Liquation Cracking in Linear Friction Welded Directionally Cast Alloy 247

被引：0
|
作者：
Neidel, A. [1 ]
Giller, M. [1 ]
Riesenbeck, S. [1 ]
机构：
[1] Siemens Energy, Gasturbinenwerk Berlin, Werkstoffpruflab, Huttenstr 12, D-10548 Berlin, Germany
来源：
PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY | 2022年 / 59卷 / 10期
关键词：
Alloy; 247; nickel base superalloy; directionally solidified investment casting; translatory friction welding; hot cracking sensitivity;
D O I：
10.1515/pm-2022-0059
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Linear Friction Welding (LFW) is a rarely used joining technology. To test the suitability of this solid-state process for hot cracking-sensitive nickel base superalloys, tests were performed using conventionally and directionally cast slabs of Alloy 247. Since LFW does not involve melting of the weld flanks, there were some expectations that this special welding technique could overcome the poor weldability of Alloy 247. However, all tested specimens failed by liquation cracking (LC) within the Weld Center Zone (WCZ) at the directionally cast side.
引用
收藏
页码：641 / 651
页数：11
相关论文
共 50 条
  • [31] Analysis on linear friction welded joint of Ti-17 alloy
    Ma, TJ
    Xu, QZ
    Yang, SQ
    Cao, HL
    Liang, YM
    Su, J
    Qian, HX
    RARE METAL MATERIALS AND ENGINEERING, 2006, 35 : 233 - 236
  • [32] Heat-Affected Zone Liquation Cracking Resistance of Friction Stir Processed Aluminum-Copper Alloy AA 2219
    Karthik, G. M.
    Ram, G. D. Janaki
    Kottada, Ravi Sankar
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2017, 48 (02): : 1158 - 1173
  • [33] Effects of processing parameters on liquation cracking of 6005A alloy weldments
    Choi, JH
    Lee, DH
    Kim, J
    Shin, DH
    Kim, YS
    METALS AND MATERIALS-KOREA, 2000, 6 (04): : 395 - 399
  • [34] Investigation of stress corrosion cracking of friction stir welded 2060 Al-Li alloy
    Yameen, Muhammad Usama
    Hussain, Khawar
    Afzal, Muhammad
    Akhtar, Naveed
    Farooq, Ameeq
    WELDING IN THE WORLD, 2024, 68 (10) : 2723 - 2733
  • [35] Research on Prediction Method of Liquation Cracking Susceptibility to Magnesium Alloy Welds
    Chen Shujun
    Wang Xuan
    Yuan Tao
    Li Xiaoxu
    ACTA METALLURGICA SINICA, 2018, 54 (12) : 1735 - 1744
  • [36] Effects of processing parameters on liquation cracking of 6005A alloy weldments
    Jae-Ho Choi
    Dong Heon Lee
    Jongryoul Kim
    Dong Hyuk Shin
    Yong-Seog Kim
    Metals and Materials, 2000, 6 : 395 - 399
  • [37] Stress Corrosion Cracking Behavior of Peened Friction Stir Welded 2195 Aluminum Alloy Joints
    Omar Hatamleh
    Preet M. Singh
    Hamid Garmestani
    Journal of Materials Engineering and Performance, 2009, 18 : 406 - 413
  • [38] Stress Corrosion Cracking Behavior of Peened Friction Stir Welded 2195 Aluminum Alloy Joints
    Hatamleh, Omar
    Singh, Preet M.
    Garmestani, Hamid
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2009, 18 (04) : 406 - 413
  • [39] Localized corrosion and stress corrosion cracking resistance of friction stir welded aluminum alloy 5454
    Frankel, GS
    Xia, Z
    CORROSION, 1999, 55 (02) : 139 - 150
  • [40] Heat-Affected Zone Liquation Cracking Resistance of Friction Stir Processed Aluminum-Copper Alloy AA 2219
    G. M. Karthik
    G. D. Janaki Ram
    Ravi Sankar Kottada
    Metallurgical and Materials Transactions B, 2017, 48 : 1158 - 1173
12345