pb to study the effect of lead on the corrosion behavior of Alloy 690, respectively. The stress corrosion cracking (SCC) behavior and the electrochemical behavior of Alloy 690 in NaOH solutions with Pb and without Pb were investigated by scanning electron microscopy (SEM) and localized electrochemical impedance spectroscopy (LEIS). The SEM surface images show that the corrosion morphology of Alloy 690 is different and Pb can be found in the surface corrosion product. The SCC results show that Alloy 690 contains transgranular stress corrosion cracking in NaOH solution with Pb. LEIS results demonstrated that the Alloy 690 in NaOH solution with 1 000 mg/L Pb has large dispersion characteristics of electrochemistry. Alloy 690 has high sensitivity of stress corrosion in NaOH solution with Pb. ©, 2015, Editorial Board of Journal of HEU. All right reserved.
引用
收藏
页码：1001 / 1005
相关论文
共 50 条
  • [1] Lead-induced stress corrosion behavior of Alloy 690
    Li, C.-T. (lctslj0630@hotmail.com), 1600, University of Science and Technology Beijing (35):
  • [2] Effect of grain orientation on the corrosion behavior of polycrystalline Alloy 690
    Wang, Siyan
    Wang, Jianqiu
    CORROSION SCIENCE, 2014, 85 : 183 - 192
  • [3] Lead assisted stress corrosion cracking of Alloy 690
    Psaila-Dombrowski, MJ
    Hua, FH
    Doherty, PE
    PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 1999, : 703 - 710
  • [4] Effect of Ultrasonic Surface Rolling Treatment on Corrosion Behavior of Alloy 690
    Liu, Jiang
    Liu, Junbiao
    Zhang, Xuehui
    Ahmad, Tahir
    Liang, Tongxiang
    Zeng, Longfei
    Wang, Chunming
    Yang, Bin
    METALS, 2020, 10 (07) : 1 - 12
  • [5] Effect of temperature on corrosion behavior of alloy 690 in high temperature hydrogenated water
    Jiazhen Wang
    Jianqiu Wang
    Hongliang Ming
    Zhiming Zhang
    En-Hou Han
    Journal of Materials Science & Technology, 2018, 34 (08) : 1419 - 1427
  • [6] Effect of surface roughness on the fretting corrosion behavior of Inconel 690 alloy tube
    Pan, Zhong
    Huang, Longxiang
    Wang, Guoping
    Yin, Meigui
    SURFACE TOPOGRAPHY-METROLOGY AND PROPERTIES, 2025, 13 (01):
  • [7] Effect of temperature on corrosion behavior of alloy 690 in high temperature hydrogenated water
    Wang, Jiazhen
    Wang, Jianqiu
    Ming, Hongliang
    Zhang, Zhiming
    Han, En-Hou
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2018, 34 (08) : 1419 - 1427
  • [8] Corrosion behavior of Alloy 690 in aerated supercritical water
    Zhong, Xiangyu
    Han, En-Hou
    Wu, Xinqiang
    CORROSION SCIENCE, 2013, 66 : 369 - 379
  • [9] Lead-induced stress corrosion cracking behavior of mechanically surface-treated alloy 690
    Li, Nana
    Shi, San-Qiang
    Luo, Jingli
    Lu, Jian
    Wang, Ning
    MATERIALS RESEARCH LETTERS, 2016, 4 (03): : 180 - 184
  • [10] Effect of heat treatment on corrosion resistance of alloy 690
    Qiu, Shaoyu, 1600, Yuan Zi Neng Chuban She, Beijing, China (16):
12345