Study on the microstructure and mechanical properties of Q235B ring casting blank

被引：4
|
作者：
Yan, Honghong [1 ,2 ]
Li, Yongtang [1 ,2 ]
Hu, Yong [1 ,2 ]
Li, Qiushu [1 ,2 ]
Zhao, Dawen [1 ,2 ]
Cao, Zhengzheng [1 ,2 ]
机构：
[1] School of Materials Science and Engineering, Taiyuan University of Science and Technology, Taiyuan,030024, China
[2] Shanxi Key Laboratory of Metallic Materials Forming Theory and Technology, Taiyuan University of Science and Technology, Taiyuan,030024, China
来源：
Jixie Gongcheng Xuebao/Journal of Mechanical Engineering | 2014年 / 50卷 / 14期
关键词：
Compendex;
D O I：
10.3901/JME.2014.14.089
中图分类号：
学科分类号：
摘要：
Tensile strength
引用
收藏
页码：89 / 94
相关论文
共 50 条
  • [21] Effect of Final Rolling Temperature on Microstructure and Properties of 2205/Q235B Duplex Stainless Steel Clad Plate
    Xiao F.
    Wang D.
    Hu W.
    Cui L.
    Gao Z.
    Zhou L.
    Wang, Dongpo (wangdp@tju.edu.cn), 1600, Cailiao Daobaoshe/ Materials Review (34): : 16119 - 16124
  • [22] Q235B储罐腐蚀失效分析
    张玉福
    宋文明
    卢雪梅
    马颖
    郝远
    杨贵荣
    热加工工艺, 2015, 44 (20) : 238 - 240
  • [23] Influence of Rolling Temperatures on Interface Microstructure and Mechanical Properties of Multi-Pass Rolling TA1/Q235B Explosive Welded Sheets
    Li, Huizhong
    Cao, Liangming
    Liang, Xiaopeng
    Zhang, Wending
    Wu, Chunping
    Zeng, Zhiheng
    Zhou, Chengshang
    METALS, 2020, 10 (12) : 1 - 14
  • [24] Q235B中板加工开裂原因分析
    王彦祥
    马静超
    许红玉
    成旭东
    金属世界, 2014, (04) : 47 - 49
  • [25] Q235B冷弯断裂原因分析
    祁敏翔
    仲阳阳
    闫政林
    刘振华
    甘肃冶金, 2022, 44 (02) : 44 - 46
  • [26] Q235B钢管的断裂失效分析
    范文静
    孙维连
    王会强
    葛静
    孙铂
    金属热处理, 2010, 35 (07) : 75 - 77
  • [27] Q235B钢指压板开裂分析
    胡长春
    朱晓红
    薛佳元
    热处理, 2019, 34 (01) : 45 - 47
  • [28] Q235B焊管开裂原因分析
    张爱梅
    新疆钢铁, 2019, (03) : 17 - 19
  • [29] Q235B板材的弯曲变形研究
    戴雨馨
    包钢科技, 2017, 43 (06) : 47 - 50
  • [30] Q235B钢性能升级试验研究
    任培东
    甘肃冶金, 2008, (01) : 3 - 5
12345