Microstructure and Fatigue Properties of Nodular Cast Iron at Low Frequency Cyclic Loading

被引：0
|
作者：
Vaško A. [1 ]
Belan J. [1 ]
Markovičová L. [1 ]
Tillová E. [1 ]
机构：
[1] Department of Materials Engineering, Faculty of Mechanical Engineering, University of Žilina, Univerzitná 8215/1, Žilina
来源：
Vaško, Alan | 1600年 / Jan-Evangelista-Purkyne-University卷 / 16期
关键词：
Fatigue tests; Mechanical tests; Metallographic analysis; Microfractographic analysis; Nodular cast iron;
D O I：
10.21062/UJEP/X.2016/A/1213-2489/MT/16/5/1188
中图分类号：
学科分类号：
摘要：
The paper deals with the influence of charge composition on microstructure, mechanical and fatigue properties of synthetic nodular cast irons and their micromechanisms of failure. The basic charge of experimental melts was formed by a different ratio of pig iron and steel scrap. Chemical composition of individual melts was regulated alternatively by silicon carbide (SiC) or ferrosilicon (FeSi) and carburizer. The specimens from three melts of nodular cast iron with different microstructure and mechanical properties were used for experiments. Fatigue tests were realised at low frequency sinusoidal cyclic push-pull loading (stress ratio R = -1) at ambient temperature (T = 20 ± 5 °C). They were carried out with using the fatigue experimental machine Zwick/Roell Amsler 150HFP 5100 at frequency f » 120 Hz. © 2016 Published by Manufacturing Technology. All Rights Reserved.
引用
收藏
页码：108 / 108
相关论文
共 50 条
  • [41] Investigation of microstructure of nodular cast iron by color etching
    1600, Trans Tech Publications Ltd (752):
  • [42] Effect of plasma nitriding on high-cycle fatigue properties and fracture behaviors of GJS']JS700 nodular cast iron under cyclic bending loading
    Aghareb Parast, Mohammad Sadegh
    Jamalkhani Khameneh, Mohammad
    Azadi, Mohammad
    Azadi, Mahboobeh
    Mahdipanah, Mohammad Hadi
    Roostaie, Saied
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2021, 44 (08) : 2070 - 2086
  • [43] Microstructure, mechanical and fatigue properties of SiMo- and SiCu- nodular cast irons
    Vasko, Alan
    Uhricik, Milan
    Kucharikova, Lenka
    Tillova, Eva
    ECF22 - LOADING AND ENVIRONMENTAL EFFECTS ON STRUCTURAL INTEGRITY, 2018, 13 : 1527 - 1532
  • [44] Mechanical Properties of Ferritic Nodular Cast Iron at Low Temperatures.
    Siefer, Wilfried
    Orths, Kurt
    Giessereiforschung, 1981, 33 (03): : 109 - 118
  • [45] Study on the low cycle fatigue damage of nodular cast iron based on elastic modulus
    Liu, Jinhai
    Hao, Xiaoyan
    Li, Guolu
    Zhao, Xuebo
    Liu, Gensheng
    FRACTURE AND DAMAGE MECHANICS V, PTS 1 AND 2, 2006, 324-325 : 851 - +
  • [46] Non-symmetrical fatigue life of nodular graphite cast iron under non-proportional multi-axial cyclic loading
    Kachit, M.
    Courbon, J.
    Boulnat, X.
    Adrien, J.
    Verdu, C.
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 125 : 128 - 137
  • [47] Fatigue crack growth in nodular cast iron - Influences of graphite spherical size and variable amplitude loading
    Mottitschka, T.
    Pusch, G.
    Biermann, H.
    Zybell, L.
    Kuna, M.
    15TH INTERNATIONAL CONFERENCE ON THE STRENGTH OF MATERIALS (ICSMA-15), 2010, 240
  • [48] Surface Microstructure and Properties of Nodular Cast Iron Rapidly Solidified by Laser Surface Melting
    Murakami, Reita
    Narita, Ichihito
    Miyahara, Hirofumi
    MATERIALS TRANSACTIONS, 2018, 59 (09) : 1465 - 1470
  • [49] High cycle variable amplitude fatigue of a nodular cast iron
    Marquis, GB
    Rabb, BR
    Karjalainen-Roikonen, P
    FATIGUE TESTING AND ANALYSIS UNDER VARIABLE AMPLITUDE LOADING CONDITIONS, 2005, 1439 : 215 - 231
  • [50] EVALUATING THE INFLUENCE OF SHRINKAGES IN NODULAR CAST IRON ON FATIGUE STRENGTH
    Bleicher, Christoph
    Wagener, Rainer
    Melz, Tobias
    PROCEEDINGS OF THE 7TH INTERNATIONAL CONFERENCE ON MECHANICS AND MATERIALS IN DESIGN (M2D2017), 2017, : 463 - 464
12345