Crystal structure and colorimetric behavior of low melting point ternary alloy

被引：0
|
作者：
Issa T.T. [1 ]
Majeed S.M. [2 ]
Ahmed D.S. [2 ]
机构：
[1] Department of Physics, College of Science, University of Baghdad, Baghdad
[2] Applied Science Department, University of Technology, Baghdad
来源：
Materials Science Forum | 2020年 / 1002卷
关键词：
Bi – Sn – Cu alloy; Bi – Sn – Zn alloy; DSC; Mechanical alloying; Ternary alloy;
D O I：
10.4028/www.scientific.net/MSF.1002.12
中图分类号：
学科分类号：
摘要：
Elements of high purity (99.999) were used to prepare the alloy, Bi, Sn, Zn and Cu. Two types alloy Bi – Sn – Zn and Bi – Sn – Cu were prepared by mechanical alloying technique (MA). Annealing at 100˚Cfor 8 hours was applied for the resulting alloys. X-ray diffraction and differential scanning colorimetriy were tested for the two types of alloy before and after annealing. The best results was noticed in the ternary alloythat prepared at 4 hours milling time, and annelid at 100˚C, for 8 hours, under static air. © 2020 Trans Tech Publications Ltd, Switzerland.
引用
收藏
页码：12 / 20
页数：8
相关论文
共 50 条
  • [1] LOW MELTING-POINT ALLOY TOOLING
    LENFESTEY, RD
    PLASTICS & POLYMERS, 1973, 41 (153): : 132 - 133
  • [2] Low melting point alloy hermetic seal
    不详
    BRITISH CORROSION JOURNAL, 1996, 31 (04): : 258 - 258
  • [3] CRYSTAL STRUCTURE AND MELTING POINT OF CURIUM METAL
    CUNNINGHAM, BB
    WALLMANN, JC
    JOURNAL OF INORGANIC & NUCLEAR CHEMISTRY, 1964, 26 (02): : 271 - 275
  • [4] CRYSTAL STRUCTURE OF TERNARY ALLOY ALPHA(ALMNSI)
    COOPER, M
    ROBINSON, K
    ACTA CRYSTALLOGRAPHICA, 1966, 20 : 614 - &
  • [5] CRYSTAL STRUCTURE OF TERNARY ALLOY ALPHA(ALFESI)
    COOPER, M
    ACTA CRYSTALLOGRAPHICA, 1967, 23 : 1106 - &
  • [6] Metamorphic robot made of low melting point alloy
    Nakai, H
    Kuniyoshi, Y
    Inaba, M
    Inoue, H
    2002 IEEE/RSJ INTERNATIONAL CONFERENCE ON INTELLIGENT ROBOTS AND SYSTEMS, VOLS 1-3, PROCEEDINGS, 2002, : 2025 - 2030
  • [7] LOW-MELTING POINT ALLOY IN LIGHTER PRODUCTION
    不详
    MACHINERY AND PRODUCTION ENGINEERING, 1973, 123 (3169): : 213 - 213
  • [8] Dependency of microstructural parameters and microindentation hardness on the temperature gradient in the In−Bi−Sn ternary alloy with a low melting point
    H. Kaya
    U. Böyük
    E. Çadirli
    Y. Ocak
    S. Akbulut
    K. Keşlioĝlu
    N. Maraşli
    Metals and Materials International, 2008, 14 : 575 - 582
  • [9] The effect of growth rate on microstructure and microindentation hardness in the In-Bi-Sn ternary alloy at low melting point
    Cadirli, E.
    Boyuk, U.
    Kaya, H.
    Marasli, N.
    Keslioglu, K.
    Akbulut, S.
    Ocak, Y.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 470 (1-2) : 150 - 156
  • [10] The effect of growth rate on microstructure and microindentation hardness in the In-Bi-Sn ternary alloy at low melting point
    Çadirli, E.
    Böyük, U.
    Kaya, H.
    Marasli, N.
    Keslioglu, K.
    Akbulut, S.
    Ocak, Y.
    Journal of Alloys and Compounds, 2009, 470 (1-2): : 150 - 156
12345