Preparation and application of environment-friendly flame-retardant silicone-acrylic flocking adhesive

被引：0
|
作者：
Wu H. [1 ,2 ]
Jiang X. [1 ,2 ]
Cai Z. [1 ,2 ]
机构：
[1] College of Chemistry, Chemical Engineering & Biotechnology, Donghua University, Shanghai
[2] Key Laboratory of Science & Technology of Eco-Textile, Ministry of Education, Donghua University, Shanghai
来源：
Fangzhi Xuebao/Journal of Textile Research | 2018年 / 39卷 / 06期
关键词：
Acrylate; Adhesive; Alkylphenol ethoxylates; Ammonium polyphosphate; Electrostatic flocking; Environment-friendly; Flame-retardant;
D O I：
10.13475/j.fzxb.20170802805
中图分类号：
学科分类号：
摘要：
In order to develop high-added value and environment-friendly flocking adhesives, a flocking adhesive featured low-temperature curing, no formaldehyde releasing, alkylphenol ethoxylates (APEO) and flame-retardancy was synthesized by blending an organic and inorganic compound retardant in semi-continuous emulsion polymerization using ethyl acrylate, butyl acrylate, methyl methacrylate and acrylic acid as polymer monomers. The influence of different retardants, mass ratio of retardants, retardant amount, synergist amount on the flocking were investigated. The results show that flocking adhesive (FR) with 30% retardant (mass ratio of ammonium polyphosphate and FR-5 is 3:1) and 10% organic montmorillonite has good properties with flocking fastness, hand feeling and flame-retardancy. Copyright No content may be reproduced or abridged without authorization.
引用
收藏
页码：96 / 100
页数：4