Thermodynamic analysis of nanostructured (Fe,Cr) 3Al formation during mechanical alloying

被引：3
|
作者：
Aghili S.E. [1 ]
Ashrafi H. [1 ]
Enayati M.H. [1 ]
Karimzadeh F. [1 ]
机构：
[1] Department of Materials Engineering, Isfahan University of Technology, Isfahan
来源：
Materials Research Innovations | 2016年 / 20卷 / 01期
关键词：
Iron aluminides; Mechanical alloying; Miedema model; Nanostructured materials;
D O I：
10.1080/14328917.2015.1109174
中图分类号：
学科分类号：
摘要：
Nanostructured (Fe,Cr)3Al compound was produced by mechanical alloying (MA) of the Fe50Cr25Al25 elemental powder mixture, and the effect of Cr addition on the formation of solid solution in the ternary Fe-Cr-Al system was investigated. The structural and phase changes of powder particles during MA were studied using X-ray diffractometry and transmission electron microscopy. The results showed that at early stages of MA, a BCC-Fe(Cr,Al) solid solution was formed, which transformed to the disordered (Fe,Cr) 3Al compound by further milling. The thermodynamic analysis based on Miedema model showed that for all binary Fe-Al, Fe-Cr and Cr-Al systems and ternary Fe-Cr-Al system, the formation of solid solution is thermodynamically favourable for all compositions. It was also demonstrated that for the ternary Fe25Cr25Al25 alloy, more driving force is available to form solid solution compared with the Fe75Al25 binary alloy. The results of thermodynamic analysis were in agreement with the MA results. © 2016 Taylor &Francis.
引用
收藏
页码：32 / 36
页数：4
相关论文
共 50 条
  • [11] Synthesis and structural characterization of nanocrystalline (Ni, Fe)3Al intermetallic compound prepared by mechanical alloying
    Adabavazeh, Z.
    Karimzadeh, F.
    Enayati, M. H.
    ADVANCED POWDER TECHNOLOGY, 2012, 23 (03) : 284 - 289
  • [12] Formation mechanism of Fe3Al and FeAl intermetallic compounds during mechanical alloying
    M. H. Enayati
    M. Salehi
    Journal of Materials Science, 2005, 40 : 3933 - 3938
  • [13] Formation mechanism of Fe3Al and FeAl intermetallic compounds during mechanical alloying
    Enayati, MH
    Salehi, M
    JOURNAL OF MATERIALS SCIENCE, 2005, 40 (15) : 3933 - 3938
  • [14] Thermodynamic analysis of nanocrystalline and amorphous phase formation in Nb-Al system during mechanical alloying
    Mostaan, H.
    Karimzadeh, F.
    Abbasi, M. H.
    POWDER METALLURGY, 2012, 55 (02) : 142 - 147
  • [15] Nanostructured Fe3Al intermetallic obtained by mechanical alloying and thermal ageing
    Bonetti, E.
    Valdre, G.
    Enzo, S.
    Cocco, G.
    Soletta, I.
    Nanostructured Materials, 1993, 2 (04):
  • [16] Thermodynamic analysis of Ti-Al-C intermetallics formation by mechanical alloying
    Sadeghi, E.
    Karimzadeh, F.
    Abbasi, M. H.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 576 : 317 - 323
  • [17] Thermodynamic analysis of Ti-Al-C intermetallics formation by mechanical alloying
    Sadeghi, E. (ehsansadeghi120@gmail.com), 1600, Elsevier Ltd (576):
  • [18] Thermodynamic analysis of NiTi formation by mechanical alloying
    Mousavi, T.
    Abbasi, M. H.
    Karimzadeh, F.
    MATERIALS LETTERS, 2009, 63 (9-10) : 786 - 788
  • [19] THERMODYNAMIC ANALYSIS OF PHASE FORMATION IN MECHANICAL ALLOYED Fe3Al POWDER
    Pang, L. X.
    Hao, X. H.
    Han, N. F.
    Xu, J.
    Tang, X. D.
    Li, J.
    SURFACE REVIEW AND LETTERS, 2011, 18 (3-4) : 115 - 120
  • [20] Formation of nanodispersoids in Fe-Cr-Al/30%TiB2 composite system during mechanical alloying
    Sachan, Ritesh
    Park, Jong-Woo
    JOURNAL OF ALLOYS AND COMPOUNDS, 2009, 485 (1-2) : 724 - 729
12345